Treatment of porous article
View Patent ↗The present invention is a method for modifying at least one property of a porous membrane. The method comprises the steps of providing a porous membrane. The method also includes exposing the membrane to a fluid at supercritical conditions. At least one property of the membrane is modified while the membrane is exposed to the fluid at supercritical conditions. The condition of the fluid is changed in such a manner that the porous membrane retains the modified property. The present invention is also sheet material that is water-resistant, moisture vapor transmissive and air permeable. The sheet material comprises a membrane having an open pore structure including surfaces defining a plurality of interconnecting pores extending through the membrane and between major sides of said membrane in which the pores have an average pore size. The membrane is made from a material tending to absorb oils and contaminating agents. A uniform coating of precipitated fluorinated urethane polymer material on at least portions of the surfaces of the nodes and fibrils defining the pores. The precipitated fluorinated urethane polymer material provides oil and contaminating agent resistance of at least a number 6 by AATCC 118 testing and an air permeability of at least 0.20 CFM per square foot by ASTM D737 testing.
1. A sheet material that is waterproof, moisture vapor transmissive and air permeable, said sheet material comprising:
a polymeric membrane having an open pore structure including surfaces defining a plurality of interconnecting pores extending through said membrane and between major sides of said membrane in which the pores have an average pore size, said membrane being made from a material tending to absorb oils and contaminating agents; and
a precipitated uniform coating material comprising at least one of fluorinated urethane polymer particles and fluorinated acrylic polymer particles having a particle size of about 1.0 to 10.0 nanometers on at least portions of the surfaces of nodes and fibrils defining the pores in said membrane;
said precipitated material provides oil and contaminating agent resistance of at least a number 6 by AATCC 118 testing and said sheet material having an air permeability of at least 0.20 CFM per square foot by ASTM D737 testing and a moisture vapor transmission at a rate of at least 70,000 gr/m 2 /day.
2. The sheet material of claim 1 wherein the thickness of said precipitated material is less than 0.10 times the average pore size of said membrane.
3. The sheet material of claim 1 wherein said membrane is made from expanded polytetrafluoroethylene material including fibrils in which surfaces of said fibrils define at least a portion of the plurality of interconnecting pores in said membrane having an average pore size no greater than 10 micron.
4. The sheet material of claim 3 wherein at least a portion of said precipitated material is absorbed in portions of the polytetrafluoroethylene material of said membrane.
5. The sheet material of claim 4 wherein at least a portion of said precipitated material exudes from said membrane wherein said exuding is demonstrated by removing the coating from the membrane surface using a solvent to decrease the oil hold-out number followed by exposing the membrane to sunlight to increase the oil hold-out number.
6. The sheet material of claim 1 wherein
said coating is applied from a low surface tension solution comprising a solvent, the solution being capable of entering the pores in said sheet material; and wherein
said coating is precipitated on surfaces of said fibrils upon rendering the coating insoluble in the solvent.
7. The sheet material of claim 6 wherein said solvent is carbon dioxide in a supercritical phase.
8. The sheet material of claim 6 wherein the solvent of the solution is in a supercritical phase.
9. The sheet material of claim 6 wherein the surface tension of the solution is less than 5.0 dynes/cm.
10. The sheet material of claim 1 wherein said sheet material comprises expanded polytetrafluoroethylene.
11. The sheet material of claim 10 wherein a portion of said coating material is absorbed in portions of polytetrafluoroethylene material of the expanded polytetrafluoroethylene sheet material.
12. The sheet material of claim 1 wherein the membrane comprises a polymer selected from the group consisting of polyolefin, polyamide, polyester, polysulfone, polyether, acrylic and methacrylic polymers, polystyrene, polyurethane, polypropylene, polyethylene, cellulosic polymer, and polytetrafluoroethylene.
13. The sheet material of claim 1 wherein said membrane is comprised of expanded polytetrafluoroethylene material, and wherein said coating of said at least one of said fluorinated urethane polymer particles and fluorinated acrylic polymer particles is applied in a solvent comprised of carbon dioxide in a supercritical phase.
14. The sheet material of claim 1 in which the particle size is 1.0 to 5.0 nanometers.
15. A sheet material that is waterproof, moisture vapor transmissive and air permeable, said sheet material comprising:
an expanded polytetrafluoroethylene membrane having an open pore structure including surfaces defining a plurality of interconnecting pores extending through said membrane and between major sides of said membrane in which the pores have an average pore size, said membrane being made from a material tending to absorb oils and contaminating agents; and
a precipitated uniform coating material comprising at least one of fluorinated urethane polymer particles and fluorinated acrylic polymer particles having a particle size of about 1.0 to 10.0 nanometers on at least portions of the surfaces of fibrils defining the pores in said membrane;
said precipitated coating material provides oil and contaminating agent resistance of at least a number 6 by AATCC 118 testing and said sheet material having an air permeability of at least 0.20 CFM per square foot by ASTM D737 testing and a moisture vapor transmission at a rate of at least 70,000 gr/m 2 /day.
16. The sheet material of claim 15 wherein at least a portion of said precipitated material is absorbed in portions of the polytetrafluoroethylene material of said membrane.
17. The sheet material of claim 16 wherein at least a portion of said precipitated material exudes from said membrane wherein said exuding is demonstrated by removing the coating from the membrane surface using a solvent to decrease the oil hold-out number followed by exposing the membrane to sunlight to increase the oil hold-out number.