Alkaline electrochemical cells with improved electrolyte
View Patent ↗Alkaline electrochemical cells containing no added mercury and having a concentration of potassium hydroxide in the electrolyte, prior to discharge, of between about 34 and 37% (w/w solution) and wherein the amount of electrolyte is such that, after a calculated level of one electron discharge of the manganese dioxide, the calculated concentration of potassium hydroxide is between 49.5 and 51.5% (w/w solution), have superior performance in intermittent discharge tests.
1. An alkaline electrochemical cell containing no added mercury and comprising:
an aqueous potassium hydroxide electrolyte;
a zinc-containing anode; and
a manganese dioxide-containing cathode; wherein prior to discharge, the concentration of potassium hydroxide in the electrolyte is between about 34 and 37% w/w solution and the amount of electrolyte is such that, at a calculated level of one electron discharge of the manganese dioxide, the calculated concentration of potassium hydroxide is between 49.5 and 51.5% w/w solution.
2. The cell according to claim 1 , wherein, at a depth of discharge of one electron, the calculated concentration of potassium hydroxide is about 50% w/w solution.
3. The cell according to claim 2 , wherein, at a depth of discharge of one electron, the calculated concentration of potassium hydroxide is no greater than 51% w/w solution.
4. The cell according to claim 2 , wherein, at a depth of discharge of one electron, the calculated concentration of potassium hydroxide is 50.6% w/w solution.
5. The cell according to claim 1 , wherein, prior to discharge, the concentration of potassium hydroxide in the electrolyte is about 36% w/w solution.
6. The cell according to claim 1 , having zinc oxide added to only the anode.
7. The cell according to claim 6 , wherein the amount of zinc oxide added is about 0.05% w/w anode.
8. The cell according to claim 1 , wherein the anode has a porosity of at least 66%, and comprises non-granular zinc.
9. The cell according to claim 8 , wherein the anode has a porosity of up to about 77%.
10. The cell according to claim 8 , wherein the non-granular zinc is in an amount of at least 0.6% w/w anode per 1% increase in porosity of the anode over 66%.
11. The cell according to claim 10 , wherein the non-granular zinc is zinc flake.
12. The cell according to claim 8 , wherein the anode comprises about 5% w/w anode of non-granular zinc.
13. The cell according to claim 12 , wherein the non-granular zinc is zinc flake.
14. The cell according to claim 1 , wherein the anode has a porosity of 70% to 76%.
15. The cell according to claim 14 , wherein the anode has a porosity of 72% to 74%.
16. The cell according to claim 1 , wherein the anode has a porosity of 66% or less and comprises no non-granular zinc.
17. The cell according to claim 1 , wherein the anode contains from 60% to 77% w/w anode zinc.
18. An alkaline electrochemical cell containing no added mercury and comprising:
an aqueous potassium hydroxide electrolyte;
a zinc-containing anode; and
a manganese dioxide-containing cathode; wherein
prior to discharge, the concentration of potassium hydroxide in the electrolyte is between about 34 and 37% w/w solution;
the amount of electrolyte is such that, at a calculated level of one electron discharge of the manganese dioxide, the calculated concentration of potassium hydroxide is between 49.5 and 51.5% w/w solution; and
a ratio of cathode capacity:cell volume is in the range of 0.47 to 0.50 Ah/cm 3 , when cathode capacity is calculated based on a one electron discharge of the manganese dioxide and using a molecular formula of MnO 1.96 for the manganese dioxide.
19. The cell according to claim 18 , wherein a ratio of theoretical anode capacity:theoretical cathode capacity is about 1.33:1, when the theoretical cathode capacity is calculated based on a one electron discharge of the manganese dioxide and using a molecular formula of MnO 1.96 for the manganese dioxide.
20. The cell according to claim 18 , wherein the cell is an LR6 cell having a theoretical cathode capacity of at least 2.9 Ah, when the theoretical cathode capacity is calculated based on a one electron discharge of the manganese dioxide and using a molecular formula of MnO 1.96 for the manganese dioxide.
21. The cell according to claim 20 , wherein the theoretical cathode capacity is in the range of 2.9 to 3.1 Ah.
22. The cell according to claim 21 , wherein the cell, when discharged at a constant resistance of 3.9 ohms for 1 hours per day with a rest period of 23 hours per day, reaches an endpoint voltage of 0.8 volt only after a total of at least 480 minutes discharge time.