Low pigments costs algae-retardant roofing granule products containing metallic copper
View Patent ↗Algae-resistant roofing granules consisting of one or two coats of a fired semi-ceramic composition having a metallic copper powder which does not significantly affect the color tint strength of the pigment contained in the coatings.
1. Algae-retardant roofing granules having enhanced ability over an extended period of time to release ions to prevent or inhibit the growth of algae and fungi upon atmospheric exposure of roofing surfaces coated with such granules comprising:
a) a base material of crushed mineral aggregates in the form of granules coated with:
b) a single layer of semi-ceramic composition consisting of a fired silicate-clay matrix containing about 0 to about 25 pounds of pigment per ton of base material; and from about 2 pounds to about 20 pounds of metallic copper powder having a particle size range of from about 5 to about 75 microns.
2. The algae-retardant roofing granules of claim 1 wherein said silicate-clay matrix contains from about 0.5 pounds to 20 pounds of pigment per ton of base material; and from about 7 pounds to about 13 pounds of metallic copper powder.
3. The algae-retardant roofing granules of claim 1 wherein said metallic copper powder has an average particle size of from about 5 to 50 microns.
4. The algae-retardant roofing granules of claim 1 wherein said pigment is selected from the group consisting of: carbon black, titanium dioxide, chromium oxide, yellow iron oxide, ultramarine blue, zinc sulfide, red iron oxide and metallic ferrites.
5. Algae-retardant roofing granules having enhanced ability over an extended period of time to release algicidal ions to prevent or inhibit the growth of algae and fungi upon atmospheric exposure of roofing surfaces coated with such granules comprising:
a) a base material of crushed mineral aggregates in the form of granules coated with:
b) a first or inner layer of semi-ceramic composition consisting of a fired silicate-clay matrix containing from about 0 to about 25 pounds of pigment per ton of base material; and from about 2 pounds to about 20 pounds of metallic copper powder having a particle size range of from about 5 to about 75 microns; and
c) a second layer of semi-ceramic composition, coated on the first or inner layer of the semi-ceramic composition, consisting of a fired silicate-clay matrix containing: of from about 0 to about 25 pounds of pigment per ton of base material; and from about 2 pounds to about 20 pounds of metallic copper powder.
6. The algae-retardant roofing granules of claim 5 wherein said silicate-clay matrix contains from about 0.5 pounds to 20 pounds of pigment, and from about 7 pounds to about 13 pounds of metallic copper powder.
7. The algae-retardant roofing granules of claim 5 wherein said metallic copper powder has an average particle size of from about 5 to 50 microns.
8. The algae-retardant roofing granules of claim 5 wherein said pigment is selected from the group consisting of: carbon black, titanium dioxide, chromium oxide, yellow iron oxide, ultramarine blue, zinc sulfide, red iron oxide and metallic ferrites.
9. A process of preparing algae-retardant roofing granules comprising the steps of:
a) crushing and sizing a base mineral aggregate to form granules therefrom;
b) preheating the granules to about 210° F.-230° F.;
c) coating the preheated granules with a single coat of semi-ceramic composition of an aqueous slurry comprising: about 30-55 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 20-35 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
d) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
e) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
f) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; and
g) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate.
10. Roofing shingles prepared by a process of preparing roofing shingles consisting of a substrate and colored roofing granules embedded in the substrate comprising the steps of:
a) crushing and sizing a base mineral aggregate to form granules therefrom;
b) preheating the granules to about 210° F.-230° F.
c) coating the preheated granules with a single coat of semi-ceramic composition of an aqueous slurry comprising: about 30-55 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 20-35 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
d) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
e) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
f) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; and
g) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate, wherein said substrate comprises an organic asphalt saturated felt material.
11. A method of protecting asphalt roof shingles against algae and fungi comprising the steps of:
a) providing asphalt coated roof shingles;
b) crushing and sizing a base mineral aggregate to form granules therefrom;
c) preheating the granules to about 210° F.-230° F.
d) coating the preheated granules with a single coat of semi-ceramic composition of an aqueous slurry comprising: about 30-55 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 20-35 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
e) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
f) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
g) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.;
h) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate; and
i) applying said treated granules to said roof shingles to obtain algae- and fungi-resistant roof shingles.
