View Patent ↗Copolymers containing trialkylsilylacrylate units are erodible in seawater and can be used to formulate antifouling marine paints. The copolymers are characterized by low levels of silylacrylate component.
1. A seawater-erodible copolymer comprising repeating units of formula
where A is present in an amount of from 5 to about 22 mole percent of the copolymer and has the formula
where R 1 , R 2 and R 3 , each independently is linear or branched alkyl elected from the group consisting of n-propyl, isopropyl, n-butyl, isobutyl, and sec-butyl;
X is H or CH 3 ; and
B represents the residue of one or more ethylenically unsaturated monomers copolymerizable with A,
said copolymer characterized by an erosion rate in seawater of from 2 to 10 μm/month.
2. A self-polishing antifoulant coating composition comprising a silylacrylate copolymer and a toxicant, the copolymer characterized by an erosion rate in seawater of from about 2 to about 10 μm/month and recurring units of formula
where X is H or CH 3 ,
R 1 , R 2 and R 3 , each independently is linear or branched alkyl selected from the group consisting of n-propyl, isopropyl, n-butyl, isobutyl, and sec-butyl, and further characterized by the presence of the silylacrylate component in an amount of from 5 to about 22 mole percent of the copolymer; and
B is the residue of one or more ethylenically unsaturated monomers that are copolymerizable with the silylacrylate monomer.
3. In a seawater-erodible copolymer comprising the residue of a silylacrylate monomer and the residues of one or more ethylenically unsaturated copolymerizable monomers, the improvement which comprises maintaining the level of the silylacrylate component of the copolymer in the range of from about 11 to about 22 mole percent, whereby the erosion rate of the copolymer can be increased by reducing the mole percentage of the silylacrylate component downward from 22 mole percent.
4. A seawater-erodible copolymer comprising from 5 to about 11 mole percent of the residue of a tri(aliphatic)silyl(meth)acrylate monomer and the balance of the copolymer comprising the residues of one or more ethylenically unsaturated monomers copolymerizable with said silyl(meth)acrylate, said copolymer having an erosion rate in seawater of from about 5 to about 15 μm/month, and wherein said aliphatic portion of said tri(aliphatic)silyl(meth)acrylate can be the same or different and is selected from the group consisting of n-propyl, isopropyl, n-butyl, isobutyl, and sec-butyl.
5. A self-polishing antifoulant coating composition comprising the silylacrylate copolymer of claim 1 and a toxicant.
6. A self-polishing antifoulant coating composition comprising the silylacrylate copolymer of claim 3 and a toxicant.
7. A self-polishing antifoulant coating composition comprising the silylacrylate copolymer of claim 4 and a toxicant.