Coating method for disc brake pads
View Patent ↗A method of coating disc brake pads to obscure and seal minor surface imperfections, thereby reducing scrap rates. A preform of friction lining material is coated prior to molding and curing the preform and bonding the same to the backing plate to form the brake pad assembly. The preform is coated with an aqueous composition containing a solids mixture of 5–50 vol. % resin and 50–95 vol. % non-resin solids. Advantageously, the coating composition has a 5–30 vol. % solids mixture content, which solids mixture includes 15–25 vol. % resin, 0–10 vol. % powdered elastomer, 5–15 vol. % carbon black, 20–50 vol. % inorganic fillers, 5–15 vol. % organic fibers and 1–10 vol. % inorganic flake material.
1. A method of coating disc brake pads comprising a backing plate and a friction lining, the method comprising the steps of:
coating a preform of friction lining material with a coating composition comprising water and a solids mixture of 5–50 vol. % resin and 50–95 vol. % non-resin solids;
drying the coated preform; and
molding and curing the coated preform, and bonding the coated preform to a backing plate, to form a brake pad having a friction lining of final desired thickness.
2. The method of claim 1 further comprising, prior to coating the preform:
forming a wet mixture of the friction lining material and a slurry solution, and
pressing the wet mixture to extract at least a portion of the shiny solution to form a wet preform of thickness greater than the final desired thickness of the friction lining,
wherein the step of drying is sufficient to dry the wet preform and the coating composition.
3. The method of claim 1 wherein the non-resin solids of the solids mixture comprise:
0–15 vol. % powdered elastomer;
2–15 vol. % carbon black;
0–50 vol. % inorganic fillers;
2–15 vol. % organic fibers; and
0–15 vol. % inorganic flake material.
4. The method of claim 3 wherein the non-resin solids of the solids mixture comprise:
0–10 vol. % powdered elastomer;
5–15 vol. % carbon black;
20–50 vol. % inorganic fillers;
5–15 vol. % organic fibers; and
1–10 vol. % inorganic flake material.
5. The method of claim 1 wherein the solids mixture comprises 15–25 vol. % resin.
6. The method of claim 1 wherein the resin includes a liquid phenolic resin.
7. The method of claim 6 wherein the resin includes rubber.
8. The method of claim 6 wherein the resin is essentially free of anti-foaming agents.
9. The method of claim 1 wherein the backing plate is coated with a carbon black-containing adhesive prior to bonding the coated preform.
10. The method of claim 1 wherein the coating composition comprises 70–95 vol. % water and 5–30 vol. % of the solids mixture.
11. A method of coating disc brake pads comprising a backing plate and a friction lining, the method comprising the steps of:
forming a wet mixture of a friction lining material and a slurry solution;
pressing the wet mixture to extract at least a portion of the slurry solution to form a wet preform of thickness greater than a final desired thickness of the friction lining;
coating the wet preform with a coating composition comprising 70–95 vol. % water and 5–30 vol. % of a solids mixture of 5–50 vol. % resin and 50–95 vol. % non-resin solids;
drying the coated preform; and
molding and curing the coated preform, and bonding the coated preform to a backing plate, to form a brake pad having the friction lining of final desired thickness.
12. The method of claim 11 wherein the non-resin solids of the solids mixture comprise:
0–15 vol. % powdered elastomer;
2–15 vol. % carbon black;
0–50 vol. % inorganic fillers;
2–15 vol. % organic fibers; and
0–15 vol. % inorganic flake material.
13. The method of claim 12 wherein the non-resin solids of the solids mixture comprise:
0–10 vol. % powdered elastomer;
5–15 vol. % carbon black;
20–50 vol. % inorganic fillers;
5–15 vol. % organic fibers; and
1–10 vol. % inorganic flake material.
14. The method of claim 11 wherein the solids mixture comprises 15–25 vol. % resin.
15. The method of claim 11 wherein the resin includes a liquid phenolic resin.
16. The method of claim 15 wherein the resin includes rubber.
17. The method of claim 15 wherein the resin is essentially free of anti-foaming agents.
18. The method of claim 11 wherein the backing plate is coated with a carbon black-containing adhesive prior to bonding the coated preform.
19. A method of coating disc brake pads comprising a backing plate and a friction lining, the method comprising the steps of:
forming a wet mixture of a friction lining material and a slurry solution;
pressing the wet mixture to extract at least a portion of the slurry solution to form a wet preform of thickness greater than a final desired thickness of the friction lining;
coating the wet preform with a coating composition comprising 70–95 vol. % water and 5–30 vol. % of a solids mixture comprising: 15–25 vol. % liquid phenolic-based resin; 0–10 vol. % powdered elastomer; 5–15 vol. % carbon black; 20–50 vol. % inorganic fillers; 5–15 vol. % organic fibers; and 1–10 vol. % inorganic flake material;
drying the coated preform; and
molding and curing the coated preform, and bonding the coated preform to a backing plate having a carbon black-containing coating thereon, to form a brake pad having the friction lining of final desired thickness.
20. The method of claim 19 wherein the resin is essentially free of anti-foaming agents.