Surface protection film for freshly painted automobile surfaces with a multicomponent adhesive

1. A self-adhesive protective film for the surface protection of painted vehicles or vehicle parts, comprising a single-ply or multi-ply backing layer and a self-adhesive layer, wherein the self-adhesive composition comprises

100 parts by weight of a component A comprising a vinyl acetate copolymer or a mixture of two or more vinyl acetate copolymers having a vinyl acetate content of from 60 to 75% by weight and a maximum of the loss factor tan δ, measured by means of DMTA and determined at an angular frequency ω=1 rad/s, of <0° C., from 5 to 80 parts by weight of a component B comprising a vinyl acetate copolymer or a mixture of two or more vinyl acetate copolymers of different molecular weight, having a vinyl acetate content of from 75 to 95% by weight and a maximum of the loss factor tan δ, measured by means of DMTA and determined at an angular frequency ω=1 rad/s, of ≧−5° C., and

from 5 to 80 parts by weight of a component C comprising a vinyl acetate copolymer or a mixture of two or more vinyl acetate copolymers of different molecular weight, having a vinyl acetate content of ≦70% by weight, which at the same time has a vinyl acetate content of at least 5% by weight below the vinyl acetate content of component A.

2. The self-adhesive protective film of claim 1 , wherein components A, B, and C are copolymers based on ethylene and/or propylene and/or further α-olefins and vinyl acetate.

3. The self-adhesive protective film of claim 1 , wherein components A and B are copolymers based on ethylene and vinyl acetate and component C is a copolymer based on ethylene and/or propylene and/or further α-olefins and vinyl acetate.

4. The self-adhesive protective film of claim 1 , wherein components A, B, and C comprise ethylene vinyl acetate copolymers.

5. The self-adhesive protective film claim 1 , wherein the thickness of the backing layer is between 20 and 80 μm, optionally including an adhesion promoter layer disposed between the backing layer and the adhesive layer.

6. The self-adhesive protective film of claim 1 , wherein the backing layer comprises at least one light stabilizer in an amount of at least 0.15% by weight.

7. The self-adhesive protective film of claim 1 , wherein the UV permeability of the protective film in the wavelength range from 290 to 360 nm is below 1%.

8. A process for producing the self-adhesive protective film of claim 1 which comprises simultaneously coextruding the adhesive layer, backing layer, and optionally further auxiliary layers.

9. A method of protecting freshly painted surfaces of automobiles or automobile parts during assembly or transit, which comprises applying a self-adhesive protective film according to claim 1 to said freshly painted surfaces.

10. A method of protecting sensitive paint, metal, plastic or glass surfaces, which comprises applying a self-adhesive protective film according to claim 1 to said surfaces.

11. The self-adhesive protective film of claim 1 , wherein said two or more vinyl acetate copolymers of component A have different molecular weights.

12. The self-adhesive protective film of claim 1 , wherein said backing layer is a polyolefinic backing layer.