Process of preparing delayed-dissolution cellulose ethers
View Patent ↗A process for preparing cellulose ethers having delayed dissolution in water is described. The process comprises: (a) treating a moist cellulose ether with a solution comprising a dialdehyde; (b) adding an aqueous salt solution to the moist cellulose ether, such that said cellulose ether has a pH of from 6.0 to 8.0, the aqueous salt addition being performed at least one of, (i) prior to step (a), (ii) concurrently with step (a), and (iii) subsequent to step (a); and (c) drying and comminuting the treated cellulose ether of step (b). The cellulose ether, or mixtures of cellulose ethers, prepared by the method of the present invention may be used as protective colloids, thickeners and adhesives.
1. A process for preparing cellulose ethers having delayed dissolution in water, comprising:
(a) treating a moist cellulose ether with a solution comprising a dialdehyde;
(b) adding an aqueous salt solution to the moist cellulose ether, such that said cellulose ether has a pH of from 6.0 to 8.0, the aqueous salt addition being performed at least one of, (i) prior to step (a), (ii) concurrently with step (a), and (iii) subsequent to step (a); and
(c) drying and comminuting the treated cellulose ether of step (b),
wherein said aqueous salt of step (b) comprises at least two salts, one salt being a weak acid having a pka of from 5.5. to 8.5, and the other salt being the salt of a weak acid having a pka of from 5.5. to 8.5.
2. The process of claim 1 wherein the cellulose ether is a nonionic cellulose ether selected from the group consisting of methylcellulose, methylhydroxyethylcellulose, methylhydroxypropylcellulose and hydroxy-ethylcellulose.
3. The process of claim 1 wherein the cellulose ether is an ionic cellulose ether selected from the group consisting of carboxymethylcellulose, carboxymethylhydroxyethylcellulose, sulphoethylcellulose and carboxy-methylsulphoethylcellulose.
4. The process of claim 1 wherein the cellulose ether prior to drying and comminuting in step (c) has a water content of from 40 to 80% by weight, based on total weight.
5. The process of claim 1 wherein said dialdehyde is glyoxal, which is added in an amount of from 0.1 to 4% by weight of glyoxal, based on dry cellulose ether weight.
6. The process of claim 1 wherein said aqueous salt solution of step (b) comprises an alkali metal dihydrogen phosphate and a di(alkali metal) hydrogen phosphate.
7. The method of claim 6 wherein said alkali metal dihydrogen phosphate is sodium dihydrogen phosphate, and said di(alkali metal) hydrogen phosphate is selected from the group consisting of disodium hydrogen phosphate and sodium potassium hydrogen phosphate.
8. The method of claim 6 wherein the molar ratio of said alkali metal dihydrogen phosphate to said di(alkali metal) hydrogen phosphate is from 2:1 to 1:2.
9. The method of claim 8 wherein the molar ratio of said alkali metal dihydrogen phosphate to said di(alkali metal) hydrogen phosphate is from 1.2:1 to 1:1.2.
10. The process of claim 1 wherein 0.01 to 2 percent by weight of salt, based on the weight of dry cellulose ether, is added in step (b) by means of said aqueous salt solution.
11. A method of preparing a protective colloid, a thickener and an adhesive from cellulose ether comprising, providing a cellulose ether prepared by the method of claim 1 .
12. The method of claim 11 wherein said cellulose ether is carboxymethylcellulose.