Glass coating agent and method for coating glass material using the same
View Patent ↗A glass coating agent is provided which is adapted for application onto the surface of a glass substrate and, upon heating, forms a metal oxide layer. The glass coating agent comprises a metallic compound represented by formula (I): R 1 k-m M(OCOR 2 ) m (I) wherein M represents a metal atom selected from the group consisting of tin, titanium, indium, silicon, zirconium, and aluminum; R 1 represents a straight-chain, branched, or cyclic alkyl, alkenyl, or aryl group having 1 to 6 carbon atoms; R 2 represents a branched alkyl group having 3 to 6 carbon atoms; k is a number representing the valence of the metal atom M; and m is a number of 1 to k. Further, there is provided a glass coating method using the glass coating agent. According to the glass coating agent, a metal oxide layer having excellent fastness properties and free from haze can be formed on the surface of glass substrates. According to the glass coating method, the metal oxide layer can be continuously and stably produced.
1. A glass coating method comprising coating a glass bottle with a glass coating agent while maintaining the temperature of the glass 450 to 750° C. to form a metal oxide layer on the surface of the glass, wherein said glass coating agent comprises a metallic compound represented by formula (I):
R 1 k-m M(OCOR 2 ) m (I)
wherein M represents a metal atom selected from the group consisting of tin, titanium, indium, silicon, zirconium, and aluminum;
R 1 represents a straight-chain, branched, or cyclic alkyl, alkenyl, or aryl group having 1 to 6 carbon atoms;
R 2 represents a branched alkyl group having 3 to 6 carbon atoms;
k is a number representing the valence of the metal atom M, and
m is 2, and
wherein said glass coating agent is in the form of a liquid, in the form of a dispersion or solution in a solvent, or in the form of a gas.
2. A glass coating method comprising coating a glass plate with a glass coating agent while maintaining the temperature of the glass at 450 to 750° C. to form a metal oxide layer on the surface of the glass, wherein said glass coating agent comprises a metallic compound represented by formula (1):
R 1 k-m M(OCOR 2 ) m (I)
wherein M represents a metal atom selected from the group consisting of tin, titanium, indium, silicon, zirconium, and aluminum;
R 1 represents a straight-chain, branched, or cyclic alkyl, alkenyl, or aryl group having 1 to 6 carbon atoms;
R 2 represents a branched alkyl group having 3 to 6 carbon atoms;
k is a number representing the valence of the metal atom M, and
m is 2, and
wherein said glass coating agent is in the form of a liquid, in the form of a dispersion or solution in a solvent, or in the form of a gas.
3. A glass coating method according to claim 1 , wherein the metallic compound is dibutyltin dipivalate, dibutyltin diisobutylate, dibutyltin dineoheptate, dibutyltin diisolactate, monobutyltin tripivalate, monomethyltin tripivalate, monobutyltin triisobutylate, dimethyltin dipivalate, dimethyltin diisobutylate, stannous pivalate, stannic pivalate, tributylsilyl pivalate, triisopropylsilyl pivalate, triisopropylsilyl isobutylate, dibutylsilyl dipivalate, diisopropylsilyl dipivalate, diphenylsilyl dipivalate, monophenylsilyl tripivalate, dimethyltitanium dipivalate, monobutylindium dipivalate, or diethylzirconium dipivalate.
4. A glass coating method according to claim 2 , wherein the metallic compound is dibutyltin dipivalate, dibutyltin diisobutylate, dibutyltin dineoheptate, dibutyltin diisolactate, monobutyltin tripivalate, monomethyltin tripivalate, monobutyltin triisobutylate, dimethyltin dipivalate, dimethyltin diisobutylate, stannous pivalate, stannic pivalate, tributylsilyl pivalate, triisopropylsilyl pivalate, triisopropylsilyl isobutylate, dibutylsilyl dipivalate, diisopropylsilyl dipivalate, diphenylsilyl dipivalate, monophenylsilyl tripivalate, dimethyltitanium dipivalate, monobutylindium dipivalate, or diethylzirconium dipivalate.
5. A glass coating method according to claim 1 , wherein the metallic compound is dibutyltin dipivalate.
6. A glass coating method according to claim 2 , wherein the metallic compound is dibutyltin dipivalate.
7. A glass coating method according to claim 1 , wherein said glass bottles are continuously coated with said coating agent by CVD while carrying the glass bottles at given intervals and constant speed on a conveyor belt.
8. A glass coating method according to claim 2 , wherein said glass plates are continuously coated with said coating agent by CVD while carrying the glass plates at given intervals and constant speed on a conveyor belt.