Heat treatable coated article with reduced color shift at high viewing angles
View Patent ↗A coated article is provided so as to have fairly neutral a* and/or b* color values at high viewing angles such as 45 and/or 60 degrees off-axis. In certain example embodiments, the neutral a* and/or b* values at high viewing angles (VA) are caused by lessening the thickness of a bottom titanium oxide layer. Coated articles herein may be used in the context of insulating glass (IG) window units, or in other suitable applications.
1. A heat treated coated article including a coating supported by a glass substrate, the coating comprising, from the glass substrate outwardly:
a layer comprising titanium oxide;
a layer comprising silicon nitride;
a first contact layer;
a first layer comprising silver provided over and in contact with said first contact layer;
a dielectric layer;
a second layer comprising silver;
another dielectric layer; and
wherein the layer comprising titanium oxide has a thickness of from 20 to 60 Å, the coated article has a Total Solar (TS) value of no greater than 40%, and the coated article has glass side reflective a* and b* color values of from −1.0 to +1.0 at a viewing angle of 60 degrees.
2. The coated article of claim 1 , wherein the coated article has glass side reflective a* and b* color values of from −0.8 to +0.8 at the viewing angle of 60 degrees, and a Δa* g (glass side reflective) value of no greater than 2.5 over a viewing angle shift of about 60 degrees.
3. The coated article of claim 2 , wherein the coated article has a Δa* g (glass side reflective) value of no greater than 1.5 over the viewing angle shift of about 60 degrees.
4. The coated article of claim 1 , wherein the titanium oxide layer has a thickness of from 30 to 60 Å, and is sandwiched between and contacts each of the glass substrate and the layer comprising silicon nitride.
5. The coated article of claim 1 , wherein the coated article has a TS of no greater than 37%.
6. The coated article of claim 1 , wherein the second layer comprising silver is at least 30 Å thicker than the first layer comprising silver.
7. The coated article of claim 1 , wherein the second layer comprising silver is at least 40 Å thicker than the first layer comprising silver.
8. The coated article of claim 1 , wherein the coated article is thermally tempered, and has a sheet resistance of no greater than 4 ohms/square.
9. The coated article of claim 1 , wherein the coated article comprises an IG window unit.
10. The coated article of claim 1 , wherein the coated article has glass side reflective a* and b* values that are both closer to zero at a 60 degree viewing angle that at a normal or 0 degree viewing angle.
11. The coated article of claim 1 , wherein the coated article has a SHGC of no greater than 0.45.
12. The coated article of claim 1 , wherein the coated article has a SHGC of no greater than 0.41.
13. A coated article including a coating supported by a glass substrate, the coating comprising, from the glass substrate outwardly:
a layer comprising titanium oxide;
a dielectric layer;
a first contact layer;
a first layer comprising silver provided over and in contact with said first contact layer;
a dielectric layer;
a second layer comprising silver;
another dielectric layer;
wherein the coated article has glass side reflective a* and b* values that are closer to 0 at a viewing angle of 60 degrees than at a normal viewing angle of 0 degrees; and
wherein the layer comprising titanium oxide has a thickness of from 20 to 60 Å.
14. A coated article including a coating supported by a glass substrate, the coating comprising, from the glass substrate outwardly:
a layer comprising titanium oxide;
a dielectric layer;
a first contact layer;
a first layer comprising silver provided over and in contact with said first contact layer;
a dielectric layer;
a second layer comprising silver;
another dielectric layer;
wherein the coated article has glass side reflective a* and b* values that are closer to 0 at a viewing angle of 60 degree than a normal viewing angle of 0 degrees; and
wherein the coated article has a Total Solar (TS) value of no greater than 40%.
15. A coated article including a coating supported by a glass substrate, the coating comprising, from the glass substrate outwardly:
a layer comprising titanium oxide;
a first contact layer;
a first layer comprising silver provided over and in contact with said first contact layer;
a dielectric layer;
a second layer comprising silver;
another dielectric layer;
wherein the article has reflective a* and b* values that are closer to 0 at a viewing angle of 60 degree than a normal viewing angle of 0 degrees; and
wherein the layer comprising titanium oxide has a thickness of from 20 to 60 Å.
16. A coated article including a supported by a glass substrate, the coating comprising, from the glass substrate outwardly:
a layer comprising titanium oxide;
a first contact layer;
a first comprising silver provided over and in contact with said first contact layer;
a dielectric layer;
a second layer comprising silver;
another dielectric layer;
wherein the coated article has glass side reflective a* and b* values that are closer to 0 at a viewing angle of 60 degrees than at a normal viewing angle of 0 degree; and
wherein the coated article has a Total solar (TS) value of no greater than 40%.