Process of forming multilayered structures
View Patent ↗The present invention provides for a method of producing an integral multilayered porous membrane by simultaneously co-casting a plurality of polymer solutions onto a support to form a multilayered liquid sheet and immersing the sheet into a liquid coagulation bath to effect phase separation and form a porous membrane. The support can be a temporary support or form an integrated support for the membrane. The plurality of layers may be of the same polymer or different, same concentration or viscosity or different and may be subjected to the same processing conditions or different ones to form unique structures.
1. A process for forming a continuous, unsupported, multizone microporous membrane having at least two zones, comprising of the acts of:
operatively positioning at least one polymer applying apparatus having at least two polymer dispensing outlets relative to a continuously moving coating surface;
co-casting polymer from each of the polymer dispensing outlets onto the continuously moving coating surface so as to create a multiple layer polymer coating on the coating surface; and
subjecting the multiple polymer layer coating to a phase separation procedure so as to form a wet multizone microporous membrane, wherein the membrane avoids skinning effects at an interface between the at least two zones.
2. The process of claim 1 wherein the polymer comprises:
nylon.
3. The process of claim 1 wherein the polymer comprises:
polyvinylidene fluoride.
4. The process of claim 1 wherein the polymer comprises:
polyethersulfone.
5. The process of claim 1 further comprising the acts of:
washing and drying the membrane.
6. The process of claim 1 wherein the zones of the multizone microporous membrane have different pore sizes.
7. The process of claim 1 wherein an interfacial zone is located between the polymer layers of the multizone microporous membrane, thereby providing a subtle change in pore size between adjacent layers.
8. A process for forming a continuous, unsupported, multizone microporous membrane having at least two zones, comprising of the acts of:
operatively positioning at least one polymer applying apparatus having at least two polymer dispensing outlets relative to a continuously moving coating surface;
co-casting polymer from each of the polymer dispensing outlets onto the continuously moving coating surface so as to create a multiple layer polymer coating on the coating surface;
subjecting the multiple polymer layer coating to a phase separation procedure so as to form a wet multizone microporous membrane, wherein the membrane avoids skinning effects at an interface between the at least two zones; and
separating the wet multizone microporous membrane from the continuously moving coating surface at some point prior to complete drying of the membrane.
9. The process of claim 8 wherein the polymer comprises:
nylon.
10. The process of claim 8 wherein the polymer comprises:
polyvinylidene fluoride.
11. The process of claim 10 wherein the separating act is accomplished prior to completion of drying the wet multizone microporous membrane.
12. The process of claim 11 wherein the separating act is accomplished after said phase separation procedure.
13. The process of claim 8 wherein the polymer comprises:
polyethersulfone.
14. The process of claim 8 further comprising the acts of:
washing and drying the membrane.
15. The process of claim 8 wherein the separating act is accomplished before drying the wet multizone microporous membrane.
16. The process of claim 8 wherein an interfacial zone is located between the polymer layers of the multizone microporous membrane, thereby providing a subtle change in pore size between adjacent layers.
17. A process for forming an unsupported, multizone microporous membrane having at least two zones, comprising of the acts of:
operatively positioning at least one polymer applying apparatus having at least two polymer dispensing outlets relative to a coating surface;
co-casting polymer from each of the polymer dispensing outlets onto the coating surface so as to create a multiple layer polymer coating on the coating surface;
subjecting the multiple polymer layer coating to a phase separation procedure so as to form a wet multizone microporous membrane, wherein the membrane avoids skinning effects at an interface between the at least two zones; and
separating the wet multizone microporous membrane from the coating surface at some point prior to complete drying of the membrane.
18. The process of claim 17 wherein an interfacial zone is located between the polymer layers of the multizone microporous membrane, thereby providing a subtle change in pore size between adjacent layers.