1. A binderless stimulable phosphor screen having a support and a vapor deposited phosphor layer with phosphor needles and voids between said needles, characterized in that said voids between said needles are partially filled with a polymeric compound wherein, said voids are filled over a length of at least 5 μm.

2. A binderless stimulable phosphor screen according to claim 1 , wherein, said voids are filled over a length of at least 10 μm.

3. A binderless stimulable phosphor screen according to claim 2 , wherein said polymeric compound is selected from the group consisting of vinyl resins comprising moieties derived from esters of acrylic acid and vinyl resins comprising moieties derived from esters of methacrylic acid.

4. A binderless stimulable phosphor screen according to claim 2 , wherein said polymeric compound is a thermoplastic rubber.

5. A binderless stimulable phosphor screen according to claim 1 , wherein said polymeric compound is selected from the group consisting of vinyl resins comprising moieties derived from esters of acrylic acid and vinyl resins comprising moieties derived from esters of methacrylic acid.

6. A binderless stimulable phosphor screen according to claim 1 , wherein said polymeric compound is a thermoplastic rubber.

7. A method for producing a binderless phosphor screen comprising the steps of:

vapor depositing a photostimulable phosphor on a substrate forming a phosphor layer with phosphor needles and voids between them,

applying a solution of a polymer on said vapor deposited phosphor,

filling said voids over a length of at least 5 μm,

wiping the excess of said solution from said phosphor layer afterwhich said voids are partially filled, and

drying the phosphor screen.

8. Method according to claim 7 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.

9. Method according to claim 7 , wherein an additional step of applying at least one colorant in said voids is performed before said step of applying a solution of a polymer on said vapor deposited phosphor.

10. Method according to claims 7 , wherein, in said step of applying a solution of a polymer on said vapor deposited phosphor, a solution of a polymer further comprising at least one colorant is used.

11. Method according to claim 10 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.

12. A method for producing a binderless phosphor screen on a substrate containing a CsX:Eu stimulable phosphor, comprising the steps of:

bringing a heatable container with a CsX:Eu phosphor, X being selected from the group consisting of Cl, Br and combinations thereof together with the substrate in a deposition chamber that is evacuated to at least 10 −1 mbar,

depositing, by a method selected from the group consisting of physical vapor deposition, chemical vapor deposition or atomisation technique, said CsX:Eu phosphor forming a vapor deposited phosphor layer with needle shaped phosphor with voids between said needle shaped phosphor,

applying a solution of a polymer on said vapor deposited phosphor,

filling said voids over a length of at least 5 μm,

wiping the excess of said solution from said vapor deposited phosphor afterwhich said voids are partially filled and

drying the phosphor screen.

13. Method according to claim 12 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.

14. Method according to claim 12 , wherein an additional step of applying at least one colorant in said voids is performed before said step of applying a solution of a polymer on said vapor deposited phosphor.

15. Method according to claims 12 , wherein, in said step of applying a solution of a polymer on said vapor deposited phosphor, a solution of a polymer further comprising at least one colorant is used.

16. Method according to claim 15 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.

17. A method for producing a binderless phosphor screen on a substrate containing a CsX:Eu stimulable phosphor, wherein X represents a halide selected from the group consisting of Cl, Br and combinations thereof, said method comprising the steps of:

bringing multiple heatable containers of CsX and a europium compound selected from the group consisting of EuX′ 2 , EuX′ 3 and EuOX′, X′ being selected from the group consisting of F, Cl, Br, I and combinations thereof together with the substrate in a deposition chamber that is evacuated to at least 10 −1 mbar,

depositing, by a method selected from the group consisting of physical vapor deposition, chemical vapor deposition or atomisation technique, both said CsX and said europium compound on a substrate in such a ratio that on said substrate a CsX phosphor, doped with between 10 −3 and 5 mol % europium is formed comprising phosphor particles with voids between said phosphor particles,

applying a solution of a polymer on said vapor deposited phosphor,

filling said voids over a length of at least 5 μm,

wiping the excess of said solution from said vapor deposited phosphor afterwhich said voids are partially filled and

drying the phosphor screen.

18. Method according to claim 17 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.

19. Method according to claim 17 , wherein an additional step of applying at least one colorant in said voids is performed before said step of applying a solution of a polymer on said vapor deposited phosphor.

20. Method according to claims 17 , wherein, in said step of applying a solution of a polymer on said vapor deposited phosphor, a solution of a polymer further comprising at least one colorant is used.

21. Method according to claim 20 , wherein said solution of a polymer is selected from the group consisting of a solution of vinyl resins comprising moieties derived from esters of acrylic acid in ethylacetate, a solution of vinyl resins comprising moieties derived from esters of methacrylic acid in ethylacetate and a solution of a thermoplastic rubber in a mixture of ethylacetate and toluene.