Expanded porous thermoplastic polymer membranes
View Patent ↗Open-celled membranes from thermoplastic polymers are prepared from foamed polymer melts by extrusion through a die and particulary suitable for filtration.
1. An open-cell foamed porous filtration membrane of at least one thermoplastic polymer having a internal three-dimensional structure comprising contiguous hollow polyhedral cells sharing common walls and having at least two of its polyhedral walls ruptured, wherein said membrane has a proportion of open cells of at least 80%, a void fraction of at least 75%, and an open-pore pore size distribution with a standard deviation of ±10% of the average pore diameter, said membrane being formed by foaming said at least one thermoplastic polymer under pressure with at least two cell-forming agents selected from the group consisting of air, nitrogen, carbon dioxide, water, helium and mixtures thereof.
2. The membrane of claim 1 wherein said membrane has a pore diameter in the microfiltration range of from 0.05 μm to 30 μm.
3. The membrane of claim 1 wherein said membrane has a pore diameter in the macrofiltration range of from greater than 30 μm to 200 μm.
4. The membrane of any of claims 1 – 3 wherein said membrane is reinforced on at least one side by a separate fabric selected from the group consisting of a woven fabric, a nonwoven fabric, and a knitted fabric wherein each of said fabrics is selected from the group consisting of a metallic fabric and a polymeric fabric that is not integral with said membrane.
5. The membrane of claim 4 wherein said at least one thermoplastic polymer is selected from the group consisting of substituted and unsubstituted cellulose derivatives, substituted and unsubstituted polycarbonates, substituted and unsubstituted polyolefins, poly(vinylidene fluoride), substituted and unsubstituted polyesters, substituted and unsubstituted polystyrenes, substituted and unsubstituted polysulfones, substituted and unsubstituted polyethersulfones, substituted and unsubstituted polyamides and mixtures thereof.
6. The membrane of claim 5 wherein said at least one thermoplastic polymer is polycarbonate.
7. The membrane of claim 5 wherein said at least one thermoplastic polymer is polystyrene.
8. The membrane of claim 5 wherein said at least one thermoplastic polymer is polypropylene.
9. The membrane of claim 1 wherein said cell-forming agents comprise carbon dioxide and water.
10. The membrane of claim 1 wherein said cell-forming agents comprise carbon dioxide and helium.