Flux coated brazing sheet
View Patent ↗A brazing flux mixture comprised of brazing flux, a polyvinyl butyral resin binder, and an organic solvent which can be applied over an entire aluminum alloy brazing sheet, or can be applied on the brazing sheet only where metallurgical bonds or joints are required, that is sufficiently durable to withstand processing operations and also provides good metallurgical bonds upon brazing.
1. A method of making a flux-coated aluminum brazing sheet comprising:
(a) combining a brazing flux with polyvinyl butyral binder to form a first mixture, wherein the brazing flux has an initial brazing flux particle size, wherein the brazing flux comprises a metal element;
(b) shearing said first mixture to form a second mixture having dispersed brazing flux particles in said second mixture, wherein about 100% of the dispersed brazing flux particles have a final brazing flux particle size on the order of about 1 micron or less, and said shearing step further reduces the initial brazing flux particle size by at least about 50% to the final brazing flux particle size;
(c) combining said second mixture with an organic solvent to form a brazing flux mixture;
(d) coating at least a portion of the surface of an aluminum brazing sheet with said brazing flux mixture; and
(e) drying said brazing flux mixture on said aluminum brazing sheet surface.
2. The method of claim 1 wherein said solvent is selected from the group consisting of alcohols, glycol ethers, ketones, esters and mixtures thereof.
3. The method of claim 1 wherein said organic solvent is selected from the group consisting of ethyl acetate, n-butyl acetate, n-propyl acetate, acetone, cyclohexanone, ethyl alcohol, isopropyl alcohol, n-butanol, n-propyl alcohol, diacetone alcohol, dipropylene glycol monomethyl ether, propylene glycol methyl ether acetate and mixtures thereof.
4. The method of claim 1 wherein said organic solvent is a toluene mixture with at least one alcohol selected from the group consisting of ethyl alcohol, isopropyl alcohol, nbutanol, n-propyl alcohol, and diacetone alcohol.
5. The method of claim 1 wherein said solvent is a mixture of either propylene glycol methyl ether acetate, isopropyl alcohol and ethyl acetate; or dipropylene monomethyl glycol ether, isopropyl alcohol and ethyl acetate.
6. The method of claim 1 wherein said brazing flux is a potassium fluoroaluminate, a cesium potassium fluoroaluminate, a zinc potassium fluoroaluminate, or a silicon and potassium fluoroaluminate mixture.
7. The method of claim 1 wherein said aluminum brazing sheet comprises a 3XXX, 5XXX, or 6XXX aluminum core alloy clad on at least one side with a 4XXX series brazing alloy.
8. The method of claim 1 wherein said aluminum brazing sheet comprises a 3XXX aluminum core alloy comprising about 1 wt. % manganese, about 0.3 wt. % copper, and about 0.15 wt. % titanium, and the balance aluminum, said core alloy clad with a 4XXX aluminum braze alloy comprising about 10 wt. % silicon, and the balance aluminum, and wherein said 4XXX alloy is clad to at least one side of said 3XXX series alloy, and said 4XXX series alloy comprises at least 5% of said total brazing sheet thickness, and said 3XXX series alloy comprises not more than 95% of said total brazing sheet thickness.
9. A method of making a brazing flux mixture comprising:
(a) combining a brazing flux with a polyvinyl butyral binder to form a first mixture, wherein the brazing flux has an initial brazing flux particle size, wherein the brazing flux comprises a metal element;
(b) shearing said first mixture with a 2-roll mill comprising two cylindrical rolls rotating at different speeds and in opposite directions in relation to one other to form a second mixture having dispersed brazing flux in said binder, wherein about 100% of the dispersed brazing flux particles have a final brazing flux particle size on the order of about 1 micron or less, and said shearing step further reduces the initial brazing flux particle size by at least about 50% to the final brazing flux particle size; and
(c) combining said second mixture with an organic solvent to form a brazing flux mixture.
10. The method of claim 9 wherein said brazing flux is potassium fluoroaluminate, a cesium potassium fluoroaluminate, a zinc potassium fluoroaluminate, or a silicon and potassium fluoroaluminate mixture.
11. The method of claim 9 wherein said solvent is selected from the group consisting of alcohols, glycol ethers, ketones, esters and mixtures thereof.
12. The method of claim 9 wherein said organic solvent is selected from the group consisting of ethyl acetate, n-butyl acetate, n-propyl acetate, acetone, cyclohexanone, ethyl alcohol, isopropyl alcohol, n-butanol, n-propyl alcohol, diacetone alcohol, dipropylene glycol monomethyl ether, propylene glycol methyl ether acetate and mixtures thereof.
13. The method of claim 9 wherein said organic solvent is selected from the group consisting of toluene mixed with at least one alcohol selected from the group consisting of ethyl alcohol, isopropyl alcohol, n-butanol, n-propyl alcohol, and diacetone alcohol.
14. The method of claim 9 wherein said solvent is a mixture of either propylene glycol methyl ether acetate, isopropyl alcohol and ethyl acetate; or dipropylene monomethyl glycol ether, isopropyl alcohol and ethyl acetate.
15. A method of making a shaped metal alloy product comprising:
(a) combining a brazing flux with polyvinyl butyral binder to form a first mixture, wherein the brazing flux comprises a metal element;
(b) shearing said first mixture to form a second mixture having dispersed brazing flux particles in said second mixture, wherein about 100% of the dispersed brazing flux particles have a final brazing flux particle size on the order of about 1 micron or less, and said shearing step further reduces the initial brazing flux particle size to the final brazing flux particle size by at least 50%;
(c) combining said second mixture with an organic solvent to form a brazing flux mixture;
(d) coating at least a portion of the surface of at least two aluminum alloy brazing sheets with said brazing flux mixture;
(e) drying said brazing flux mixture on said aluminum alloy brazing sheet surfaces;
(f) forming said flux coated aluminum alloy brazing sheets into flux coated parts having predetermined shapes; and
(g) brazing said parts together to form a shaped metal alloy product.
16. The method of claim 1 comprising the shearing of the first mixture with a 2-roll mill comprising two cylindrical rolls rotating at different speeds and in opposite directions in relation to one other.
17. The method of claim 15 comprising the shearing of the first mixture with a 2-roll mill comprising two cylindrical rolls rotating at different speeds and in opposite directions in relation to one other.