Extensible laminate having improved stretch properties and method for making same
View Patent ↗An extensible laminate having improved set and hysteresis is disclosed. The extensible laminate includes an extensible nonwoven web laminated to an elastomeric sheet that have been mechanically stretched in the cross direction after lamination. A method for making the extensible laminate includes laminating an extensible nonwoven web to an elastomeric sheet to form a laminate and mechanically stretching the laminate in a cross direction by at least about 50 percent.
1. An extensible laminate comprising:
a necked nonwoven web; and
an elastomeric sheet,
wherein the necked nonwoven web and the elastomeric sheet after lamination and prior to a cycling test, have been mechanically stretched in the cross direction to provide an extensible laminate having a hysteresis value, measured during a first 100 percent elongation/retraction cycle of the cycling test, at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
2. The extensible laminate of claim 1 , wherein the extensible laminate has a hysteresis value at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
3. The extensible laminate of claim 1 , wherein the extensible laminate has a 7-day hysteresis value at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
4. The extensible laminate of claim 1 , wherein the extensible laminate has a 30-day hysteresis value at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
5. The extensible laminate of claim 1 , wherein the extensible laminate has a lower elastic set value than a comparable extensible laminate that has not been previously stretched.
6. The extensible laminate of claim 1 , wherein the extensible laminate has an elastic set value at least about 10 percent lower than a comparable extensible laminate that has not been previously stretched.
7. The extensible laminate of claim 1 , wherein the extensible laminate has an elastic set value at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
8. The extensible laminate of claim 1 , wherein the extensible laminate has an elastic set value at least about 30 percent lower than a comparable extensible laminate that has not been previously stretched.
9. The extensible laminate of claim 1 , wherein the extensible laminate has a lower elongation/retraction ratio than a comparable extensible laminate that has not been previously stretched.
10. The extensible laminate of claim 1 , wherein the extensible laminate has an elongation/retraction ratio at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
11. The extensible laminate of claim 1 , wherein the extensible laminate has an elongation/retraction ratio at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
12. The extensible laminate of claim 1 , wherein the extensible laminate has an elongation/retraction ratio at least about 25 percent lower than a comparable extensible laminate that has not been previously stretched.
13. The extensible laminate of claim 1 , wherein the extensible laminate has a 7-day elongation/retraction ratio at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
14. The extensible laminate of claim 1 , wherein the extensible laminate has a 30-day elongation/retraction ratio at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
15. The extensible laminate of claim 1 , wherein the elastomeric sheet comprises a film including a styrene copolymer selected from styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-ethylene/butylene-styrene, styrene-ethylene/propylene-styrene and combinations thereof.
16. The extensible laminate of claim 1 , wherein the elastomeric sheet comprises a film including a single-site catalyzed ethylene-alpha olefin copolymer having a density of about 0.860 to about 0.900 grams per cubic centimeter.
17. The extensible laminate of claim 1 , wherein the elastomeric sheet comprises a breathable elastomeric film.
18. An extensible laminate comprising:
a necked nonwoven web; and
an elastomeric sheet,
wherein the necked nonwoven web and the elastomeric sheet, after lamination and prior to a cycling test, have been mechanically stretched in the cross direction to provide an extensible laminate having an elastic set value, measured during a first 100 percent elongation/retraction cycle of the cycling test, at least about 10 percent lower than a comparable extensible laminate that has not been previously stretched.
19. The extensible laminate of claim 18 , wherein the extensible laminate has an elastic set value at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
20. The extensible laminate of claim 18 , wherein the extensible laminate has an elastic set value at least about 30 percent lower than a comparable extensible laminate that has not been previously stretched.
21. The extensible laminate of claim 18 , wherein the extensible laminate has a 7-day elastic set value at least about 10 percent lower than a comparable extensible laminate that has not been previously stretched.
22. The extensible laminate of claim 18 , wherein the extensible laminate has a 30-day elastic set value at least about 10 percent lower than a comparable extensible laminate that has not been previously stretched.
23. The extensible laminate of claim 18 , wherein the extensible laminate has a lower hysteresis value than a comparable extensible laminate that has not been previously stretched.
24. The extensible laminate of claim 18 , wherein the extensible laminate has a lower elongation/retraction ratio than a comparable extensible laminate that has not been previously stretched.
25. The extensible laminate of claim 18 , wherein the extensible laminate has an elongation/retraction ratio at least about 20 percent lower than a comparable extensible laminate that has not been previously stretched.
26. The extensible laminate of claim 18 , wherein the extensible laminate has a 7-day elongation/retraction ratio at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
27. The extensible laminate of claim 18 , wherein the extensible laminate has a 30-day elongation/retraction ratio at least about 15 percent lower than a comparable extensible laminate that has not been previously stretched.
28. The extensible laminate of claim 18 , wherein the elastomeric sheet comprises a film including a styrene copolymer selected from styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-ethylene/butylene-styrene, styrene-ethylene/propylene-styrene and combinations thereof.
29. The extensible laminate of claim 18 , wherein the elastomeric sheet comprises a film including a single-site catalyzed ethylene-alpha olefin copolymer having a density of about 0.860 to about 0.900 grams per cubic centimeter.
30. The extensible laminate of claim 18 , wherein the elastomeric sheet comprises a breathable elastic film.
31. The extensible laminate of claim 1 , wherein the extensible laminate is breathable.
32. The extensible laminate of claim 1 , wherein the necked nonwoven web comprises a multilayer nonwoven web.
33. The extensible laminate of claim 1 , wherein the elastomeric sheet comprises a filled elastomeric sheet.
34. The extensible laminate of claim 1 , further comprising an additional extensible nonwoven web, wherein the elastomeric sheet is disposed between the reversibly necked nonwoven web and the additional extensible nonwoven web.
35. The extensible laminate of claim 1 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 50 percent.
36. The extensible laminate of claim 1 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 65 percent.
37. The extensible laminate of claim 1 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 75 percent.
38. The extensible laminate of claim 1 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 100 percent.
39. The extensible laminate of claim 18 , wherein the extensible laminate is breathable.
40. The extensible laminate of claim 18 , wherein the necked nonwoven web comprises a multilayer nonwoven web.
41. The extensible laminate of claim 18 , wherein the elastomeric sheet comprises a filled elastomeric sheet.
42. The extensible laminate of claim 18 , further comprising an additional extensible nonwoven web, wherein the elastomeric sheet is disposed between the reversibly necked nonwoven web and the additional extensible nonwoven web.
43. The extensible laminate of claim 18 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 50 percent.
44. The extensible laminate of claim 18 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 65 percent.
45. The extensible laminate of claim 18 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 75 percent.
46. The extensible laminate of claim 18 , wherein the necked nonwoven web and the elastomeric sheet after lamination have been mechanically stretched in the cross direction by at least about 100 percent.