Paper release compositions having improved adhesion to paper and polymeric films
View Patent ↗The present invention relates to curable alkenyl based silicone release coating compositions having improved adhesion to paper and polymeric substrates. Furthermore the present invention relates to the process for making a silicone release coating with improved adhesion to paper and polymeric substrates.
1. An aqueous emulsion comprising a release composition, said release composition comprising:
(A) additives for anchorage of release coatings consisting essentially of:
(R a SiO 4−a)/2 ) n
wherein:
n is an integer greater than 3; a is from 1 to 3; R is independently selected from the group consisting of a carboxylic acid anhydride containing radical having from one to forty carbon atoms, monovalent hydrocarbon radicals, monovalent hydrocarbonoxy radicals, and hydride atoms, with at least one carboxylic acid anhydride and hydride being present on the molecule;
(B) a curable alkenyl silicone having the formula:
M Vi a T b D c M d
wherein:
a and b have values ranging from 2 to 5; c is an integer ranging from about 50 to about 1,000; d has a value ranging from 0 to about 0.5; and a +d>b;
M Vi =R 1 3−p R 2 p SiO 1/2 , wherein: R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; R 2 is independently selected from the group consisting of terminal olefinic monovalent hydrocarbon radicals having two to forty carbon atoms and alkenyl groups having two to ten carbon atoms; p ranges from 1 to 3;
T=R 3 SiO 3/2 , wherein: R 3 is independently selected from the group consisting of R 1 and R 2 ;
D=R 4 R 5 SiO 2/2 , wherein: R 4 and R 5 are each independently selected from the group consisting of R 1 and R 2 ;
M=R 1 3 SiO 1/2 , wherein: each R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl;
(C) a hydrogen siloxane selected from the group consisting of:
MD e D′ f M, MD′ f M, MD e D′ f M′, M′D e D′ f M, and M′D e M′
wherein:
M=R′ 3 SiO 1/2 ; M′=H g R′ 3−g SiO 1/2 ; D=R′R′SiO 2/2 ; and D′=R′HSiO 2/2 ; wherein each R′ in M, M′, D, and D′ is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; the subscripts e and f may be zero or positive whereby the sum of e and f ranges from about 10 to about 100 subject to the limitation that the sum of f and g is two or greater; and
wherein said composition has a viscosity that ranges from about 100 to about 10,000 centipoise.
2. The aqueous emulsion of claim 1 , wherein the hydrogen siloxane is selected from the group consisting of MD e D′ f M, MD′ f M, and mixtures thereof wherein the subscripts e and f may be zero or positive whereby the sum of e and f ranges from about 10 to about 100 subject to the limitation that the sum off and g is two or greater.
3. A curable aqueous emulsion comprising a curable release coating composition, said release composition comprising:
(A) additives for anchorage of release coatings consisting essentially of:
(R a SiO 4−a)/2 ) n
wherein:
n is an integer greater than 3; a is from 1 to 3; R is independently selected from the group consisting of a carboxylic acid anhydride containing radical having from one to forty carbon atoms, monovalent hydrocarbon radicals, monovalent hydrocarbonoxy radicals, and hydride atoms, with at least one carboxylic acid anhydride and hydride being present on the molecule;
(B) a alkenyl silicone having the formula:
M Vi a T b D c M d
wherein:
a and b have values ranging from 2 to 5; c is an integer ranging from about 50 to about 1,000; d has a value ranging from 0 to about 0.5; and a +d>b;
M Vi =R 1 3−p R 2 p SiO 1/2 , wherein: R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; R 2 is independently selected from the group consisting of terminal olefinic monovalent hydrocarbon radicals having two to forty carbon atoms and alkenyl groups having two to ten carbon atoms; p ranges from 1 to 3;
T=R 3 SiO 3/2 , wherein: R 3 is independently selected from the group consisting of R 1 and R 2 ;
D=R 4 R 5 SiO 2/2 , wherein: R 4 and R 5 are each independently selected from the group consisting of R 1 and R 2 ;
M=R 1 3 SiO 1/2 , wherein: each R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl;
(C) a hydrogen siloxane selected from the group consisting of:
MD e D′ f M, MD′ f M, MD e D′ f M′, M′D e D′ f M, and M′D e M′
wherein:
M=R′ 3 SiO 1/2 ; M′=H g R′ 3−g SiO 1/2 ; D=R′ R′SiO 2/2 ; and D′=R′ HSiO 2/2 ; wherein each R′ in M, M′, D, and D′ is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; the subscripts e and f may be zero or positive whereby the sum of e and f ranges from about 10 to about 100 subject to the limitation that the sum of f and g is two or greater;
(D) a hydrosilylation catalyst; and
(E) an inhibitor;
wherein said composition has a viscosity that ranges from about 100 to about 10,000 centipoise.
