Ammonium hydroxide scavenged binder for low TMA fiberglass insulation products
View Patent ↗A phenol-formaldehyde resole resin is combined with an ammonia-based formaldehyde scavenger to produce a product useful, for example, as a binder used in the production of glass fiber insulation products. The starting resin may have a free formaldehyde content of 1.5 to 14 wt. %, based on a total weight of the resin, and the resin and scavenger may be combined at a molar ratio in the range of 0.1 to 5. The resulting binder may have a free formaldehyde content of 1 wt. % or less, based on a total weight of the reaction product. This binder may then be applied to a glass fiber base material in a conventional manner.
1. A method comprising:
combining a phenol-formaldehyde resole resin and an ammonia-based formaldehyde scavenger to form a mixture, wherein the resin has a free formaldehyde content of 1.5 to 14%, by weight, based on a total weight of the resin, wherein the mixture contains 5% urea, by weight, or less, based on a total weight of the mixture, and wherein the resin and the scavenger are combined in amounts such that a molar ratio of the free formaldehyde to ammonia from the ammonia-based formaldehyde scavenger is in a range of 0.1 to 5; and
reacting the free formaldehyde and the scavenger to thereby form a formaldehyde-scavenged product, wherein the formaldehyde-scavenged product has a free formaldehyde content of 1% or less, by weight, based on a total weight of the formaldehyde-scavenged product, and wherein the formaldehyde-scavenged product has a water dilutability of 50:1 or higher.
2. A method according to claim 1 , wherein the ammonia-based formaldehyde scavenger includes a member selected from the group consisting of anhydrous ammonia and aqueous ammonium hydroxide.
3. A method according to claim 1 , further comprising:
combining water with the phenol-formaldehyde resole resin and the ammonia-based formaldehyde scavenger.
4. A method according to claim 1 , further comprising:
combining a latent acid catalyst with the phenol-formaldehyde resole resin and the ammonia-based formaldehyde scavenger.
5. A method according to claim 4 , wherein the latent acid catalyst includes at least one member selected from the group consisting of an ammonium salt of sulfuric acid, an ammonium salt of oxalic acid, and an ammonium salt of a sulfonic acid.
6. A method according to claim 1 , wherein the molar ratio is in a range of 0.5 to 2.
7. A method according to claim 1 , wherein the phenol-formaldehyde resole resin has a weight average molecular weight of 800 or less.
8. A method according to claim 1 , further comprising:
applying the formaldehyde-scavenged product to a glass fiber base material.
9. A method according to claim 8 , wherein the formaldehyde-scavenged product is applied to the glass fiber base material less than 5 minutes after the free formaldehyde and the ammonia-based formaldehyde scavenger are reacted to form the formaldehyde-scavenged product.
10. A glass fiber material prepared by the method of claim 8 .
11. A method according to claim 1 , wherein the free formaldehyde content of the resole resin is in the range of 3 to 14%, by weight, based on the total weight of the resole resin.
12. A reaction product prepared by the method of claim 1 .
13. A method for preparing a glass fiber product, comprising:
preparing a binder including a phenol-formaldehyde resole resin and an ammonia-based formaldehyde scavenger, wherein the resin has a free formaldehyde content of 1.5 to 14%, by weight, based on a total weight of the resin, wherein the resin and the scavenger are present in amounts such that a molar ratio of the free formaldehyde to ammonia from the ammonia-based formaldehyde scavenger is in a range of 0.1 to 5, wherein the binder has a final free formaldehyde content of 1% or less, by weight, based on a total weight of the binder, and wherein the binder has a water dilutability of 50:1 or higher; and
applying the binder to a glass fiber base material to thereby produce a glass fiber product, wherein the preparing and applying steps occur in an in-line manner.
14. A method according to claim 13 , further comprising:
drying the binder on the glass fiber base material.
15. A method according to claim 13 , further comprising:
forming the glass fiber base material to a predetermined size or shape after the binder is applied to the glass fiber base material.
16. A method according to claim 13 , wherein the ammonia-based formaldehyde scavenger includes a member selected from the group consisting of anhydrous ammonia and aqueous ammonium hydroxide.
17. A method according to claim 13 , further comprising:
mixing a latent acid catalyst with the phenol-formaldehyde resole resin and the ammonia-based formaldehyde scavenger.
18. A method according to claim 13 , wherein the molar ratio is in a range of 0.5 to 2.
19. A method according to claim 13 , wherein the binder contains 5 wt. % urea or less.
20. A method according to claim 13 , wherein the free formaldehyde content of the resole resin is in the range of 3 to 14%, by weight, based on the total weight of the resin.
21. A method according to claim 13 , further comprising:
curing the binder on the glass fiber base material.
22. A glass fiber product prepared by the method of claim 21 .
23. A glass fiber product according to claim 22 , wherein the glass fiber product releases 25 ppm trimethylamine or less when cured for 1 minute at 525° F.
24. A glass fiber product according to claim 22 , wherein the glass fiber product releases 10 ppm trimethylamine or less when cured for 10 minutes at 450° F.
25. A method for preparing a glass fiber product, comprising:
preparing a binder including a phenol-formaldehyde resole resin and an ammonia-based formaldehyde scavenger, wherein the resin has a free formaldehyde content of 1.5 to 14%, by weight, based on a total weight of the resin, wherein the resin and the scavenger are present in amounts such that a molar ratio of the free formaldehyde to ammonia from the ammonia-based formaldehyde scavenger is in a range of 0.1 to 5, wherein the binder has a final free formaldehyde content of 1% or less, by weight, based on a total weight of the binder, and wherein the binder has a water dilutability of 50:1 or higher; and
applying the binder to a glass fiber base material to thereby produce a glass fiber product, wherein the applying step occurs within one hour of the preparing step.
26. A method according to claim 25 , further comprising:
drying the binder on the glass fiber base material.
27. A method according to claim 25 , further comprising:
forming the glass fiber base material to a predetermined size or shape after the binder is applied to the glass fiber base material.
28. A method according to claim 25 , wherein the ammonia-based formaldehyde scavenger includes a member selected from the group consisting of anhydrous ammonia and aqueous ammonium hydroxide.
29. A method according to claim 25 , further comprising:
mixing a latent acid catalyst with the phenol-formaldehyde resole resin and the ammonia-based formaldehyde scavenger.
30. A method according to claim 25 , wherein the molar ratio is in a range of 0.5 to 2.
31. A method according to claim 25 , wherein the binder contains 5 wt. % urea or less.
32. A method according to claim 25 , wherein the free formaldehyde content of the resole resin is in the range of 3 to 14%, by weight, based on the total weight of the resin.
33. A method according to claim 25 , further comprising:
curing the binder on the glass fiber base material.
34. A glass fiber product prepared by the method of claim 33 .
35. A glass fiber product according to claim 34 , wherein the glass fiber product releases 25 ppm trimethylamine or less when cured for 1 minute at 525° F.
36. A glass fiber product according to claim 34 , wherein the glass fiber product releases 10 ppm trimethylamine or less when cured for 10 minutes at 450° F.