Green glass composition
View Patent ↗The present invention is a green soda-lime-silica glass composition. The composition comprises 68 to 75% SiO 2 , 10 to 18% Na 2 O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al 2 O 3 , and 0 to 5% K 2 0, where CaO+MgO is 6 to 15% and Na 2 O+K 2 0 is 10 to 20%, and colorants comprising: 0.3 to 0.8 wt. % total iron as Fe 2 O 3 wherein the ratio of FeO/total Fe as Fe 2 O 3 is 0.35 to 0.62; 0.05 to 0.5 wt. % manganese compound as MnO 2 ; 0 to 0.1 wt. % titanium oxide as TiO 2 ; and 0 to 1 wt. % cerium oxide as CeO 2 . The colored glass has the following spectral properties at 4.0 mm. thickness: 65 to 81% light transmittance using Illuminant A (LTA) and using Illuminant C has a dominant wavelength of 494 to 555 nanometers with an excitation purity of 2 to 9%.
1. A colored glass for use in a motor vehicle having a base and a colorant, wherein composition of the colorant by weight of the colored glass consists essentially of:
0.3 to 0.65 wt. % of total iron as Fe 2 O 3 , wherein ratio of FeO to total iron as Fe 2 O 3 is in a range of 0.37 to 0.65;
0.05 to 0.8 wt. % of manganese oxide as MnO 2 ; and
wherein the colored glass at 4 mm. control thickness has a light transmittance using illuminant A in a range of 65% to 81%, an infrared transmittance in the range of 10% to 32%, an ultraviolet transmittance in the range of 39% to 60%, an excitation purity in a range of 2% to 9%, and a dominant wavelength using illuminant C in a range of 494 to 555 nanometers.
2. The colored glass of claim 1 , wherein the colorant further comprises up to 1 wt. % titanium oxide as TiO 2 .
3. The colored glass of claim 2 , wherein the amount of titanium oxide is in the range of 0.3 to 0.6 wt. %.
4. The colored glass of claim 1 , wherein the colorant further comprises up to 1 wt. % cerium oxide as CeO 2 .
5. The colored glass of claim 4 , wherein the amount of cerium oxide is in the range of 0.2 to 0.5 wt. %.
6. The colored glass of claim 1 , wherein the amount of total iron expressed as Fe 2 O 3 is in the range of 0.4 to 0.6 wt. %.
7. The colored glass of claim 1 , wherein the amount of manganese oxide as MnO 2 is in the range of 0.1 to 0.3 wt. %.
8. A colored glass for use in a motor vehicle having a base and a colorant, wherein composition of the colorant by weight of the colored glass comprising:
0.3 to 0.65 wt. % of total iron as Fe 2 O 3 , wherein ratio of FeO to total iron as Fe 2 O 3 is in a range of 0.37 to 0.65;
0.05 to 0.8 wt. % of manganese oxide as MnO 2 ; and
wherein the colored glass at 4 mm. control thickness has a light transmittance using illuminant A in a range of 65% to 81%, an infrared transmittance in the range of 10% to 32%, an ultraviolet transmittance in the range of 39% to 60%, an excitation purity in a range of 2% to 9%, and a dominant wavelength using illuminant C in a range of 494 to 555 nanometers;
wherein a color of the colored glass is defined by a chromatography coordinates inside the polygon ABCDA, wherein the chromaticity coordinates are:
x
y
A
0.284
0.321
B
0.301
0.317
C
0.307
0.326
D
0.314
0.352
and the polygon ABCDA represent the full scope of the color space of the present invention.
9. The colored glass of claim 8 , wherein the preferred chromaticity coordinates inside the polygon ABCDA are:
x
y
A
0.3
0.319
B
0.293
0.325
C
0.305
0.338
D
0.304
0.325
and the smaller polygon ABCDA represents the preferred color space of the present invention.
10. The colored glass of claim 8 , wherein the color defined inside the polygon ABCDA is green.
11. The colored glass of claim 1 , wherein the dominant wavelength in the range of 496 to 520 nanometers.
12. The colored glass of claim 1 , wherein the composition of the base by weight of the colored glass is:
68 to 75 wt. % SiO 2;
10 to 18 wt. % Na 2 O;
5 to 15 wt. % CaO;
0 to 10 wt. % MgO;
0 to 5 wt. % Al 2 O 3 ; and
0 to 5 wt. % K 2 O;
wherein the total amount of CaO and MgO is in a range of 6 to 15 wt. % and the total amount of Na 2 O and K 2 O is in a range of 10 to 20 wt. %.