Exhaust gas purifying catalyst compound, catalyst comprising said compound and method for preparing the compound
View Patent ↗The invention is to provide (i) a catalyst which does not require an activation of catalyst components by means of a calcination which has become a hindrance in the way of obtaining a catalyst having a high activity through a conventional technology and in which catalyst the compositing of vanadium with molybdenum is contemplated more than enough; ii) a method for producing the catalyst; (iii) a catalyst having an activity, especially having an activity at low temperatures and a durability both greatly increased; (iv) a catalyst compound for purifying an exhaust gas, in which compound the ratio of vanadium atom to molybdenum atom (V/Mo) is 3/2 or close thereto and which compound is expressed by the rational formula (NH 4 ) x Mo 2 V x O (3x+6) wherein x is 2.8 to 3.2; and (v) a method for producing the catalyst compound through a step for reacting molybdenum oxide (MoO 3 ) with ammonium metavanadate (NH 4 VO 3 ) in the co-presence of water for a prescribed period of time.
1. A catalyst compound for purifying an exhaust gas, in which compound the ratio of vanadium atom to molybdenum atom (V/Mo) is 1.4 to 1.6 and which compound is expressed by the rational formula
(NH 4 ) x MoV x O (3x+6)
wherein x is 2.8 to 3.2.
2. A process for producing the catalyst compound defined in claim 1 , which process comprises a step for reacting molybdenum oxide (MoO 3 ) with ammonium metavanadate (NH 4 VO 3 ) in the presence of water for a prescribed period of time.
3. A catalyst for purifying an exhaust gas, comprising a water soluble compound supported on a carrier, the water soluble compound being expressed by the rational formula
(NH 4 ) x Mo 2 V x O (3x+6)
wherein x is 2.8 to 3.2 and the ratio of vanadium atom to molybdenum atom is 1.4 to 1.6.
4. The catalyst for purifying an exhaust gas according to claim 3 wherein the catalyst is produced by further subjecting the catalyst to a calcination at a temperature lower that 500° C.
5. A composition used for a catalyst for purifying an exhaust gas, which composition comprises a water soluble compound and a sol-like substance, the water soluble compound being expressed by the rational formula
(NH 4 ) x Mo 2 V x O (3x+6)
wherein x is 2.8 to 3.2 and the ratio of vanadium atom to molybdenum atom is 1.4 to 1.6.
6. A catalyst for purifying an exhaust gas, in which catalyst the composition defined in claim 5 is supported on a carrier.
7. A composition according to claim 5 , wherein the sol-like substance is a silica-sol.
8. A process for producing a catalyst for purifying an exhaust gas, which process comprises a step for having a mixture of a water soluble compound with a sol-like substance supported on a titanium oxide carrier, or a step for blending the mixture with powders of a titanium oxide, after the water soluble compound was mixed with the sol-like substance in advance, the water soluble compound being expressed by the rational formula
(NH 4 ) x Mo 2 V x O (3x+ 6)
wherein x is 2.8 to 3.2 and the ratio of vanadium atom to molybdenum atom is 1.4 to 1.6.
9. A process according to claim 8 , wherein the sol-like substance is a silica-sol.
10. A catalyst for purifying an exhaust gas, which catalyst is produced through a step for impregnating a titanium oxide carrier with a water soluble compound, or a step for kneading powders of a titanium oxide together with the water soluble compound, the water soluble compound being expressed by the rational formula
(NH 4 ) x MO 2 V x O (3x+6)
wherein x is 2.8 to 3.2 and the ratio of vanadium atom to molybdenum atom is 1.4 to 1.6.
11. The catalyst for purifying an exhaust gas according to claim 10 wherein the catalyst is produced by further subjecting the catalyst to a calcination at a temperature lower than 500° C.