Method of producing nanophase WC-based powder by vapor phase reaction at atmospheric pressure
View Patent ↗The present invention relates to a method of producing nanophase powder, which can be used as materials for high-strength and wear-resistance cemented carbide. It purports to provide a method of producing WC powder of a 10˜20 nm grade by using vapor phase reaction with a precursor containing tungsten. For achieving said objectives, the method of producing WC-based powder according to the present invention comprises preparing a precursor containing tungsten; producing gas by vaporizing said precursor in a reactor; and carburizing said gas in a non-oxidizing atmosphere. The nanophase WC powder produced as such has high-strength and excellent wear-resistance, which can be suitably used as materials for carbide tools, carbide cement, wear-resistance components, or metal molds.
1. A method of producing nanophase WC-based powder by a vapor phase reaction at atmospheric pressure, which comprises the steps of:
preparing a precursor containing tungsten;
producing gas by vaporizing or sublimating said precursor; and
carburizing said gas in a non-oxidizing atmosphere.
2. The method of producing nanophase WC-based powder by a vapor phase reaction at atmospheric pressure according to claim 1 , wherein said precursor is at least one material selected from the group consisting of tungsten ethoxide, tungsten chloride and tungsten hexacarbonyl.
3. The method of producing nanophase WC-based powder by a vapor phase reaction at atmospheric pressure according to claim 1 , wherein said non-oxidizing atmosphere comprises at least one camer gas selected from the group consisting of He, Ar, N 2 and H 2 .
4. The method of producing nanophase WC-based powder by a vapor phase reaction at atmospheric pressure according to claim 1 , wherein said step of carburizing said gas comprises heat treatment at a temperature of 900˜1,500° C.
5. A method of producing nanophase WC-based powder by a vapor phase reaction at atmospheric pressure, which comprises the steps of:
preparing a precursor containing tungsten, said precursor being a source of carbon;
producing gas by vaporizing or sublimating said precursor; and
carburizing said gas in a non-oxidizing atmosphere.