Non-stick coated molds
View Patent ↗The invention provides non-stick coated molds, a process for the preparation thereof and their use for the production of plastics molded parts, particularly for the production of molded parts made of polyurethane foam.
1. A mold having a non-stick coating wherein the non-stick coating comprises organomodified nanoscale SiO 2 particles.
2. The mold of claim 1 , wherein the non-stick coating additionally comprises colloidal alkylsilsesquioxane in aqueous/alcoholic suspension.
3. The mold of claim 1 , wherein the non-stick coating comprises the reaction product of:
a) one or more colloidal silicon dioxide solutions with an average particle size of 5 to 150 nanometers diameter,
b) one or more organofunctional trialkoxysilanes corresponding to the general formula:
R′—Si(OR) 3
wherein:
R′: represents an optionally fluorinated alkyl substituent having 1 to 6 carbon atoms, a vinyl substituent, an acryloyl substituent, a methacryloyl substituent, a γ-glycidoxypropyl substituent, or a γ-methacryoxypropyl substituent, and
each R: represents an alkyl substituent having 1 to 8 carbon atoms,
c) one or more pH regulating additives and, optionally,
d) a catalyst.
4. A process for the production of a mold having a non-stick coating, comprising
(1) applying a coating to the internal surface(s) of a metal or plastic mold, wherein the coating comprises the reaction product of:
a) one or more colloidal silicon dioxide solutions having an average particle size of 5 to 150 nanometers diameter,
b) one or more organofunctional trialkoxysilanes corresponding to the general formula:
R′—Si(OR) 3
wherein:
R′: represents an optionally fluorinated alkyl substituent having 1 to 6 carbon atoms, a vinyl substituent, an acryloyl substituent, a methacryloyl substituent, a γ-glycidoxypropyl substituent, or a γ-methacryloxypropyl substituent, and
each R: may be the same or different and represents an alkyl substituent having 1 to 8 carbon atoms,
c) one or more pH regulating additives
and, optionally,
d) a catalyst; and
(2) curing the coating of step (1).
5. The process of claim 4 , wherein in component b):
R′: represents a methyl substituent, an ethyl substituent, an acryloyl substituent, a methacryloyl substituent, or a fluoroalkyl substituent with 1 to 6 carbon atoms; and
each R: may be the same or different and represents a methyl substituent, an ethyl substituent, an isopropyl substituent, or a sec-butyl substituent.
6. The process of claim 4 , wherein at least 70 wt. %, based on 100 wt. % of b), comprises trialkoxyalkylsilanes.
7. The process of claim 4 , wherein a) said colloidal silicon dioxide solutions have an average particle size of 10 to 30 nanometers diameter.
8. The process of claim 4 , wherein the coating additionally comprises one or more polar solvents.
9. In a process for the production of a plastic molded part, comprising filling a mold with a reaction mixture suitable to form a plastic part, allowing the plastic part to cure and removing the plastic part from the mold, the improvement wherein the mold has a non-stick coating which comprises organomodified nanoscale SiO 2 particles.