View Patent ↗An extrusion process is described for the extrusion of a synthetic wood material. The process includes a significantly higher compression ratio through which the extruded product must pass. The higher compression ratio results in significantly improved product qualities.
1. A synthetic wood component comprising:
an extrusion of blended cellulosic material and thermoplastic material, said extrusion compressed in at least one die under heat and pressure at a ratio of at least about 1.5 to 1 to form a final shape and a final cross sectional area of said synthetic wood component;
wherein the cross sectional area of said final shape has been compressed from an intermediate cross sectional area to said final cross sectional area, and the ratio of said intermediate cross sectional area to said final cross sectional area was at least about 1.5 to 1.
2. The synthetic wood component of claim 1 wherein the ratio of said intermediate cross sectional area to said final cross sectional area of said final shape was at least about 2 to 1.
3. The synthetic wood component of claim 2 wherein the ratio of said intermediate cross sectional area to said final cross sectional area of said final shape was at least about 3.5 to 1.
4. The synthetic wood component of claim 1 wherein said thermoplastic material includes polyethylene.
5. The synthetic wood component of claim 1 wherein said thermoplastic material includes polyvinyl chloride.
6. The synthetic wood component of claim 1 wherein said cellulosic material comprises about 60 percent to about 80 percent by weight of said extrusion.
7. A process for producing a component, said process comprising:
providing a synthetic wood material comprising cellulosic material and thermoplastic material;
extruding said synthetic wood material through a die system to form a final shape having an intermediate cross sectional area; and
compressing said synthetic wood material in said die system at a ratio of at least about 1.5 to 1 to form a final cross sectional area of said final shape of said component.
8. The process of claim 7 wherein the ratio of said intermediate cross sectional area to said final cross sectional area is at least about 2 to 1.
9. The process of claim 8 wherein the ratio of said intermediate cross sectional area to said final cross sectional area is at least about 3.5 to 1.
10. The process of claim 7 wherein said die system has a first aperture and a second aperture, said first aperture having said intermediate cross sectional area, said second aperture having said final cross sectional area;
wherein said synthetic wood material enters said die system through said first aperture and exits said die system through said second aperture; and
wherein said synthetic wood material exits said second aperture in said final shape of said component.
11. The process of claim 10 wherein said first aperture has substantially the same shape as said second aperture.
12. The process of claim 10 wherein:
said die system is comprised of a first die and a second die, said first die having said first aperture and a third aperture, said second die having a fourth aperture and said second aperture, said first die connected to said second die such that said synthetic wood material exits said first die through said third aperture and enters said second die through said fourth aperture;
said synthetic wood material exits said third aperture of said first die substantially in said final shape and said final cross sectional area of said component; and
said second die substantially maintains said final shape and said final cross sectional area of said component.
13. The process of claim 12 further comprising the step of stranding said synthetic wood material prior to compressing said synthetic wood material in said die system at a ratio of at least about 1.5 to 1.
14. A process of producing a component, said process comprising:
providing a synthetic wood material comprising cellulosic material and thermoplastic material;
stranding said synthetic wood material;
forming said synthetic wood material into a final shape of said component having an intermediate cross sectional area; and
compressing said final shape from said intermediate cross sectional area to a final cross sectional area;
wherein the ratio of said intermediate cross sectional area to said final cross sectional area is at least about 1.5 to 1.