Magnetic recording medium and magnetic storage device
View Patent ↗An inplane magnetic recording medium having high S/N and thermal stability and a reliable magnetic storage device having surface recording density of 50 megabit/mm 2 or more is described. The magnetic recording medium includes magnetic layers formed on a nonmagnetic substrate with a plurality of ground layers therebetween, at least one of the ground layers formed from an alloy of a body-centered cubic structure containing Cr as a main component and B of from 2 atomic % to 12 atomic %. Main components of the magnetic layers include a lower magnetic layer containing Co and Cr of from 10 atomic % to 16 atomic %, with film thickness of from 1.5 nm to 4.5 nm, and an upper magnetic layer containing Co, coupling anti-ferromagnetically with the lower magnetic layer through nonmagnetic intermediate layers.
1. A magnetic recording medium comprising
a non-magnetic substrate;
a plurality of underlayers disposed on the non-magnetic substrate, at least one of the underlayers being composed of a Cr—Ti—B alloy which contains Cr as a main component and between 2% and 12% by atomic weight B;
a lower magnetic layer having Co as a main component and between 10% and 16% by atomic weight Cr, the lower magnetic layer having a film thickness of between 1.5 nm to 4.5 nm, formed on an underlayer;
a non-magnetic intermediate layer disposed on the lower magnetic layer; and
an upper magnetic layer disposed on the non-magnetic intermediate layer, the upper magnetic layer containing Co as a main component and being coupled antiferromagnetically with the lower magnetic layer.
2. A magnetic recording medium comprising:
a non-magnetic substrate;
a first underlayer having an amorphous or microcrystal structure disposed on the non-magnetic substrate;
a second underlayer disposed on the first underlayer, the second underlayer comprising a Cr—Ti—B alloy containing Cr as a main component, and from 2% to 12% by atomic weight B,
a lower magnetic layer disposed on the second underlayer, the lower magnetic layer containing Co as a main component and from 10% to 16% by atomic weight Cr, and having a film thickness of from 1.5 nm to 4.5 nm;
a non-magnetic intermediate layer disposed on the lower magnetic layer; and
an upper magnetic layer disposed on the non-magnetic intermediate layer, the upper magnetic layer containing Co as a main component, and being and antiferromagnetically coupled with the lower magnetic layer.
3. A magnetic recording medium comprising:
a non-magnetic substrate;
a first underlayer having a B2 structure disposed on the non-magnetic substrate;
a second underlayer comprising a Cr—Ti—B alloy containing Cr as a main component and from 2% to 12% by atomic weight of B, the second underlayer being disposed on the first underlayer;
a lower magnetic layer disposed on the second underlayer, the lower magnetic layer containing Co as a main component and from 10% to 16% by atomic weight Cr, and having a film thickness of from 1.5 nm to 4.5 nm;
a non-magnetic intermediate layer disposed on the lower magnetic layer; and
an upper magnetic layer disposed on the non-magnetic intermediate layer, the upper magnetic layer containing Co as a main component and being antiferromagnetically coupled with the lower magnetic layer.
4. A magnetic recording medium comprising:
a non-magnetic substrate;
a first underlayer having an amorphous or B2 structure disposed on the non-magnetic substrate;
a second underlayer disposed on the first underlayer, the second underlayer containing Cr as a main component and from 2% to 12% by atomic weight B;
a non-magnetic third underlayer disposed on the second underlayer, the third underlayer having a hexagonal close-packed structure and containing Co as a main component;
a lower magnetic layer disposed on the third underlayer, the lower magnetic layer containing Co as a main component and from 10% to 16% by atomic weight Cr and having a film thickness from 1.5 nm to 4.5 nm;
a non-magnetic intermediate layer disposed on the lower magnetic layer; and
an upper magnetic layer disposed on the non-magnetic intermediate layer, the upper magnetic layer containing Co as a main component and being antiferromagnetically coupled with the lower magnetic layer.
5. The magnetic recording medium according to claim 1 , wherein the lower magnetic layer further contains less than 10% atomic weight of Pt.
6. The magnetic recording medium according to claim 1 , including a layer comprising an alloy having a higher saturation magnetization than that of the upper magnetic layer and containing Co as a main component, disposed between the upper magnetic layer and the non-magnetic intermediate layer.
7. The magnetic recording medium according to claim 2 , wherein the lower magnetic layer further comprises less than 10% by atomic weight of Pt.
8. The magnetic recording medium according to claim 2 , wherein the first underlayer comprises a Ni—Ta alloy.
9. The magnetic recording medium according to claim 2 , including a layer comprising an alloy having a higher saturation magnetization than that of the upper magnetic layer and containing Co as a main component, the layer being disposed between the upper magnetic layer and the non-magnetic intermediate layer.
10. The magnetic recording medium according to claim 3 , wherein the lower magnetic layer further comprises less than 10% by atomic weight Pt.
11. The magnetic recording medium according to claim 3 , wherein the first underlayer comprises a Ni—Al alloy.
12. The magnetic recording medium according to claim 3 , layer composed of an alloy that has a higher saturation magnetization than that of the upper magnetic layer and contains Co as a main component, is deposited between the upper magnetic layer and the non-magnetic intermediate layer.
13. The magnetic recording medium according to claim 4 , wherein the lower magnetic layer further contains Pt of 10 atomic % or less.
14. The magnetic recording medium according to claim 4 , wherein the lower magnetic layer further contains B of 10 atomic % or less.
15. The magnetic recording medium according to claim 4 , wherein the first underlayer comprises a Ni—Ta alloy.
16. The magnetic recording medium according to claim 4 , wherein the first underlayer is comprises a Ni—Al alloy.
17. The magnetic recording medium according to claim 4 , including an alloy layer having a higher saturation magnetization than that of the upper magnetic layer and containing Co as a main component, the alloy layer disposed between the upper magnetic layer and the non-magnetic intermediate layer.
18. A magnetic storage device comprising
a magnetic recording medium according to claim 1 ;
a drive unit for driving the magnetic recording medium in a direction of recording;
a composite head having in combination an electromagnetic induction magnetic head for recording and a spin valve magnetic head for reproducing;
means for moving the composite head relative to the magnetic recording medium; and
recording/reproducing signal processing means for the composite head.