Method to blend separator powders
View Patent ↗A method for making a blended powder mixture, whereby two or more powders are mixed in a container with a liquid selected from nitrogen or short-chain alcohols, where at least one of the powders has an angle of repose greater than approximately 50 degrees. The method is useful in preparing blended powders of Li halides and MgO for use in the preparation of thermal battery separators.
1. A method for making a blended powder mixture, comprising:
adding in a container a liquid selected from the group consisting of liquid nitrogen, methanol, ethanol and isopropanol, to a first powder and a second powder, said first powder having an angle of repose greater than approximately 50°, to form a mixture;
mixing said mixture to form a homogenous mixture; and
removing said liquid to make a blended powder mixture.
2. The method of claim 1 wherein said second powder has an angle of repose greater than approximately 50°.
3. The method of claim 1 wherein said first powder is an electrolyte.
4. The method of claim 3 wherein said electrolyte is an alkali-halide salt.
5. The method of claim 1 wherein said first powder is selected from a LiCl—KCl eutectic powder, a LiCl—LiBr—LiF electrolyte powder, a LiBr—KBr—LiF eutectic powder, a LiNO 3 —KNO 3 powder, and a CsBr—LiBr—KBr powder.
6. The method of claim 4 wherein the second powder is MgO.
7. The method of claim 1 wherein removing said liquid is performed by a method selected from evaporation and combustion.
8. The method of claim 1 wherein the liquid is liquid nitrogen and the container is precooled to a temperature less than approximately −55° C.
9. The method of claim 8 wherein the first powder and second powder are precooled to a temperature less than approximately −55° C.
10. The method of claim 1 wherein said blended powder mixture is heated at an elevated temperature to produce a fused material.
11. The method of claim 10 wherein said fused material is granulated and sieved to prepare a separator powder.
12. The method of claim 11 wherein said separator powder is pressed to form a separator pellet.