Filter material and method of making same
View Patent ↗Non-shedding light duty fibrous filter material containing activated carbon and/or other sorbtive granules is disclosed having a thickness of ⅛ inch to ⅜ inch and composed entirely of low melt fibers of 4 to 15 denier. Heavy duty filter material, also of a non-shedding clean character, is of ¾ to 1 inch thickness and comprises a mixture of 70% structural fibers and 30% low melt fibers.
1. Fluid filter material capable of being rolled comprising:
a fiber web of structural fibers having substantially uniformly distributed there through sorbtive particles of a size ranging from about 6/8 mesh thru 12/28 mesh and a loading of from about 100 to 400 grams per square foot; and
said web including low melt fibers adhered to the structural fibers and to the sorbtive particles and coalesced with each other providing a more open structure for increased air flow.
2. Fluid filter material for light duty applications comprising:
a fiber web of between about ⅛ inch to ⅜ inch thickness and composed substantially entirely of low melt fibers of 4 to 20 denier;
sorbtive particles distributed substantially uniformly through the fiber web and being of a size ranging from about 20/50 to 30/80 mesh;
the sorbtive particle loading lying in the range from about 5 grams per square foot to about 90 grams per square foot; and
said low melt fibers having been heated to adhere to each other and to said sorbtive particles to retain the particles in position in the fired web all without the use of adhesives.
3. The fluid filter material of claim 2 wherein the low melt fibers comprise about a 50/50 blend of (1) a 15 denier fiber and (2) a 4 denier fiber.
4. A low sorbtive particle fluid filter comprising:
a fibrous mat having between about 5 to 12 grams of sorbtive particles per square foot; and
said fibrous mat consisting of up to about 33% of 15 denier structural fibers with the balance being low melt fibers.
5. A light duty fluid filter material comprising, in combination:
a fiber web of from about ⅛″ to about ⅜″ thickness consisting entirely of low melt fibers of 4 to 15 denier;
sorbtive particles of a size ranging from about 20/50 to 30/80 mesh distributed uniformly through the web; and
said low melt fibers having been heated sufficiently to cause the fibers to adhere to each other around the particles forming interstices trapping the particles therein after the fibers are cooled.
6. The filter material of claim 5 wherein the heating of the low melt fibers is sufficient to cause the fibers to adhere to the particles helping to retain particles in position in the web after the fibers are cooled.
7. A fluid filter comprising, in combination:
a fiber web of from about one-inch thickness for heavy duty applications to about ⅛-inch thickness for light duty applications; said web formed of about 70% 200-denier structural fibers and about 30% 15-denier low melt fibers for heavy duty applications, down to about a 50/50 mixture of about 15-denier low melt fibers and about 4-denier low melt fibers for light duty applications;
sorbtive particles distributed through the fiber web ranging from about 300 grams per square foot of 6/12 mesh for heavy duty applications to about 5 grams per square foot at 20/50 mesh for light duty applications; and
wherein the low melt fibers have been heated to cause the lower denier fibers to coalesce with each other for light duty applications and also with each other and with the structural fibers for heavy duty applications, thereby providing a more open structure for improved air flow for both heavy and light duty applications and entrapment of the sorbtive particles in the interstices of the structure, all without the use of adhesives.
8. The filter material of claim 7 characterized in that for light duty applications the web ranges from about ⅛inch to about ⅜ inch.
9. The filter material of claim 8 characterized in that for light duty applications the sorbtive particles loading lies in the range from about 5 grams per square foot to 90 grams per square foot.
10. The filter material of claim 7 wherein the particles are activated carbon.
11. The filter material of claim 7 wherein for heavy duty applications the sorbtive particle loading ranges from about 300 grams per square foot to about 100 grams per square foot, and the sorbtive particles size range from 6/8 to 12/28 mesh.
12. The filter material of claim 7 wherein for heavy duty applications the web thickness ranges from about ¾ inch to one inch plus or minus ⅛ inch.