Hydrogenated nitrile rubbers with improved low-temperature properties
View Patent ↗Hydrogenated copolymers of an unsaturated nitrile, butadiene and isoprene, wherein the molar ratio of butadiene to isoprene is less than 3:1, display valuable low temperature properties.
1. A hydrogenated copolymer comprising an unsaturated nitrile, butadiene and isoprene, wherein the molar ratio of butadiene to isoprene is between 0.75:1 to 1:0.75, and wherein the unsaturated nitrile content is between 15 to 25% based on the copolymer.
2. A copolymer according to claim 1 , wherein the unsaturated nitrile is acrylonitrile.
3. A copolymer according to claim 2 , wherein the unsaturated nitrile is methacrylonitrile.
4. A copolymer according to claim 1 which has a residual double bond content of 30% or less.
5. A copolymer according to claim 4 , wherein the residual double bond content is 10% or less.
6. A process for preparing a hydrogenated copolymer comprising an unsaturated nitrite, butadiene and isoprene comprising the steps of
copolymerizing the unsaturated nitrite, butadiene and isoprene, wherein the molar ratio of butadiene to isoprene is between 0.75:1 to 1:0.75, and wherein the unsaturated nitrile content is between 15 to 25% based on the copolymer and,
selectively hydrogenating the copolymer obtained.
7. A process according to claim 6 , wherein the selective hydrogenation is carried out in the presence of a rhodium-containing compound as catalyst and a co-catalyst ligand.
8. A process according to claim 7 , wherein the rhodium-containing compound is tris(triphenylphosphine)-rhodium (I) chloride and the co-catalyst ligand is triphenylphosphine.