Catalyst for polymerization and copolymerization of ethylene
A solid titanium complex catalyst for polymerization and copolymerization of ethylene is prepared by the process comprising: (1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol; (2) reacting the magnesium solution with an ester compound having at least one hydroxyl group and a boron compound having at least one alkoxy group to produce a magnesium composition; and (3) producing a solid titanium catalyst through recrystallization by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound; and optionally reacting the solid titanium catalyst with an additional titanium compound. The solid titanium complex catalyst for polymerization and copolymerization of ethylene according to present invention exhibits high catalytic activity and can be advantageously used in the polymerization and copolymerization of ethylene to produce polymers of high bulk density, narrow particle size distribution and small amount of fine particles.
1. A catalyst for polymerization and copolymerization of ethylene, prepared by a method comprising:
(1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol in the presence or absence of a hydrocarbon solvent;
(2) reacting the magnesium solution with an ester compound having at least one hydroxyl group and a boron compound having at least one alkoxy group to produce a magnesium composition solution; and
(3) producing a solid titanium catalyst by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound.
2. The catalyst of claim 1 , wherein the method further comprises reacting the solid titanium catalyst with an additional titanium compound.
3. The catalyst of claim 1 , wherein the ester compound having at least one hydroxyl group is an unsaturated aliphatic acid ester having at least one hydroxyl group, an aliphatic monoester or a polyester having at least one hydroxyl group, an aromatic ester having at least one hydroxyl group, or an alicyclic ester having at least one hydroxyl group.
4. The catalyst of claim 1 , wherein the boron compound having at least one alkoxy group is a compound represented by the general formula of BR 1 n (OR 2 ) 3-n and wherein R 1 is a hydrocarbon having 1˜20 carbon atoms, or halogen, R 2 is a hydrocarbon having 1˜20 carbon atoms, and n is 0, 1 or 2.
5. The catalyst of claim 1 , wherein the titanium compound is represented by the general formula of Ti(OR) a X 4-a , and wherein R is an alkyl group having 1˜10 carbon atoms, X is a halogen atom, and a is 0, 1, 2, 3 or 4.
6. The catalyst of claim 1 , wherein the haloalkane compound is a hydrocarbon compound which contains at least one halogen atom and has 1˜20 carbon atoms.
7. The catalyst of claim 1 , wherein the amount of the mixture of titanium compound and haloalkane compound is about 0.1˜200 mol per one mole of magnesium compound, and wherein the mixing molar ratio of the haloalkane compound to the titanium compound is about 0.05˜0.95.
8. A method of preparing a catalyst for polymerization and copolymerization of ethylene, comprising:
(1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol in the presence or absence of a hydrocarbon solvent;
(2) reacting the magnesium solution with an ester compound having at least one hydroxyl group and a boron compound having at least one alkoxy group to produce a magnesium composition solution; and
(3) producing a solid titanium catalyst by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound.
9. The method of claim 8 , wherein the method further comprises reacting the solid titanium catalyst with an additional titanium compound.
10. The method of claim 8 , wherein the ester compound having at least one hydroxyl group is an unsaturated aliphatic acid ester having at least one hydroxyl group, an aliphatic monoester or a polyester having at least one hydroxyl group, an aromatic ester having at least one hydroxyl group, or an alicyclic ester having at least one hydroxyl group.
11. The method of claim 8 , wherein the boron compound having at least one alkoxy group is a compound represented by the general formula of BR 1 n (OR 2 ) 3-n and wherein R 1 is a hydrocarbon having 1˜20 carbon atoms, or halogen, R 2 is a hydrocarbon having 1˜20 carbon atoms, and n is 0, 1 or 2.
12. The method of claim 8 , wherein the titanium compound is represented by the general formula of Ti(OR) a X 4-a , and wherein R is an alkyl group having 1˜10 carbon atoms, X is a halogen atom, and a is 0, 1, 2, 3 or 4.
13. The method of claim 8 , wherein the haloalkane compound is a hydrocarbon compound which contains at least one halogen atom and has 1˜20 carbon atoms.
14. The method of claim 8 , wherein the amount of the mixture of titanium compound and haloalkene compound is about 0.1˜200 mol per one mole of magnesium compound, and wherein the mixing molar ratio of the haloalkane compound to the titanium compound is about 0.05˜0.95.