Surface for use on implantable device
View Patent ↗An attachment surface for an implantable device has an irregular pattern formed through a process including masking, chemical or electrochemical etching, blasting and debris removal steps. Surface material is removed from the implant surface without stress on the adjoining material and the process provides fully dimensional fillet radii at the base of the surface irregularities. This irregular surface is adapted to receive the ingrowth of bone material and to provide a strong anchor for that bone material which is resistant to cracking or breaking. The surface is prepared through an etching process which utilizes the random application of a maskant and subsequent etching in areas unprotected by the maskant. This chemical etching process is repeated a number of times as necessitated by the nature of the irregularities required in the surface. The blasting and debris removal steps produce microfeatures on the surface that enhance the ingrowth of bone material.
1. An irregular exterior surface portion integral to a substrate material which is particularly adapted to be joined to a second material, the surface portion to be so joined comprising a plurality of randomly sized and spaced protrusions having micro-features located upon said surface portion, produced by the method comprising the steps of:
a) masking said surface portion of said substrate material in a random pattern with a maskant material, such that less than the entire surface portion is covered thereby;
b) etching said surface portion such that said substrate material is removed thereby in areas uncovered by said maskant material, and areas covered by said maskant material are left intact;
c) removing said maskant material;
d) repeating said masking, etching and maskant removing steps upon said surface portion until a desired surface irregularity is achieved;
e) blasting the etched surface portion with a blast media to create said micro-features that is dissolvable in a solvent, said blasting resulting in blast media particulate debris being affixed to said surface portion; and
f) removing said blast media particulate debris affixed to said surface portion during said blasting step using said solvent without substantial deleterious effect upon said substrate material.
2. An irregular exterior surface portion, produced by the method described in claim 1 , said step of removing said blast media particulate debris comprising exposing said surface portion to a nitric acid solvent.
3. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said masking, etching and maskant removing steps are repeated two additional times prior to said blasting step.
4. An irregular exterior surface portion, produced by the method as described in claim 3 , wherein each of said etching steps removes approximately 0.005 inches of said surface portion.
5. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said blast media comprises a fractured shot blast media.
6. An irregular exterior surface portion, produced by the method as described in claim 5 , wherein said blast material is fractured metallic shot.
7. An irregular exterior surface portion, produced by the method as described in claim 6 , wherein said blast material is comprised of steel.
8. An irregular exterior surface portion, produced by the method as described in claim 7 , wherein said blast material is fractured steel shot.
9. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said blast material has a grit rating between G10 and G120.
10. An irregular exterior surface portion, produced by the method as described in claim 9 , wherein said blast material has a grit rating of G40.
11. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said blasting step lasts for between 1 and 30 seconds.
12. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said blasting step utilizes a blasting pressure in the range of 20 to 120 psi.
13. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein during said blasting step, a distance between a source of said blast media and said surface portion is less than twelve inches.
14. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein during said blasting step a stream of said blast media is directed toward said surface portion at an incident angle of between 5 and 90 degrees.
15. An irregular exterior surface portion, produced by the method as described in claim 1 , wherein said blast media comprises a fractured shot blast media, wherein said blasting step lasts for between 1 and 30 seconds, wherein said blasting step utilizes a blasting pressure in the range of 20 to 120 psi, wherein during said blasting step, a distance between a source of said blast media and said surface portion is less than twelve inches and a stream of said blast media is directed toward said surface portion at an incident angle of between 5 and 90 degrees.
16. An irregular exterior surface portion, produced by the method as described in claim 15 , further comprising repeating said masking, etching and maskant removing steps upon said surface portion until a desired surface irregularity is achieved prior to said blasting step.
17. An irregular exterior surface portion, produced by the method as described in claim 16 , wherein said masking, etching and maskant removing steps are repeated two additional times prior to said blasting step.
18. An irregular exterior surface portion, produced by the method as described in claim 17 , wherein each of said etching steps removes approximately 0.005 inches of said surface portion.
19. An irregular exterior surface portion, produced by the method as described in claim 15 , wherein said blast media is G40 fractured steel shot.
20. An irregular exterior surface portion, produced by the method as described in claim 15 , wherein said blasting step lasts for between 2 and 6 seconds, wherein said blasting step utilizes a blasting pressure of approximately 80 psi, and wherein during said blasting step, said distance between said source of said blast media and said surface portion is between 2 and 4 inches and said stream of said blast media is directed toward said surface portion at an incident angle of between 40 and 50 degrees.
21. An irregular exterior surface portion, produced by the method as described in claim 20 , further comprising repeating said masking, etching and maskant removing steps upon said surface portion until a desired surface irregularity is achieved prior to said blasting step.
22. An irregular exterior surface portion, produced by the method as described in claim 21 , wherein said masking, etching and maskant removing steps are repeated two additional times prior to said blasting step.
23. An irregular exterior surface portion, produced by the method as described in claim 22 , wherein each of said etching steps removes approximately 0.005 inches of said surface portion.
24. An irregular exterior surface portion, produced by the method as described in claim 20 , wherein said blast media is G40 fractured steel shot.
25. An irregular exterior surface portion, produced by the method as described in claim 2 , wherein said solvent comprises 40% nitric acid, by volume, in deionized water.
26. An irregular exterior surface portion, produced by the method as described in claim 25 , wherein said solvent is maintained at room temperature at a specific gravity between 1.175 and 1.225 (60°/60°).
27. An irregular exterior surface portion, produced by the method as described in claim 2 , wherein said debris removal lasts for at least six hours.
28. An irregular exterior surface portion, produced by the method as described in claim 1 , further comprising the step of exposing said surface portion to a hydrofluoric acid/nitric acid bath before said step of removing said blast media particulate debris.
29. An irregular exterior surface portion, produced by the method as described in claim 28 , wherein said hydrofluoric acid/nitric acid bath is maintained at room temperature and consists of 11 gallons nitric acid 42 Degrees Baume, 6.5 gallons hydrofluoric acid 70%, 4 pounds titanium (CP), balance deionized water per 100 gallons thereof.
30. An irregular exterior surface portion, produced by the method as described in claim 2 , wherein said blast media comprises a G40 fractured steel shot, wherein said blasting step lasts for between 2 and 6 seconds, wherein said blasting step utilizes a blasting pressure of approximately 80 psi, wherein during said blasting step, a distance between a source of said blast media and said surface portion is between 2 and 4 inches and a stream of said blast media is directed toward said surface portion at an incident angle of between 40 and 50 degrees, wherein said masking, etching and maskant removing steps are repeated two additional times prior to said blasting step, each of said etching steps removing approximately 0.005 inches of said surface portion, and wherein said solvent comprises 40% nitric acid, by volume, in deionized water.
31. An irregular exterior surface portion, produced by the method as described in claim 30 , further comprising the step of exposing said surface portion to a hydrofluoric acid/nitric acid bath before said step of removing said blast media particulate debris, said hydrofluoric acid/nitric acid bath being maintained at room temperature and comprising 11 gallons nitric acid 42 Degrees Baume, 6.5 gallons hydrofluoric acid 70%, 4 pounds titanium (CP), balance deionized water per 100 gallons thereof.