Process for the production of composite tubing particularly for air conditioning and tubing thus obtained
View Patent ↗A process for the production of composite tubing, particularly for air conditioning, from a structure of mineral or organic fibers, natural or artificial. The structure of fibers is impregnated with a suitable resin, and after shaping in or on a mold, the temperature and possibly the pressure is raised for polymerization of the resin, a sealing of the wall of the shaped piece being carried out in the course of this process. The structure of fibers is constituted by a single ply of a unit weight of at least about 400 g/m 2 , which ply is impregnated with resin at an impregnation quantity of at least 40%, then there is emplaced on one of the surfaces of the single ply a coating of a sealing agent. The polymerization is carried out while the single ply and its coating have the desired shape in or on the mold.
1. A process for the production of composite tubing from a structure of mineral or organic fibers, natural or artificial, in which said structure of fibers is impregnated with a suitable resin and after shaping in or on a mold, the temperature is raised for polymerization of said resin, a sealing of a wall of the tubing being carried out in the course of this process, wherein,
there is used a fiber structure constituted by a single ply ( 2 , 24 ) of a unit weight of at least about 400 g/m 2 ,
said single ply ( 2 , 24 ) is impregnated with said resin at an impregnation quantity of at least 40%,
then there is placed on one of the surfaces of said single ply ( 2 , 24 ) a coating ( 6 , 26 ) of a sealing agent,
said polymerization being carried out while said single ply ( 2 , 24 ) and its coating ( 6 , 26 ) are in the desired shape in or on said mold ( 20 a , 20 b ).
2. The process according to claim 1 , wherein said sealing agent is constituted by a thin self-extinguishing film ( 6 ).
3. The process according to claim 2 , wherein said film ( 6 ) is pressed against a cloth ( 4 ) of fibers previously impregnated with a suitable resin and constituting said single ply ( 4 ), so as to obtain a single strip of which one of the surfaces is constituted by said impregnated cloth and the other surface is constituted by the film of a sealing agent, said strip being then draped in or on a mold of suitable shape.
4. The process according to claim 3 , wherein said surface of the strip constituted by the impregnated cloth ( 4 ) is disposed against the wall of the mold.
5. The process according to claim 1 , wherein said sealing agent is constituted by a paste.
6. The process according to claim 5 , wherein the sealing agent constituted by said paste is applied against one of the surfaces of a cloth of previously impregnated fibers ( 4 ) constituting said single ply, then the assembly is draped in or on a mold of suitable shape.
7. The process according to claim 6 , wherein the surface of the ply ( 4 ) that is not covered with said sealing agent is disposed against the wall of the mold.
8. The process according to claim 1 , wherein said single pre-impregnated ply ( 24 ) is emplaced by draping in or on the mold ( 20 a , 20 b ), then the coating of sealing agent ( 26 ) is emplaced on said draped ply ( 24 ), then the ply-coating assembly is pressed against the mold ( 20 a , 20 b ) and said polymerization is carried out in an oven or an autoclave ( 22 ).
9. The process according to claim 5 , wherein the paste is a self-extinguishing melamine paste.
10. The process according to claim 1 , wherein the composite tubing is air conditioning tubing.
11. The process according to claim 1 , wherein pressure is also raised during polymerization of said resin.