Pulverulent, cross-linked polymers capable of absorbing aqueous liquids
View Patent ↗The invention relates to absorbent, cross-linked polymers based on partially neutralized, monoethylenically unsaturated monomers that bear acidic groups. Said polymers exhibit improved properties with regard to their ability to transport liquids in a swollen state. The surface of the polymers is postreticulated, using a combination of an organic cross-linking compound, excluding polyols, and a cation that is in salt form in an aqueous solution.
1. A pulverulent polymer which absorbs water, aqueous or serous liquids as well as blood, which is post-cross-linked on the surface and is synthesized from
a) from about 55 to about 99.9 wt. % polymerized, ethylenically unsaturated, acid group-containing monomers which are at least about 25 mol % neutralized,
b) from 0 to about 40 wt. % polymerized, ethylenically unsaturated monomers which are copolymerizable with a),
c) from about 0.1 to about 5.0 wt. % of one or more polymerized cross-linking agents,
d) from 0 to about 30 wt. % of a water-soluble polymer, wherein the sum of the quantities by weight a) to d) is 100 wt. %, wherein the polymer is formed into polymer particles that are coated and post-cross-linked, with heating, with
e) from about 0.01 to about 5 wt. %, in relation to the polymer, of an organic surface post-cross-linking agent, with the exception of polyols, in the form of an aqueous solution and with
f) from about 0.001 to about 1.0 wt. %, in relation to the polymer, of a trivalent or a higher-valent cation in the form of a salt dissolved in an aqueous solution,
g) the polymer particles coated with elements e) and f) are heat treated at a temperature from at least 150 to 250° C. to form the pulverulent polymer, and wherein the total quantity of water of the coating solution is from about 0.5 to about 10 wt %, in relation to the polymer, and the ratio by weight of the salt to the post-cross-linking agent is within the range from about 1:0.8 to about 1:4 wherein the pulverulent polymer has a retention (TB) of at least about 25 g/g and a saline flow permeability (SFC) of about 45×10 −7 cm 3 sec/g or more.
2. The pulverulent polymer according to claim 1 wherein the ratio by weight of water-soluble salt to the post-cross-linking agent is from about 1:1 to about 1:3.5.
3. The pulverulent polymer according to claim 1 wherein the component e) has been utilized at from about 0.1 to about 2.5 wt. %, and the component f) has been utilized at from about 0.005 to about 0.5 wt. %.
4. The pulverulent polymer according to claim 1 wherein only water has been utilized as a solvent for the components e) and f).
5. The pulverulent polymer according to claim 1 wherein the components e) and f) have been utilized together in an aqueous solution.
6. The pulverulent polymer according to claim 1 wherein the total quantity of water of the aqueous solutions which are added separately or together was from about 0.75 to about 5 wt. %.
7. The pulverulent polymer according to claim 1 wherein the component f) is a cation of iron, aluminum, titanium or of a further transition metal, or of a double salt of two different cations or of a mixture of the salts.
8. The pulverulent polymer according to claim 1 wherein the organic surface post crosslinking agent is an alkylene carbonate.
9. The pulverulent polymer according to claim 6 wherein the alkylene carbonate 1,3-dioxolan-2-one has been utilized, and as the salt an inorganic aluminum salt has been utilized.
10. The pulverulent polymer according to claim 1 wherein at least about 50% of the acid groups of the monomer units a) are carboxyl groups.
11. The pulverulent polymer according to claim 1 wherein the monomer units a) are derived from acrylic acid and/or methacrylic acid.
12. The pulverulent polymer according to claim 1 wherein the component d) is selected from the group consisting of starch, polyvinyl alcohol and derivatives thereof.
13. The pulverulent polymer according to claim 1 wherein the polymer has a retention (TB) of at least about 27 g/g at a permeability (SFC) of up to about 70·10 −7 cm 3 sec/g.
14. The pulverulent polymer according to claim 1 wherein the polymer has a permeability (SFC) of from at least about 70·10 −7 to about 150·10 −7 cm 3 sec/g.
