Method for the preparation of plate glass having low residual stress
View Patent ↗A flat glass plate having a low residual stress, suitable for use in preparing a display, can be prepared without an annealing or polishing process by way of controlling the horizontal temperature gradient of a molten glass plate to a specific range during cooling.
1. A method for preparing a plate glass by cooling a molten glass plate having a width of L cm, comprising: 1) gradually increasing the temperature gradient between a maximum temperature point set at the center part and a minimum temperature point set at 0.005 L cm away from the end part toward the center on a horizontal line across the width of the plate glass from 0 to 0.10° C./mm while the glass is in a fluid state, 2) gradually decreasing said temperature gradient from 0.10 to 0.03° C./mm while the glass changes from a fluid state into a glassy state, 3) gradually increasing said temperature gradient from 0.03 to 0.10° C./mm until the transition into a glassy state is completed, and 4) gradually decreasing said temperature gradient while the glass is in a glassy state, wherein the difference between the final temperature gradient values of steps 2) and 3) is adjusted within the range of 0.01 to 0.04° C./mm.
2. The method of claim 1 , wherein in step 2), the temperature gradient between the end part and the minimum temperature point is adjusted to 0.1 to 1.5° C./mm, and the cooling rate of the end part is controlled to 0.1 to 3° C./sec.
3. The method of claim 1 , wherein L is in the range of 100 to 300 cm.
4. The method of claim 1 , wherein the initial temperature of the maximum temperature point of step 2) is in the range of 890 to 990° C.
5. The method of claim 1 , wherein the final temperature of the maximum temperature point of step 2) is in the range of 710 to 810° C.
6. The method of claim 1 , wherein the final temperature of the maximum temperature point of step 3) is in the range of 640 to 700° C.
7. The method of claim 1 , wherein steps 1), 2), 3) and 4) are conducted for 40 to 360, 30 to 240, 15 to 90 and 60 to 240 seconds, respectively.
8. The method of claim 2 , wherein L is in the range of 100 to 300 cm.