Agents for reducing the force-to-crush (FTC) of high support flexible foams
View Patent ↗The present invention provides a high support (HS) and high support-high resilience (HS-HR) flexible polyurethane foams prepared by catalyzed reaction of one or more di- or polyisocyanates at an isocyanate index from about 70 to about 130 with: (a) a polyoxyalkylene polyol or polyoxyalkylene polyol blend having an average hydroxyl weight of at least about 1000 and an average primary hydroxyl content of at least about 25%; and (b) an effective amount of a blowing agent containing water; in the presence of from about 0.01 to about 0.5% parts by weight based on 100 parts by weight of said polyol component of a liquid hydrocarbon containing greater than 50% of polymerized butadiene. The high support (HS) and high support-high resilience (HS-HR) flexible polyurethane foams of the present invention have a reduced force to crush (FTC).
1. A high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam prepared by the catalyzed reaction of one or more di- or polyisocyanates at an isocyanate index from about 70 to about 130 with:
(a) a polyoxyalkylene polyol or polyoxyalkylene polyol blend having an average hydroxyl equivalent weight of at least about 1000 and an average primary hydroxyl content of at least about 25%; and
(b) an effective amount of a blowing agent comprising water,
in the presence of from about 0.01 to about 0.5 parts by weight based on 100 parts by weight of said polyol component (a) of a liquid hydrocarbon comprising greater than 50% of polymerized butadiene.
2. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said liquid hydrocarbon comprises from about 0.01 to about 0.3 parts by weight.
3. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said polyol component (a) comprises a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
4. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said polyol polyoxyalkylene blend comprises at least one polyol comprising a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
5. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said polyol blend further includes one or more polyol polymer dispersions effective to provide a solids content of from about 3 to about 50 weight percent based on the weight of said polyol blend.
6. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said isocyanate index is between about 80 and about 120.
7. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said isocyanate index is between about 90 and about 115.
8. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said blowing agent comprises water in an amount from about 1 to about 7 parts by weight per 100 parts of said polyol component (a).
9. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said blowing agent comprises water in an amount from about 1 to about 5 parts by weight per 100 parts of said polyol component (a).
10. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said liquid hydrocarbon is free of isocyanate reactive groups.
11. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said blowing agent further includes at least one member selected from the group consisting of dichloromethane, difluorodichloromethane, 1,1-dichloro-1-fluoroethane, 1,1,2-trichloro-1,2,2-trifluoroethane, hydrofluorocarbons (HFC's), perfluorocarbons (PFC's), lower alkanes low molecular weight ethers and ketones, air and liquid CO 2 under pressure.
12. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 1 , wherein said liquid hydrocarbon comprises polybutadiene.
13. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 12 , wherein less than 65% of unsaturation in said polybutadiene is of 1,2 vinyl type.
14. The high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam according to claim 12 , wherein less than 50% of unsaturation in said polybutadiene is of 1,2 vinyl type.
15. A method for producing a high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam comprising reacting one or more di- or polyisocyanates at an index from about 70 to about 130 and in the presence of a catalyst with
(a) a polyoxyalkylene polyol or polyoxyalkylene polyol blend having an average hydroxyl equivalent weight of at least about 1000 and an average primary hydroxyl content of at least about 25%, and
(b) an effective amount of a blowing agent comprising water,
in the presence of from about 0.01 to about 0.5 parts by weight based on 100 parts by weight of said polyol component of a liquid hydrocarbon comprising greater than 50% of polymerized butadiene.
16. The method according to claim 15 , wherein said polyol component (a) comprises a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
17. The method according to claim 15 , wherein said polyol polyoxyalkylene blend comprises at least one polyol comprising a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
18. The method according to claim 15 , wherein said polyol blend further includes one or more polyol polymer dispersions effective to provide a solids content of from about 3 weight percent to about 50 weight percent based on the weight of said polyol blend.
