Process for homogenizing polyolefin drag reducing agents
View Patent ↗A process for producing polymer drag reducing agent (DRA) slurries without cryogenic temperatures or conventional grinding is described. The homogenizing or size reduction of polymer, such as poly(alpha-olefins), may be achieved by the use of granulated polymer and at least one liquid, non-solvent for the polymer DRA. In one non-limiting embodiment of the invention, the homogenizing is conducted at ambient temperature. Examples of suitable non-solvents include water and non-aqueous non-solvents including, but not necessarily limited to, alcohols, glycols, glycol ethers, ketones, and esters; having from 2-6 carbon atoms, and combinations thereof. The polymeric DRA may be homogenized to an average particle size of about 600 microns or less.
1. A method for producing a polymer drag reducing agent (DRA) slurry, comprising:
feeding to a homogenizer components comprising:
a granulated polymer DRA; and
at least one liquid, non-solvent for the polymer DRA; and
homogenizing the components to reduce the particle size of the polymer DRA to yield a polymer DRA slurry in the absence of cryogenic temperatures.
2. The method of claim 1 where in the feeding, the granulated polymer DRA has an average particle size between about 6 mm and about 20 mm.
3. The method of claim 1 where in the feeding, the granulated polymer DRA is poly(alpha-olefin).
4. The method of claim 1 where in homogenizing the components, the average particle size of the homogenized polymer DRA is equal to or less than about 600 microns.
5. The method of claim 1 where the feeding and homogenizing are conducted at ambient temperatures.
6. The method of claim 1 where the liquid, non-solvent is selected from the group of compounds consisting of alcohols, glycols, glycol ethers, ketones, and esters; where the non-solvent has from 2-6 carbon atoms, water and combinations thereof.
7. A method for producing a polymer drag reducing agent (DRA) slurry, comprising:
feeding to a homogenizer components comprising:
a granulated polymer DRA that is poly(alpha-olefin); and
at least one liquid, non-solvent for the polymer DRA, where the liquid, non-solvent is selected from the group of compounds consisting of alcohols, glycols, glycol ethers, ketones, and esters; where the non-solvent has from 2-6 carbon atoms, water and combinations thereof; and
homogenizing the components to reduce the particle size of the polymer DRA to yield a polymer DRA slurry in the absence of cryogenic temperatures.
8. The method of claim 7 where in the feeding, the granulated polymer DRA has an average particle size between about 6 mm and about 20 mm.
9. The method of claim 7 where in homogenizing the components, the average particle size of the homogenized polymer DRA is equal to or less than about 600 microns.
10. The method of claim 7 where the feeding and homogenizing are conducted at ambient temperatures.
11. A polymer drag reducing agent (DRA) slurry made by a method comprising:
feeding to a homogenizer components comprising:
a granulated polymer DRA that is poly(alpha-olefin); and
at least one liquid, non-solvent for the polymer DRA; and
homogenizing the components to reduce the particle size of the polymer DRA to yield a polymer DRA slurry.
12. The polymer DRA slurry of claim 11 where in the feeding, the granulated polymer DRA has an average particle size between about 6 mm and about 20 mm.
13. The polymer DRA slurry of claim 11 where the homogenizing is conducted in the absence of cryogenic temperatures.
14. The polymer DRA slurry of claim 11 where the average particle size of the homogenized polymer DRA is equal to or less than about 600 microns.
15. The polymer DRA slurry of claim 11 where the feeding and homogenizing are conducted at ambient temperatures.
16. The polymer DRA slurry of claim 11 where the liquid, non-solvent is selected from the group of compounds consisting of alcohols, glycols, glycol ethers, ketones, and esters; where the non-solvent has from 2-6 carbon atoms, water and combinations thereof.