Granted Patent B2

US 6,846,446 · App. 10/294,296 · Granted Jan 25, 2005

Abstract

Claims (84)

1. Method for calibrating near infrared (NIR) spectroscopic instrumentation so as to enable use in quantitative measurement of resin-loading of wood-materials during in-line assembly for subsequent bonding during production of a composite wood-product, comprising

(A) providing NIR spectroscopic instrumentation including an associated source of NIR radiation covering a range of wavelengths selected within about 350 nm to about 2500 nm;

(B) quantitatively pre-establishing resin-loading of reference-source test-samples of wood-materials of a type selected for in-line assembly, and capable of providing for bonding to produce a composite wood-product;

(C) supporting said pre-established resin-loaded test-samples on a conveyance surface capable of establishing a controlled rate of relative movement between said supported test-samples and said source of NIR radiation for irradiating wood-materials of said test-samples;

(D) establishing said controlled rate of relative movement for said test-samples simulating a selected in-line controlled-rate of movement of resin-loaded wood-materials being directed in-line for assembly;

(E) irradiating said pre-established resin-content test-samples with NIR radiation, covering said selected range of wavelengths, during relative movement between said NIR source and said test samples at a selected controlled rate for quantitative measurement of absorption of said NIR radiation of said wood-materials of said pre-established resin-content test-samples;

(F) calibrating said spectroscopic instrumentation by providing a calibration curve enabling quantitative analyses of resin-loading of test-sample during said controlled movement of said test samples, by measuring non-absorbed NIR energy within said selected range of wavelengths as reflected by said exposed test-samples on said conveyance surface; and

(G) removing the absorptive effect of said reflected NIR energy resulting from NIR absorption by constituents of said test samples other than resin.

2. The invention of claim 1 , including

establishing resin-content of said test-samples so as to present an incrementally-progressive resin-loading for wood-materials of respective test-samples, with said resin-loading being selected from the group, consisting of:

(i) a spread weight per unit area, and

(ii) percentage weight of resin to weight of wood materials, extending in a range of zero percent to about fourteen (14%) percent.

3. The invention of claim 1 , in which

relative movement is established between said test-samples and said source of NIR, including steps of

selecting a rotatable conveyance surface capable of being driven at a rotational rate to simulate a selected in-line movement rate for resin-loading of said type wood-materials of test-samples during in-line assembly of said wood-materials, and

for measuring reflected NIR energy from wood materials of said resin-loaded test-samples.

4. The invention of claim 1 , in which

providing a calibration curve for said NIR spectroscopic instrumentation, includes

removing absorptive effects responsive to moisture content of said wood-materials and of said resin.

5. The invention of claim 4 , including

obtaining calibrated measurement, in a selected wavelength range of about 400 nm to about 2250 nm, of resin-content of said test-samples by removing measured non-absorbed reflected NIR energy at wavelengths of:

900 nm to 1000 nm,

1450 nm to 1500 nm, and

1900 nm to 2000 nm.

6. Method for calibrating near infrared (NIR) spectroscopic instrumentation for non-invasive measurement of resin-loading of wood-materials during movement in-line for assembly and subsequent bonding for production of composite wood-strand product, comprising the steps of

(A) preparing said wood-materials by strand-cutting wood strands having a high length-to-thickness ratio and selected surface-area dimension parameters, for in-line resin-loading and subsequent production of composite wood-strand product;

(B) providing near infrared (NIR) spectroscopic measuring instrumentation including a sensor head and a source of NIR radiation, for irradiating said wood-materials, in a range of wavelengths selected within about 350 nm to about 2500 nm;

(C) calibrating said NIR spectroscopic measuring instrumentation for use in quantitative analyses of resin-loading of said wood-materials during movement in an assembly line, by

(i) preparing reference-source test-samples from said wood-materials, including:

(a) pre-establishing resin-loading of said test-samples;

(b) quantitatively pre-selecting resin-loading for said wood-materials providing an incrementally-increasing resin-loading of wood-materials of said test-samples within a selected resin-loading range, and

(c) positioning said pre-established resin-loaded test-samples on a conveyor surface capable for use during assembly of said cut wood strand materials;