19. The method according to claim 15 , wherein said isocyanate index is between about 80 and about 120.
20. The method according to claim 15 , wherein said isocyanate index is between about 90 and about 115.
21. The method according to claim 15 , wherein said blowing agent comprises water in an amount from about 1 to about 7 parts by weight per 100 parts of said polyol component (a).
22. The method according to claim 15 , wherein said blowing agent comprises water in an amount from about 1 to about 5 parts by weight per 100 parts of said polyol component (a).
23. The method according to claim 15 , wherein said liquid hydrocarbon is free of isocyanate reactive groups.
24. The method according to claim 15 , wherein said blowing agent further includes at least one member selected from the group consisting of dichloromethane, difluorodichloromethane, 1,1-dichloro-1-fluoroethane, 1,1,2-trichloro-1,2,2-trifluoroethane, hydrofluorocarbons (HFC's), perfluorocarbons (PFC's), lower alkanes low molecular weight ethers and ketones, air and liquid CO 2 under pressure.
25. The method according to claim 15 , wherein said liquid hydrocarbon comprises polybutadiene.
26. The method according to claim 25 , wherein less than 65% of unsaturation in said polybutadiene is of 1,2 vinyl type.
27. The method according to claim 25 , wherein less than 50% of unsaturation in said polybutadiene is of 1,2 vinyl type.
28. A method of reducing force to crush (FTC) of a high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam comprising combining
a) a polyoxyalkylene polyol or polyoxyalkylene polyol blend having an average hydroxyl equivalent weight of at least about 1000 and an average primary hydroxyl content of at least about 25%,
b) an effective amount of a blowing agent comprising water,
c) from about 0.01 to about 0.5 parts by weight based on 100 parts by weight of said polyol component of a liquid hydrocarbon comprising greater than 50% of polymerized butadiene, and
reacting a), b) and c) in the presence of a catalyst with one or more di- or polyisocyanates at an index from about 70 to about 130, wherein the resulting high support (HS) or high support-high resilience (HS-HR) flexible polyurethane foam has a reduced force to crush (FTC).
29. The method according to claim 28 , wherein said polyol component a) comprises a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
30. The method according to claim 28 , wherein said polyol polyoxyalkylene blend comprises at least one polyol comprising a polyoxyalkylene polyol at least partially prepared in the presence of a double metal cyanide complex oxyalkylation catalyst.
31. The method according to claim 28 , wherein said polyol blend further includes one or more polyol polymer dispersions effective to provide a solids content of from about 3 weight percent to about 50 weight percent based on the weight of said polyol blend.
32. The method according to claim 28 , wherein said isocyanate index is between about 80 and about 120.
33. The method according to claim 28 , wherein said isocyanate index is between about 90 and about 115.
34. The method according to claim 28 , wherein said blowing agent comprises water in an amount from about 1 to about 7 parts by weight per 100 parts of said polyol component (a).
35. The method according to claim 28 , wherein said blowing agent comprises water in an amount from about 1 to about 5 parts by weight per 100 parts of said polyol component (a).
36. The method according to claim 28 , wherein said liquid hydrocarbon is free of isocyanate reactive groups.
37. The method according to claim 28 , wherein said liquid hydrocarbon comprises polybutadiene.
38. The method according to claim 37 , wherein less than 65% of unsaturation in said polybutadiene is of 1,2 vinyl type.
39. The method according to claim 37 , wherein less than 50% of unsaturation in said polybutadiene is of 1,2 vinyl type.
40. The method according to claim 28 , wherein said blowing agent further includes at least one member selected from the group consisting of dichloromethane, difluorodichloromethane, 1,1-dichloro-1-fluoroethane, 1,1,2-trichloro-1,2,2-trifluoroethane, hydrofluorocarbons (HFC's), perfluorocarbons (PFC's), lower alkanes low molecular weight ethers and ketones, air and liquid CO 2 under pressure.