Dental pastes, dental articles, and methods
View Patent ↗The present invention provides a dental paste, a dental article, methods of making and using the dental paste, and compositions prepared therefrom. In one embodiment, the dental paste includes (a) a filler including porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals and (b) a filler including non-aggregated primary silica particles, with the fillers being dispersed in a hardenable resin.
1. A dental paste comprising:
a hardenable resin;
a first filler dispersed in the resin, the first filler comprising aggregates of non-porous primary silica particles forming a porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals; and
a second filler dispersed in the resin, the second filler comprising non-aggregated non-porous primary silica particles having a silane treated surface and having an average diameter of at most 200 nanometers, wherein the paste comprises at least 55% by weight of the combined first and second fillers.
2. The dental paste of claim 1 wherein the paste comprises at least 60% by weight of the combined first and second fillers.
3. The dental paste of claim 1 wherein the ratio of the first filler to the second filler is at least 1:4 by weight.
4. The dental paste of claim 1 wherein the ratio of the first filler to the second filler is at most 4:1 by weight.
5. The dental paste of claim 1 wherein the first filler comprises a silica gel.
6. The dental paste of claim 1 wherein the first filler comprises a silica cluster.
7. The dental paste of claim 1 wherein the porous, non-pyrogenic silica comprises aggregates of primary silica particles having an average particle size of about 5 nanometers to about 120 nanometers.
8. The dental paste of claim 7 wherein the aggregated silica has an average size of at least 1 micrometer.
9. The dental paste of claim 7 wherein the aggregated silica has an average size of about 1 micrometer to about 10 micrometers.
10. The dental paste of claim 7 wherein the aggregated silica has an average aspect ratio of at most 4:1.
11. The dental paste of claim 1 wherein the first filler has a bulk density of at least 0.4 g/cm.sup.3.
12. The dental paste of claim 1 wherein the hardenable resin is selected from the group consisting of acrylates, methacrylates, epoxies, and mixtures thereof.
13. The dental paste of claim 1 further comprising an initiator.
14. The dental paste of claim 1 wherein the paste is substantially non-sticky.
15. The dental paste of claim 1 having a String Work Done/Hardness value of at most 0.5.
16. The dental paste of claim 1 wherein the paste forms a material selected from the group consisting of dental restoratives, dental adhesives, casting materials, dental cements, dental sealants, and dental coatings.
17. The dental paste of claim 1 wherein the paste, upon hardening, has one or more properties selected from the group consisting of: a contrast ratio of at most 50, a MacBeth value of at most 0.4, a volumetric shrinkage of at most 4%, a diametral tensile strength of at least 15 MPa, a compressive strength of at least 35 MPa, and a loss in polish of at most 3% after 500 brushes in a polish retention test.
18. A method of preparing a dental paste comprising:
dispersing in a hardenable resin a first filler comprising aggregates of substantially non-porous primary silica particles forming a porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals; and
dispersing in the hardenable resin a second filler comprising non-aggregated substantially non-porous primary silica particles having a silane treated surface and having an average particle size of at most 200 nanometers to form a paste, wherein the paste comprises at least 55% by weight of the combined first and second fillers.
19. A dental article comprising:
a hardened resin;
a first filler dispersed in the hardened resin, the first filler comprising aggregates of substantially non-porous primary silica particles forming porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals;
and a second filler dispersed in the hardened resin, the second filler comprising non-aggregated substantially non-porous primary silica particles having a silane treated surface and having an average particle size of at most 200 nanometers, wherein the article comprises at least 55% by weight of the combined first and second fillers.
20. The dental article of claim 19 wherein the article is selected from the group consisting of dental mill blanks, dental prostheses, orthodontic devices, artificial crowns, anterior fillings, posterior fillings, and cavity liners.
21. The dental article of claim 19 having one or more properties selected from the group consisting of: a contrast ratio of at most 50, a MacBeth value of at most 0.4, a diametral tensile strength of at least 15 MPa, a compressive strength of at least 35 MPa, and a loss in polish of at most 30% after 500 brushes in a polish retention test.
22. A method of preparing a dental article comprising:
dispersing a first filler in a hardenable resin, the first filler comprising aggregates of substantially non-porous primary silica particles forming porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals;
dispersing a second filler in the resin, the second filler comprising non-aggregated substantially non-porous primary silica particles having a silane treated surface and having an average particle size of at most 200 nanometers to form a paste,
wherein the paste comprises at least 55% by weight of the combined first and second fillers; and hardening the paste to fabricate a dental article selected from the group consisting of dental mill blanks, dental prostheses, orthodontic devices, artificial crowns, anterior fillings, posterior fillings, and cavity liners.
23. The method of claim 22 further comprising changing the topography of the paste before hardening the paste.