12. A process of preparing algae-retardant roofing granules comprising the steps of:
a) crushing and sizing a base mineral aggregate to form granules therefrom;
b) preheating the granules to about 210° F.-230° F.;
c) coating the preheated granules with a first or inner coat of semi-ceramic composition of an aqueous slurry comprising: about 30-60 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 25-40 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment; and about 2-20 pounds of metallic copper powder;
d) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
e) kiln-firing the pre-dried granules at a temperature of from about 700° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
f) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.;
g) coating the cooled granules with a second coat of a semi-ceramic composition of an aqueous slurry comprising: about 30 to 60 pounds of 38% solid sodium silicate solution per ton of said base mineral aggregate; about 20 to 30 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment; and about 2-20 pounds of metallic copper powder;
h) pre-drying the double coated granules to a moisture content of about 0.2 to 0.5%;
i) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
j) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; and
k) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate.
13. Roofing shingles prepared by a process of preparing roofing shingles consisting of a substrate and colored roofing granules embedded in the substrate comprising the steps of:
a) crushing and sizing a base mineral aggregate to form granules therefrom;
b) preheating the granules to about 210° F.-230° F.;
c) coating the preheated granules with a first or inner coat of semi-ceramic composition of an aqueous slurry comprising: about 30-60 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 25-40 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
d) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
e) kiln-firing the pre-dried granules at a temperature of from about 700° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
f) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.;
g) coating the cooled granules with a second coat of a semi-ceramic composition of an aqueous slurry comprising: about 30 to 60 pounds of 38% solid sodium silicate solution per ton of said base mineral aggregate; about 20 to 30 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
h) pre-drying the double coated granules to a moisture content of about 0.2 to 0.5%;
i) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
j) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; and
k) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate, wherein said substrate comprises an organic asphalt saturated felt material.
14. A method of protecting asphalt-coated roof shingles against algae and fungi comprising the steps of:
a) providing asphalt-coated roof shingles;
b) crushing and sizing a base mineral aggregate to form granules therefrom;
c) preheating the granules to about 210° F.-230° F.;
d) coating the preheated granules with a first or inner coat of semi-ceramic composition of an aqueous slurry comprising: about 30-60 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 25-40 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment; and about 2-20 pounds of metallic copper powder;
e) pre-drying the single-coated granules to a moisture content of about 0.2% to 0.5%;
f) kiln-firing the pre-dried granules at a temperature of from about 700° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
g) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.;
h) coating the cooled granules with a second coat of a semi-ceramic composition of an aqueous slurry comprising: about 30 to 60 pounds of 38% solid sodium silicate solution per ton of said base mineral aggregate; about 20 to 30 pounds Kaolin clay per ton of said base mineral aggregate; about 0-15 pounds of a pigment, and about 2-20 pounds of metallic copper powder;
i) pre-drying the double coated granules to a moisture content of about 0.2 to 0.5%;
j) kiln-firing the pre-dried granules at a temperature of from about 840° F. to 960° F. to form an insolubilized silicate-clay matrix coating in which the metallic copper powder and the pigment are uniformly distributed;
k) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; and
l) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate; and
m) applying said treated granules to said roof shingles to obtain algae- and fungi-resistant roof shingles.
15. A process of preparing algae-retardant green granules containing copper polychlorophthalocyanine pigment comprising the steps of:
a) crushing and sizing a base mineral aggregate to form granules therefrom;
b) preheating the granules to about 170° F.-200° F.;
c) coating the preheated granules with a semi-ceramic composition of an aqueous slurry comprising: about 30-55 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 0-15 pounds of a pigment; and about 2-20 pounds of metallic copper powder;
d) pre-drying the first or inner coated granules to a moisture content of about 0.2% to 0.5%;
e) kiln-firing the pre-dried granules at a temperature of from about 450° F. to 550° F.;
f) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; in the presence of an AlCl 3 or MgCl 2 solution to chemically insolubilize said coating; and
g) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate.
16. A method of protecting asphalt-coated roof shingles against algae and fungi comprising the steps of:
a) providing asphalt-coated roof shingles;
b) crushing and sizing a base mineral aggregate to form granules therefrom;
c) preheating the granules to about 170° F.-200° F.;
d) coating the preheated granules with a first or inner coat of semi-ceramic composition of an aqueous slurry comprising: about 30-55 pounds of 38% solids sodium silicate solution per ton of said base mineral aggregate; about 0-15 pounds of a pigment; and about 2-20 pounds of metallic copper powder;
e) pre-drying the first or inner coated granules to a moisture content of about 0.2% to 0.5%;
f) kiln-firing the pre-dried granules at a temperature of from about 450° F. to 550° F.;
g) cooling the kiln-fired granules to a temperature of from about 200° F. to about 220° F.; in the presence of an AlCl 3 or MgCl 2 solution to chemically insolubilize said coating;
h) treating the granules with a mixture of a process oil and an organosilicone compound to impart dust control and adhesion to a substrate; and
i) applying said treated granules to said roof shingles to obtain algae- and fungi-resistant roof shingles.