High strength steel pipe for an air bag and a process for its manufacture
View Patent ↗In order to manufacture a steel pipe for an air bag which can cope with increase in the pressure of gas blown into an air bag and decreases in the wall thickness of an accumulator, a steel having a composition, mass %, of: C: 0.05-0.20%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%, if necessary at least one of Mo: at most 0.50%, Ni: at most 1.5%, Cu: at most 0.5%, V: at most 0.2%, Ti: at most 0.1%, Nb: at most 0.1%, and B: at most 0.005%, and also if necessary, at least one of Ca: at most 0.01%, Mg: at most 0.01%, and REM (rare earth elements): at most 0.01%, and a remainder of Fe and impurities is used to produce a steel pipe, and the pipe is then subjected to cold working to predetermined dimensions, then to heating to a temperature of at least the Ac 1 transformation temperature followed by quenching, and then to tempering at a temperature no higher than the Ac 1 transformation temperature.
1. A process of manufacturing a high strength steel pipe for an air bag having excellent bursting resistance, characterized by producing a pipe from a steel material having a composition, in mass %, of:
C: 0.05-0.20%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%, and a remainder of Fe and impurities,
subjecting the steel pipe to cold working to obtain predetermined dimensions, then heating it to a temperature of at least the Ac 1 transformation temperature followed by quenching, and then performing tempering at a temperature no higher than the Ac 1 transformation temperature, the steel pipe having a tensile strength of 900 Mpa or more.
2. A manufacturing process as set forth in claim 1 , wherein the steel composition further contains, in mass %, at least one of Cu: at most 0.5%, Ti: at most 0.1%, and Nb: at most 0.1%.
3. A manufacturing process as set forth in claim 1 , wherein the steel composition further contains, in mass %, V; at most 0.2%.
4. A manufacturing process as set forth in claim 1 , wherein the steel composition further contains, in mass %, at least one of Ca: at most 0.01%, Mg: at most 0.01%, and REM (rare earth elements): at most 0.01%.
5. A steel pipe for an air bag manufactured by claim 1 , wherein the L/T ratio of the X-ray integrated intensity ratio of the {110} plane in a plane perpendicular to the axial direction L to that in a plane perpendicular to the circumferential direction T of the steel pipe for an air bag is at most 4.
6. An accumulator for an air bag made from a steel pipe for an air bag as set forth in claim 5 .
7. A process of manufacturing a high strength steel pipe for an air bag having excellent bursting resistance, characterized by producing a pipe from a steel material having a composition, in mass %, of:
C: 0.05-0.20%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%,
at least one of Mo: at most 0.50%, Ni: at most 1 .5%, and B: at most 0.005%, and a remainder of Fe and impurities,
subjecting the steel pipe to cold working to obtain predetermined dimensions, then heating it to a temperature of at least the Ac 1 transformation temperature followed by quenching, and then performing tempering at a temperature no higher than the Ac 1 transformation temperature, the steel pipe having a tensile strength of 900 Mpa or more.
8. A manufacturing process as set forth in claim 7 , wherein the steel composition further contains, in mass %, V; at most 0.2%.
9. A manufacturing process as set forth in claim 7 , wherein the steel composition further contains, in mass %, at least one of Ca: at most 0.01%, Mg: at most 0.01%, and REM (rare earth elements): at most 0.01%.
10. A steel pipe for an air bag manufactured by claim 7 , wherein the L/T ratio of the X-ray integrated intensity ratio of the {110} plane in a plane perpendicular to the axial direction L to that in a plane perpendicular to the circumferential direction T of the steel pipe for an air bag is at most 4.
11. An accumulator for an air bag made from a steel pipe for an air bag as set forth in claim 10 .
12. A process of manufacturing a high strength steel pipe for an air bag having excellent bursting resistance, characterized by producing a pipe from a steel material having a composition, in mass %, of:
C: 0.05-0.20%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%,
at least one of Mo: at most 0.50%, Ni: at most 1.5%, and B: at most 0.005%,
at least one of Cu: at most 0.50%, Ti: at most 0.1%, and Nb: at most 0.1%, and a remainder of Fe and impurities,
subjecting the steel pipe to cold working to obtain predetermined dimensions, then heating it to a temperature of at least the Ac 1 transformation temperature followed by quenching, and then performing tempering at a temperature no higher than the Ac 1 transformation temperature, the steel pipe having a tensile strength of 900 Mpa or more.
13. A manufacturing process as set forth in claim 12 , wherein the steel composition further contains, in mass %, V; at most 0.2%.
14. A manufacturing process as set forth in claim 12 , wherein the steel composition further contains, in mass %, at least one of Ca: at most 0.01%, Mg: at most 0.01%, and REM (rare earth elements): at most 0.01%.
15. A steel pipe for an air bag manufactured by claim 12 , wherein the L/T ratio of the X-ray integrated intensity ratio of the {110} plane in a plane perpendicular to the axial direction L to that in a plane perpendicular to the circumferential direction T of the steel pipe for an air bag is at most 4.
16. An accumulator for an air bag made from a steel pipe for an air bag as set forth in claim 15 .