View Patent ↗A method of increasing the useful life of heating elements that consist essentially of molybdenum silicide and alloys thereof, wherein the heating elements operate at high temperatures in heat treatment processes and generally rest against the floor and/or the ceiling of a furnace. The heating elements contain aluminum to an extent sufficient to maintain a stable, slowly growing layer of aluminum oxide on the surfaces of the heating elements, and the heating elements are placed in direct abutment with an aluminum oxide brick material.
1. A method of increasing the useful life of heating elements that consist essentially of molybdenum silicide, wherein said elements operate at temperatures higher than about 1200° C. in heat treatment processes, said method comprising the steps of:
providing a heating element formed from a material selected from the group consisting of molybdenum silicide, alloys of molybdenum silicide,
adding to the heating element material aluminum in a form and in an amount sufficient to maintain a stable, slowly growing layer of aluminum oxide on the surface of the heating element; and
positioning the heating element within a furnace to lie in direct abutment with an aluminum oxide brick material, wherein the heating element material contains Mo(Si 1-x Al x ) 2 , wherein x lies in the range of 0.2-0.6.
2. A method according to claim 1 , wherein x lies in the range of 0.40-0.50.
3. A method according to claim 1 , wherein the heating element material contains up to 40% by volume Al 2 O 3 .