Positive electrode films for alkali metal polymer batteries and method for making same
View Patent ↗A process for extruding a thin positive electrode sheet having at least 40%/wt of solid content for a lithium polymer battery through a single or twin screw extruder is disclosed as well as a positive electrode sheet produced therefrom. A mixture of active cathodic intercalation material, lithium salt and electronic conductive material is mixed with a polymer of the polyether family in a ratio of at least 40% of total weight into the mixing chamber of an extrusion machine and extruded through a classical sheet die into a thin cathode sheet or film onto a substrate in sheet form.
1. A process for extruding a positive electrode sheet having at least 40%/wt of solid content for a solid polymer battery through a single or twin screw extruder, said process comprising:
a) mixing an ionically conductive electrolyte including a polyethylene oxide based polymer and a lithium salt, an active cathode material, water in a proportion ranging from 0.005% to 5%/wt, and an electronic conductive material into a single or twin screw section of said extruder;
b) melting the materials mixed in step a) through the single or twin screw section of the extruder to form an homogenous slurry and thereafter eliminating the water contained in the slurry by evaporation and dissipation of the water vapor in a decompression zone defined by a greater thread pitch of the screw or screws through a vent aligned with the decompression zone of the extruder;
c) extruding a positive electrode material through a die opening in the form of a sheet having a thickness within a range of 40 to 200 microns and a porosity of less than 10%;
d) feeding said positive electrode material in sheet form directly between a pair of rollers maintained at a temperature ranging from about −5° C. to about −30° C., without a substrate; and
e) depositing said positive electrode material onto a substrate traveling near said rollers.
2. A process as defined in claim 1 , wherein said pair of rollers rotate at a speed higher than a feeding rate of discharge of said positive electrode material through said die opening such that said positive electrode material in the form of a sheet is stretched thereby reducing the thickness of the sheet.
3. A process as defined in claim 2 , wherein said pair of rollers further reduce the thickness of said positive electrode material in the form of a sheet to a thickness of between about 25 microns and about 100 microns by calendering, laminating or rolling the sheet.
4. A process as defined in claim 1 , wherein said pair of rollers reduce the thickness of said positive electrode material in the form of a sheet to a thickness of between about 25 microns and about 100 microns by calendering, laminating or rolling the sheet.
5. A process as defined in claim 1 , wherein said positive electrode material in the form of a sheet remains in contact with a particular one of said pair of rollers through a portion of the rotation of that particular roller, thereby increasing the heat transfer between the positive electrode material in the form of a sheet and the particular roller.
6. A process as defined in claim 1 , wherein the sheet of extruded positive electrode material has a thickness of between 35 and 70 microns after calendaring between said pair of rollers.
7. A process as defined in claim 1 , wherein water is mixed with the ionically conductive electrolyte, the active cathode material and the electronic conductive material in a proportion ranging from 0.1% to 0.8%/wt.