Flame retardant thermoplastic resin composition containing styrene polymer as compatabilizer and oxaphospholane compound as flame retardant
The present invention relates to a flame retardant thermoplastic resin composition that comprises (A) about 40 to 95 parts by weight of a rubber modified styrene-containing resin, (B) about 5 to 60 parts by weight of polyphenylene ether resin, (C) about 2 to 30 parts by weight of a styrene-containing copolymer resin having about 5 to 18 % by weight of acrylonitrile in the copolymer per 100 parts by weight of the sum of (A) and (B), (D) about 0.5 to 20 parts by weight of an oxaphospholane compound per 100 parts by weight of the sum of (A) and (B), and (E) about 0 to 30 parts by weight of a phosphoric acid ester compound per 100 parts by weight of the sum of (A) and (B).
1. A flame retardant thermoplastic resin composition comprising:
(A) about 40 to 95 parts by weight of a rubber modified styrene-containing resin composed of
(a1) about 20 to 100% by weight of a styrene-containing graft copolymer resin prepared by graft-polymerizing about 90 to 40% by weight of a monomer mixture comprised of
about 50 to 82% by weight of styrene-containing monomer,
about 19 to 50% by weight of unsaturated nitrile-containing monomer and
about 0 to 40% by weight of monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic anhydride and N-substituted maleimide onto about 10 to 60% by weight of a rubber, and
(a2) about 80 to 0% by weight of a styrene-containing copolymer resin prepared by copolymerizing about 50 to 82% by weight of styrene-containing monomer, about 19 to 50% by weight of unsaturated nitrile-containing monomer and about 0 to 40% by weight of monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic anhydride and N-substituted maleimide;
(B) about 5 to 60 parts by weight of polyphenylene ether resin;
(C) about 2 to 30 parts by weight of a styrene-containing copolymer resin having about 5 to 18% by weight of acrylonitrile in the copolymer per 100 parts by weight of the sum of (A) and (B); (D) about 0.5 to 20 parts by weight of an oxaphospholane compound per 100 parts by weight of the sum of (A) and (B); and
(E) about 0 to 30 parts by weight of a phosphoric acid ester compound per 100 parts by weight of the sum of (A) and (B) wherein the oxaphospholane compound (D) is represented by the following formula:
where R 1 is hydrogen, alkyl of C 1-6 , or aryl of C 6-15 , R 2 and R 3 are hydrogen or alkyl of C 1-6 , and n is in the range of 1 to 3.
2. The flame retardant thermoplastic resin composition according to claim 1 , wherein the styrene-containing monomer is styrene, α-methylstyrene or p-methylstyrene.
3. The flame retardant thermoplastic resin composition according to claim 1 , wherein the unsaturated nitrile-containing monomer is acrylonitrile.
4. The flame retardant thermoplastic resin composition according to claim 1 , wherein the polyphenylene ether resin (B) is poly(2,6-dimethyl-1,4-phenylene) ether.
5. The flame retardant thermoplastic resin composition according to claim 1 , wherein the oxaphospholane compound (D) is 2-methyl-2,5-dioxo-1-oxa-2-phospholane or 2-phenyl-2,5-dioxo-1-oxa-2-phospholane.
6. The flame retardant thermoplastic resin composition as defined in claim 1 , wherein said phosphoric acid ester compound (E) is represented by the following formula:
where R 4 , R 5 and R 6 are hydrogen or alkyl of C 1-4 , X is resorcinol, hydroquinol, bisphenol-A or bisphenol-S aryl or an alkyl-substituted derivative of resorcinol, hydroquinol, bisphenol-A or bisphenol-S, and m is in the range of 0 to 4.
7. The flame retardant thermoplastic resin composition as defined in claim 6 , wherein said phosphoric acid ester compound (E) is a mixture of at least two aromatic phosphoric acid ester compounds having different m.
8. The flame retardant thermoplastic resin composition as defined in claim 1 , wherein said resin composition further comprises up to 50 parts by weight of a resin selected from the group consisting of polyamide, polycarbonate, polystyrene, rubber-reinforced polystyrene and a mixture thereof per 100 parts by weight of the base resin (A) and (B).
9. The flame retardant thermoplastic resin composition as defined in claim 1 , wherein said resin composition further comprises up to 50 parts by weight of an anti-dripping agent, an impact modifier, an inorganic filler, a heat stabilizer, an oxidation inhibitor, a light stabilizer, pigment and/or dye per 100 parts by weight of the base resin (A) and (B).
10. A molded article prepared with the flame retardant thermoplastic resin composition of claim 1 .
11. A molded article prepared with the flame retardant thermoplastic resin composition of claim 2 .
12. A molded article prepared with the flame retardant thermoplastic resin composition of claim 5 .
13. A flame retardant thermoplastic resin composition comprising: about 60 to 85, parts by weight of (A) a rubber modified styrene-containing resin composed of
(a1) about 25 to 70%, by weight of a styrene-containing graft copolymer resin prepared by graft-polymerizing about 90 to 40% by weight of a monomer mixture comprised of
about 65 to 80%, by weight of a styrene-containing monomer,
about 20 to 35%, by weight of unsaturated nitrile-containing monomer and
about 0 to 40% by weight of monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic anhydride and N-substituted maleimide onto about 10 to 60% by weight of a rubber, and
(a2) about 30 to 75%, by weight of a styrene-containing copolymer resin prepared by copolymerizing
about 50 to 82% by weight of styrene-containing monomer,
about 20 to 35%, weight of unsaturated nitrile-containing monomer and
about 0 to 40% by weight of monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic anhydride and N-substituted maleimide.
(B) about 5 to 60 parts by weight of polyphenylene ether resin;
(C) about 2 to 30 parts by weight of a styrene-containing copolymer resin having about 5 to 18% by weight of acrylonitrile in the copolymer per 100 parts by weight of the sum of (A) and (B); (D) about 0.5 to 20 parts by weight of an oxaphospholane compound per 100 parts by weight of the sum of (A) and (B); and (E) about 0 to 30 parts by weight of a phosphoric acid ester compound per 100 parts by weight of the sum of (A) and (B) wherein the oxaphospholane compound (D) is represented by the following formula:
where R 1 is hydrogen, alkyl of C 1-6 , or aryl of C 6-15 , R 2 and R 3 are hydrogen or alkyl of C 1-6 , and n is in the range of 1 to 3.
14. The flame retardant thermoplastic resin composition according to claim 13 , wherein the styrene-containing monomer is styrene, α-methylstyrene or p-methylstyrene.
15. The flame retardant thermoplastic resin composition according to claim 13 , wherein the unsaturated nitrile-containing monomer is acrylonitrile.
16. The flame retardant thermoplastic resin composition according to claim 13 , wherein the polyphenylene ether resin (B) is poly(2,6-dimethyl-1,4-phenylene) ether.
17. The flame retardant thermoplastic resin composition according to claim 13 , wherein the oxaphospholane compound (D) is 2-methyl-2,5-dioxo-1-oxa-2-phospholane or 2-phenyl-2,5-dioxo-1-oxa-2-phospholane.
18. A molded article prepared with the flame retardant thermoplastic resin composition of claim 13 .
19. A molded article prepared with the flame retardant thermoplastic resin composition of claim 14 .
20. A molded article prepared with the flame retardant thermoplastic resin composition of claim 17 .