Fluorinated silica microchannel surfaces
View Patent ↗A method for surface modification of microchannels and capillaries. The method produces a chemically inert surface having a lowered surface free energy and improved frictional properties by attaching a fluorinated alkane group to the surface. The coating is produced by hydrolysis of a silane agent that is functionalized with either alkoxy or chloro ligands and an uncharged C 3 -C 10 fluorinated alkane chain. It has been found that the extent of surface coverage can be controlled by controlling the contact time from a minimum of about 2 minutes to a maximum of 120 minutes for complete surface coverage.
1. A method of coating the interior surface of a microchannel with a fluorocarbon coating, comprising:
contacting the microchannel walls with a chemical mixture comprising an acid catalyst and a fluorine functionalized silane agent in a solvent, wherein the chemical mixture is contacted with the microchannel walls for a predetermined period of time and at a fixed temperature to control the extent to which the walls are coated.
2. The method of claim 1 , wherein the silane agent is functionalized with an uncharged fluorinated alkane and alkoxy or halogen ligands.
3. The method of claim 2 , wherein the halogen ligands are chloro ligands.
4. The method of claim 2 , wherein the uncharged fluorinated alkane is an uncharged C 3 -C 10 fluorinated alkane chain.
5. The method of claim 2 , wherein alkoxy is methoxy, ethoxy, acetoxy, methoxyethoxy or methoxymethyl.
6. The method of claim 1 , wherein the silane agent is (tridecafluoro-1,1,2,2-tetrahydrooctyl) triethoxysilane.
7. The method of claim 1 , wherein the period of time is in the range of from about 2 to about 120 minutes.
8. The method of claim 1 , wherein the fixed temperature is a temperature in the range of from about 50 to 90° C.
9. The method of claim 8 , wherein the temperature is about 70° C.
10. The method of claim 1 , wherein the microchannel is a silica microchannel.
11. A device comprising a system of microchannels, wherein the interior surfaces of the microchannels are coated with the fluorocarbon coating of claim 1 .
12. An improved device for controlling fluid flow in a microchannel in which a mobile, monolithic polymer element, made by polymerizing a monomer mixture within the microchannel, is disposed in the microchannel, and in which a displacing force controls the movement of the monolithic polymer element in the microchannel, wherein the improvement comprises coating the interior surface of the microchannel with the fluorocarbon coating of claim 1 .
13. A method for controlling the surface energy of a microchannel, comprising:
introducing into the microchannel a chemical mixture comprising an acid catalyst and a fluorine functionalized silane agent in a solvent, wherein the chemical mixture is contacted with the microchannel walls for a predetermined period of time and at a fixed temperature to control the extent to which the walls are coated.
14. The method of claim 13 , wherein the silane agent is functionalized with an uncharged fluorinated alkane and alkoxy or halogen ligands.
15. The method of claim 14 , wherein the halogen ligands are chloro ligands.
16. The method of claim 14 , wherein the uncharged fluorinated alkane is an uncharged C 3 -C 10 fluorinated alkane chain.
17. The method of claim 14 , wherein alkoxy is methoxy, ethoxy, acetoxy, methoxyethoxy or methoxymethyl.
18. The method of claim 13 , wherein the silane agent is (tridecafluoro-1,1,2,2-tetrahydrooctyl) triethoxysilane.
19. The method of claim 13 , wherein the period of time is in the range of from about 2 to about 120 minutes.
20. The method of claim 13 , wherein the fixed temperature is a temperature in the range of from about 50 to 90° C.
21. The method of claim 20 , wherein the temperature is about 70° C.