15. The pulverulent polymer according to claim 13 wherein the polymer has a liquid absorption at pressure (AAP) at 0.7 psi of at least about 18 g/g.
16. A process for the preparation of absorbent polymers according to claim 1 wherein a mixture of:
a) from about 55 to about 99.9 wt. % ethylenically unsaturated, acid group-carrying monomers which are at least about 25 mol % neutralized,
b) from 0 to about 40 wt. % ethylenically unsaturated monomers which are copolymerizable with a),
c) from about 0.1 to about 5.0 wt. % of one or more cross-linking compounds,
d) from 0 to about 30 wt. % of a water-soluble polymer,
wherein the sum of the components a) to d) is 100 wt. %, is radically polymerized, optionally comminuted, dried, pulverized, sieved, and then the resulting pulverized polymer powder is treated with
e) from about 0.01 to about 5 wt. %, in relation to the polymer, of an organic surface post-cross-linking agent, with the exception of polyols, in the form of an aqueous solution and with
f) from about 0.005 to about 0.5 wt. %, in relation to the polymer, of a trivalent or a higher-valent cation of a salt dissolved in an aqueous solution,
g) the polymer particles coated with elements e) and f) are heat treated at a temperature from at least 150 to 250° C. to form the pulverulent polymer, and wherein the salt and the surface post-cross-linking agent are utilized in a ratio by weight of from about 1:0.8 to about 1:4 and the total quantity of water of the aqueous coating solution(s) is from about 0.5 to about 10 wt. %, in relation to the polymer, and wherein, with intensive mixing of the aqueous solutions of the components e) and f) which are present together or separately, with the polymer powder and with heating, a post-cross-linking of the polymer powder takes place.
17. The process according to claim 16 wherein the polymer powder utilized has a moisture content of from about 0.5 to about 25 wt. %.
18. The process according to claim 16 wherein the polymer powder utilized has a particle size of less than about 3000 μm.
19. The process according to claim 16 wherein the aqueous solutions of the components e) and f) are heated up to from about 20° C. to about 100° C. before they are utilized.
20. Absorption agents for water, aqueous liquids or blood, foamed and non-foamed flat materials, in packaging materials, in constructions for plant cultivation, as carriers for soil improvers or as carriers for active substances comprising pulverulent polymer made according to claim 1 .
21. A predominant to sole absorption agent in at least one layer of absorbent inserts comprising the pulverulent polymer made according to claim 1 .
22. A pulverulent polymer which absorbs water, aqueous or serous liquids as well as blood, which is post-cross-linked on the surface and the pulverulent polymer consists essentially of
a) from about 55 to about 99.9 wt. % polymerized, ethylenically unsaturated, acid group-containing monomers which are at least about 25 mol % neutralized,
b) from 0 to about 40 wt. % polymerized, ethylenically unsaturated monomers which are copolymerizable with a),
c) from about 0.1 to about 5.0 wt. % of one or more polymerized cross-linking agents,
d) from 0 to about 30 wt. % of a water-soluble polymer, wherein the sum of the quantities by weight a) to d) is 100 wt. %, wherein the polymer is formed into polymer particles that are coated and post-cross-linked, with heating, with
e) from about 0.01 to about 5 wt. %, in relation to the polymer, of an organic surface post-cross-linking agent, with the exception of polyols, in the form of an aqueous solution and with
f) from about 0.001 to about 1.0 wt. %, in relation to the polymer, of a trivalent or a higher-valent cation in the form of a salt dissolved in an aqueous solution,
g) the polymer particles coated with elements e) and f) are heat treated at a temperature from at least 150 to 250° C. to form the pulverulent polymer, and wherein the total quantity of water of the coating solution is from about 0.5 to about 10 wt. %, in relation to the polymer, and the ratio by weight of the salt to the post-cross-linking agent is within the range from about 1:0.8 to about 1:4 wherein the pulverulent polymer has a retention (TB) of at least about 25 g/g and a saline flow permeability (SFC) of about 45×10 −7 cm 3 sec/g or more.