Fabric conditioning composition
View Patent ↗Fabric softening compositions with 1-10% by weight of cationic fabric softening compound show a surprising increase in viscosity when a fatty acid partial ester of a polyhydric alcohol at a level greater than 0.01% by weight and less than or equal to 0.45% by weight based on the composition is added and if the resulting mixture is sheared at a temperature below the phase transition temperature of the fabric softener composition. As a result, viscosities in the range 35-500 mPa·s at 106 s −1 can be obtained in a surprising manner.
1. A process for preparing a fabric conditioning composition, comprising mixing water with:
(a) 1-10% by weight of a cationic fabric softening composition based on the total mixture, and
(b) a fatty acid partial ester of a polyhydric alcohol at a level greater than 0.01% by weight and less than or equal to 0.45% by weight based on the composition,
wherein the aqueous dispersion is sheared at a temperature below the phase transition temperature of the dispersed phase.
2. The process according to claim 1 , wherein said composition further comprises a fatty acid.
3. The process according to claim 2 , wherein said fatty acid is present in an amount of more than about 0.1% to less than about 5% by weight of said composition.
4. The process according to claim 2 , wherein the weight ratio of component (a) to said fatty acid is from 10:1 to 1:10.
5. The process according to claim 1 , wherein said fabric conditioning composition comprises about 2.0 to about 5.5% by weight of component (a).
6. The process according to claim 1 , wherein said component (b) is a fatty acid partial ester of glycerol.
7. The process to claim 6 , wherein said component (b) comprises glycerol monostearate.
8. The process according to claim 1 , wherein said component (a) is a quaternary ammonium compound.