Polyethylene terephthalate compositions
View Patent ↗A method for increasing the crystallization rate of a polyethylene terepthalate (PET) prepared based on terepthalic acid (TPA) and ethylene glycol monomers, by adding into said TPA-based PET an effective amount of a polyethylene terepthalate prepared based on dimethyl terephthalate (DMT), in an amount sufficient for said thermally formable composition to have an increase in crystallization temperature as required for the final end-use application.
1. A method for increasing the crystallization rate of a crystallisable polyethylene terephthalate (PET) composition prepared based on terephthalic acid (TPA) and ethylene glycol monomers by blending in said PET composition an effective amount of a polyethylene terephthalate prepared based on dimethyl terephthalate (DMT).
2. The method of claim 1 , wherein said DMT-based PET is incorporated into said TPA-based composition in an amount of about 5–70 wt. %, based on the total weight of said PET composition.
3. The method of claim 1 , wherein DMT-based PET is incorporated into said TPA-based composition in an amount sufficient to raise the crystallization temperature of said composition of at least 0.5 degree Celsius, compared to the crystallization temperature of a TPA-based PET composition without any addition of DMT-based PET.
4. The method of claim 1 , further comprising blending into said PET composition a nucleating agent.
5. The method of claim 4 , wherein said nucleating agent is selected from the group of talcum, boron nitride, aluminum nitride, silica, PTFE, a salt of organic compounds having acidic groups, pyrazole, or mixtures thereof.
6. The method of claim 1 , further comprising forming said PET composition into an article by a process selected from one of extrusion, injection molding, blow molding, co-extrusion, and thermoforming.
7. The method of claim 1 , wherein said polyethylene terephthalate (PET) composition prepared based on terephthalic acid (TPA) and ethylene glycol monomers is a recycled material.
8. The method of claim 1 , wherein said polyethylene terephthalate prepared based on dimethyl terephthalate (DMT) is a recycled material.
9. A thermally formable composition comprising a blend of a polyethylene terephthalate (PET) prepared based on terephthalic acid (TPA) and ethylene glycol monomers, and an effective amount of a polyethylene terephthalate prepared based on dimethyl terephthalate (DMT), wherein said DMT-based PET is present in an amount sufficient for said thermally formable composition to have a crystallization temperature of at least 0.5 degree Celsius higher than a TPA-based PET composition without any DMT-based PET present.
10. The composition of claim 9 , further comprising a nucleating agent.
11. The composition of claim 10 , wherein said nucleating agent is selected from the group of talcum, boron nitride, aluminum nitride, silica, PTFE, a salt of organic compounds having acidic groups, pyrazole, or mixtures thereof.
12. The composition of claim 9 , wherein said DMT-based PET is present in an amount of about 5–70 wt. %, based on the total weight of said PET composition.
13. An article comprising the composition of claim 9 .
14. An article comprising a combination of a blend of a polyethylene terephthalate (PET) prepared based on terephthalic acid (TPA) and ethylene glycol monomers, and an effective amount of a polyethylene terephthalate prepared based on dimethyl terephthalate (DMT) in a ratio of 95:5 to 5:95.
15. The article of claim 13 , wherein said TPA-based PET comprises pelletized scrap TPA-based PET materials.
16. The article of claim 13 , wherein said DMT-based PET comprises pelletized scrap DMT-based PET materials.