(D) positioning said spectroscopic measuring instrumentation, and said NIR source, for

(i) irradiating said test-samples, and

(ii) providing penetration of, and at least partial absorption by, said resin-loaded test-samples of said NIR radiation within said selected range of wavelengths: and

(E) calibrating said NIR spectroscopic instrumentation, by

(i) measuring non-absorbed NIR energy as reflected by said wood-strand materials of said test-samples,

(ii) comparing said calibrated absorbed NIR spectroscopic absorptive measurements of said incrementally-increasing pre-established resin-loading test-samples, with

(iii) said pre-established resin-loading of wood-strand materials of said respective test-samples for verifying accurate calibrating of said instrumentation for measurement of resin-loading, and

(iv) selectively removing NIR absorptive effects due to moisture-content of said wood test-samples and of said resin.

7. The invention of claim 6 , further including

(F) providing for in-line use of said calibrated NIR spectroscopic measuring instrumentation for non-invasive measuring of resin-loading of wood-strand materials moving in an assembly line for subsequent bonding-treatment production of composite wood-strand product, selected from the group consisting of:

(i) oriented strand board, and

(ii) oriented strand lumber.

8. The invention of claim 7 for production of oriented strand board (OSB), carried out by

controlling rate of movement of said wood-strand materials through a resin-loading structure, and

correlating introduction of resin with rate of movement of said wood-strand materials so as to control resin-loading weight.

9. The invention of claim 8 , further including

(H) establishing a rate of movement for resin-loaded wood-strand materials onto a strand-layer forming conveyor surface which is moving at a rate correlated with said calibrated NIR spectroscopic instrumentation for measurement of resin-loading;

(I) utilizing said calibrated NIR spectroscopic instrumentation for quantitatively-monitoring resin-loading of wood-strand materials, by

(i) measuring resin-loading of said resin-loaded wood-strand materials, as delivered from said resin-loading structure, while moving on said strand-layer-forming conveyor, and

(ii) indicating said measured resin-loading of raw said wood-strand materials so as to be available for control of assembly operations for purposes of controlling resin-loading.

10. The invention of claim 9 , further including:

(J) providing for quantitative-control of said resin-loading by

(i) indicating resin-loading value as measured by said NIR calibrated instrumentation, for

(ii) feedback control of resin-loading, by

(iii) selecting from the group consisting of

(a) quantitatively controlling resin as introduced for contact with said strand materials,

(b) controlling rate of movement of said strand materials being delivered for said assembly line, and

(c) combinations of (a) and (b), for

(iv) maintaining a desired uniform resin-loading weight in relation to weight of said wood-strands during strand layer forming assembly.

11. The invention of claim 10 , including

providing multiple separate movable strand-layer conveyor assembly surfaces for assembly of planar strand layers selected from the group consisting of

(i) three-strand layers, and

(ii) five-strand layers.

12. The invention of claim 11 , for assembly of oriented strand board of three-strand layers,

each strand layer receiving wood-strand materials at a controlled rate for separately forming:

(i) a face layer,

(ii) a core-layer, and

(iii) a remaining face layer.

13. The invention of claim 12 , further including

selecting respective resin and resin-loading percentage weight for each said separate layer;

controlling resin-loading for each said separate strand-layer while moving on its respective conveyor surface, and

combining said multiple planar layers by:

(i) positioning a resin-loaded face layer on each planar surface of said centrally-located resin-loaded core-layer, for

(ii) pressing said combined wood-strand layers by timed exposure to heat and pressure, for

(iii) polymerizing said controlled resin-loaded combined layers, producing said composite oriented wood board.

14. The invention of claim 6 for production of oriented strand lumber (OSL), comprising

selecting strand lumber having a high length-to-thickness ratio,

controlling resin-loading of said strand lumber using NIR calibrated spectroscopic measurement of resin loading,

combining said resin-loaded strand lumber forming an enlarged mat for pressing under heat and pressure, and

finishing said bonded mat by cutting said mat into end-usage product selected from the group consisting of

(a) structural studs, and

(b) millwork components.