Method of making a continuous coating on the surface of a part
View Patent ↗A method and apparatus for a continuous coating of a part may include providing a separation layer made of a material that is weaker than the material of the coating to be made. The part may be placed on one or more supports, the supports coated with the separation layer. A continuity layer of a component material of the coating to be made is interposed between the part and the or each support, at least in vicinity of the or each support zone. The coating is formed by chemical vapor infiltration or deposition, and the part is then separated from the or each support by rupture within the separation layer, the continuity of the coating of the part in the or each support zone being provided by the portion of the coating that comes from the continuity layer that remains in place on the part.
1. A method of making a continuous coating over an entire external surface of a part without leaving uncoated any portion of said surface, comprising the steps of:
providing at least one support having a substrate, a separation layer formed over the substrate and a continuity layer formed over the separation layer, the separation layer being made of a material that is weaker than the material of the coating to be made on said part, and the continuity layer being made of a component material of the coating to be made on said part, and the continuity layer being made of a component material of the coating to be made on said part,
placing said part to be coated on said at least one support with the continuity layer of the support being in contact with said surface of the part to be coated,
forming a coating by chemical vapor infiltration or deposition over said surface of the part and said at least one support, and
subsequently separating the part from said at least one support substrate by rupture within the separation layer, the continuity of the coating at the surface of the part at the location of contact with said at least one support being achieved by a potion of coating provided by the continuity layer that remains in place on the part after rupture within the separation layer.
2. A method as claimed in claim 1 , wherein the separation layer is made of a material of flaky structure, separation between the support and the part being achieved by cleavage within said material.
3. A method as claimed in claim 2 , wherein the material of the separation layer is selected from the group consisting of laminar type pyrolytic carbon; hexagonal structure boron nitride; flake graphite; or flaky structure alumino-silicates such as talc or clays.
4. A method according to claim 1 , wherein the continuity layer is made of a porous material.
5. A method according to claim 4 , wherein the coating is made by chemical vapor infiltration causing the continuity layer to be densified at least partially.
6. A method according to claim 1 , wherein the continuity layer is of a material similar to that of the coating to be made.
7. A method according to claim 6 , wherein, prior to chemical vapor infiltration or deposition, surface treatment is performed on the continuity layer in order to enhance bonding with the coating made subsequently.
8. A method according to claim 7 , wherein the surface treatment is heat treatment.
9. A method according to claim 7 , wherein the surface treatment is acid attack treatment.
10. A method according to claim 1 , for making a continuous coating on a part made at least in part out of carbon or graphite to provide the part with protection against oxidation.
11. A method according to claim 1 , wherein the continuous coating formed over the entire surface of the part is made of a refractory ceramic material selected from carbides and nitrides.
12. A method according to claim 1 , wherein the continuous coating formed over the entire surface of the part is made of silicon carbide.
13. A method of making a continuous coating over an entire external surface of a part eithout leaving uncoated any portion of said surface, comprising the steps of:
providing at least one support having a substrate and a separation layer formed over the substrate, the separation layer being made of a material that is weaker than the material of the coating to be made on said part,
forming locally on the surface of said part at least one continuity layer of a component material of the coating to be made on said part,
placing said part to be coated on said at least one support with said at least one continuity layer formed at the surface of the part being in contact and resting upon the separation layer of said support,
forming a coating by chemical vapor infiltration or deposition over said surface of the part and said at least one support, and
subsequently separating the part from said at least one support substrate by rupture within the separation layer, the continuity of the coating at the surface of the part at the location of contact with said at least one support being achieved by a portion of coating provided by the continuity layer that remains in place on, the part after rupture within the separation layer.
14. A method as claimed in claim 13 , wherein the separation layer is made of a material of flaky structure, separation between the support and the part being achieved by cleavage within said material.
15. A method as claim in claim 14 , wherein the material of the separation layer is selected from: laminar type pyrolytic carbon; hexagonal structure boron nitride; flake graphite; or flaky structure alumino-silicates such as talc or clays.
16. A method as claimed in claim 13 , wherein the continuity layer is made of a porous material.
17. A method as claimed in claim 16 , wherein the coating is made by chemical vapor infiltration causing the continuity layer to be densified at least partially.
18. A method as claimed in claim 13 , wherein the continuity layer is of a material similar to that of the coating to be made.
19. A method as claimed in claim 18 , wherein, prior to chemical vapor infiltration or deposition, surface treatment is performed on the continuity layer in order to enhance bonding with the coating made subsequently.
20. A method as claimed in claim 19 , wherein the surface treatment is heat treatment.
21. A method as claimed in claim 19 , wherein the surface treatment is acid attack treatment.
22. A method as claimed in claim 13 , for making a continuous coating on a part made at least in part out of carbon or graphite to provide the part with protection against oxidation.
23. A method as claimed in claim 13 , wherein the continuous coating formed over the entire surface of the part is made of a refractory ceramic material selected from carbides and nitrides.
24. A method as claimed in claim 23 , wherein the continuous coating formed over the entire surface of the part is made of silicon carbide.