4. An aqueous emulsion comprising a curable release coating composition, said release composition comprising:
(A) additives for anchorage of release coatings consisting essentially of:
(R a SiO 4−a)/2 ) n
wherein:
n is an integer greater than 3; a is from 1 to 3; R is independently selected from the group consisting of a carboxylic acid anhydride containing radical having from one to forty carbon atoms, monovalent hydrocarbon radicals, monovalent hydrocarbonoxy radicals, and hydride atoms, with at least one carboxylic acid anhydride and hydride being present on the molecule;
(B) a alkenyl silicone having the formula:
M Vi a T b D c M d
wherein:
a and b have values ranging from 2 to 5; c is an integer ranging from about 50 to about 1,000; d has a value ranging from 0 to about 0.5; and a+d>b;
M Vi =R 1 3−p R 2 p SiO 1/2 , wherein: R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; R 2 is independently selected from the group consisting of terminal olefinic monovalent hydrocarbon radicals having two to forty carbon atoms and alkenyl groups having two to ten carbon atoms; p ranges from 1 to 3;
T=R 3 SiO 3/2 , wherein: R 3 is independently selected from the group consisting of R 1 and R 2 ;
D=R 4 R 5 SiO 2/2 , wherein: R 4 and R 5 are each independently selected from the group consisting of R 1 and R 2 ;
M=R 1 3 SiO 1/2 , wherein: each R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl;
(C) a hydrogen siloxane selected from the group consisting of:
MD e D′ f M, MD′ f M, MD e D′ f M′, M′D e D′ f M, and M′D e M′
wherein:
M=R′ 3 SiO 1/2 ; M′=H g R′ 3−g SiO 1/2 ; D=R′R′SiO 2/2 ; and D′=R′HSiO 2/2 ; wherein each R′ in M, M′, D, and D′ is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms, methyl, trifluoropropyl, and phenyl; the subscripts e and f may be zero or positive whereby the sum of e and f ranges from about 10 to about 100 subject to the limitation that the sum of f and g is two or greater;
(D) a hydrosilylation catalyst; and
(E) an inhibitor;
wherein said composition has a viscosity that ranges from about 125 to about 1,000 centipoise.
5. A laminate having a substrate and a coating, said coating comprising a curable release coating composition comprising:
(A) additives for anchorage of release coatings consisting essentially of:
(R a SiO 4−a)/2 ) n
wherein:
n is an integer greater than 3; a is from 1 to 3; R is independently selected from the group consisting of a carboxylic acid anhydride containing radical having from one to forty carbon atoms, monovalent hydrocarbon radicals, monovalent hydrocarbonoxy radicals, and hydride atoms, with at least one carboxylic acid anhydride and hydride being present on the molecule;
(B) an alkenyl silicone having the formula:
M Vi a T b D c M d
wherein:
a and b have values ranging from 2 to 5; c is an integer ranging from about 50 to about 1,000; d has a value ranging from 0 to about 0.5; and a+d>b;
M Vi =R 1 3−p R 2 p SiO 1/2 , wherein: R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms; R 2 independently selected from the group consisting of olefinic monovalent hydrocarbon radicals having two to forty carbon atoms; p ranges from 1 to 3;
T=R 3 SiO 3/2 , wherein: R3 is independently selected from the group consisting of R 1 and R 2;
D=R 4 R 5 SiO 2/2 , wherein: R 4 and R 5 are each independently selected from the group consisting of R 1 and R 2 ;
M=R 1 3 SiO 1/2 , wherein: each R 1 is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms;
(C) a hydrogen siloxane selected from the group consisting of:
MD e D′ f M, MD′ f M, MD e D′ f M′, M′D e D′ f M, and M′D e M′
wherein:
M=R′ 3 SiO 1/2 ; M′=H g R′ 3−g SiO 1/2 ; D=R′R′SiO 2/2 ; and D′=R′HSiO 2/2 ; wherein each R′ in M, M′, D, and D′ is independently selected from the group consisting of monovalent hydrocarbon radicals having one to forty carbon atoms; the subscripts e and f may be zero or positive whereby the sum of e and f ranges from about 10 to about 100 subject to the limitation that the sum of f and g is two or greater;
(D) a hydrosilylation catalyst; and
(E) an inhibitor.
6. The laminate of claim 5 wherein the substrate is selected from the group consisting of polyester, polypropylene, polyethylene kraft, and polypropylene kraft.