Segmented glass laminate
View Patent ↗A flexible laminate is disclosed which includes a flexible support as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer and wherein the first or the second layer is a non-continuous, segmented layer. In the embodiment of the figure, a plastic foil 1 is provided with a plurality of thin adjacent glass segments 2 , which are separated by a space 3 . The laminate can be provided with functional layers, e.g. using a web coating or printing process, and can then be cut easily in the space between the segments so as to obtain a plurality of glass laminates.
1. A laminate in sheet or web form windable around a core, the laminate comprising a support windable around a core as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the first or the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry and the glass is chemically hardened glass.
2. A laminate in sheet or web form windable around a core, the laminate comprising a metal foil, paper or plastic support as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the first or the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry, wherein the laminate is provided with a functional layer.
3. A laminate in sheet or web form windable around a core, the laminate comprising a support as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer, whrein the first or the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry, wherein the laminate is provided with a functional layer selected from the group consisting of an electroconductive layer, a liquid crystal orientation layer, a colour filter layer, a phosphor layer, a large number of microtips, an electroluminescent layer, a hole-injection layer, a transparent anode and a reflecting cathode.
4. A laminate in sheet or web form windable around a core, the laminate comprising a metal foil, paper or plastic support windable around a core as a first layer and borosilicate glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry.
5. Laminate according to claim 4 , wherein the glass has a thickness in the range from 30 μm to 350 μm.
6. Laminate according to claim 4 , wherein the glass has a thickness in the range from 50 μm to 200 μm.
7. Laminate according to claim 4 , wherein an adhesive is present between the first and the second layer.
8. Laminate according to claim 4 , wherein the support windable around a core is plastic formed of one or more material(s) selected from the group consisting of polyether resin, cellulose resins, polyether-sulfone, acrylic resin, poly(ethylene terephthalate) resin, phenoxy resin, phenoxy-urethane resin, urethan resin, polyether-ketone resin, polyether-ether-ketone resin, polyimideamide resin, polycarbonate resin, polysulfone resin, polyethylene resin, polypropylene resin, a copolymer of acrylonitrile, styrene and butadiene and cyclo-olefin copolymers.
9. A laminate in sheet or web form windable around a core, the laminate comprising a support windable around a core as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the first layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry and said first layer is a metal foil, paper or plastic.
10. Laminate according to claim 9 , wherein the glass has a thickness in the range from 30 μm to 350 μm.
11. Laminate according to claim 9 , wherein the glass has a thickness in the range from 50 μm to 200 μm.
12. Laminate according to claim 9 , wherein an adhesive is present between the first and the second layer.
13. Laminate according to claim 9 , wherein the support windable around core is metal foil, paper or plastic.
14. Laminate according to claim 9 , wherein the support windable around a core is plastic formed of one or more material(s) selected from the group consisting of polyether resin, celluose resins, polyether-sulf one, acrylic resin, poly(ethylen terephthalate) resin, phenoxy resin, phenoxy-urethane resin, urethane resin, polyether-ketone resin, polyether-etier-ketone resin, polyimideamide resin, polycarbonate resin, polysulfone resin, polyethylene resin, polypropylene resin, a copolymer of acrylonitrile, styrene and butadien and cyclo-olefin copolymers.
15. A method of making a laminate in sheet or web form windable around a core, the laminate having a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry, said method comprising the steps of
positioning a plurality of sheets consisting of a first material with respect to a layer consisting of a second material;
laminating said sheets to said layer;
wherein the first or the second material is borosilicate glass having a thickness in the range from 10 μm to 500 μm and the first or the second material which is not said borosilicate glass is metal foil, paper or plastic.
16. A method of making a laminate in sheet or web form windable around a core, the laminate having a non-continuous layer which comprises plurality of adjacent or adjoining segments having a controlled size and geometry, said method comprising the steps of
laminating a first layer consisting of a first material to a second layer consisting of a second material;
cutting the first or the second layer into segments;
wherein the first or the second material is borosilicate glass having a thickness in the range from 10 μm to 500 μm and the first or the second material which is not said borosilicate glass is metal, foil, paper or plastic.
17. A method of making a flat panel display, a photovoltaic cell or a light emitting diode comprising the step of providing with a functional layer a laminate in sheet or web form windable around a core, the laminate comprising a metal foil, paper or plastic support as a first layer and borosilicate glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the first or the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry.
18. A method of making a flat panel display, a photovoltaic cell or a light emitting diode comprising the step of providing with a functional layer selected from the group consisting of an electroconductive layer, a liquid crystal orientation layer, a colour filter layer, a phosphor layer, a large number of microtips, an electroluminescent layer, a hole-injection layer, a transparent anode and a reflecting cathode, a laminate in sheet or web form windable around a core, the laminate comprising a support as a first layer and glass having a thickness in the range from 10 μm to 500 μm as a second layer, wherein the first or the second layer is a non-continuous layer which comprises a plurality of adjacent or adjoining segments having a controlled size and geometry.