Method of manufacturing steel sheet having excellent workability and shape accuracy
View Patent ↗A method of manufacturing a high strength steel sheet containing, in mass %, C: 0.02 to 0.04%, Si: at most 0.4%, Mn: 0.5-3.0%, P: at most 0.15%, S: at most 0.03%, Al: at most 0.50%, N: at most 0.01%, and Mo: 0.01-1.0%. The method includes performing hot rough rolling either directly or after heating to a temperature of at most 1300° C., commencing hot finish rolling either directly or after reheating or holding, completing finish rolling at a temperature of at least 780° C., performing coiling after cooling to a temperature of 750° C. or below at an average cooling rate of at least 3° C./second, heating to an annealing temperature of at least 700° C. and then cooling to a temperature of 600° C. or below at an average cooling rate of at least 3° C./second, then holding in a temperature range of 450-600° C. for at least 10 seconds, and performing hot dip galvanizing after cooling.
1. A method of manufacturing a high strength steel sheet comprising casting a slab of steel comprising, in mass %, C: 0.02 to 0.04%, Si: at most 0.4%, Mn: 0.5-3.0%, P: at most 0.15%, S: at most 0.03%, Al: at most 0.50%, N: at most 0.01%, and Mo: 0.01-1.0%, performing hot rough rolling either directly or after heating to a temperature of at most 1300° C., commencing hot finish rolling either directly or after reheating or holding, completing finish rolling at a temperature of at least 780° C., performing coiling after cooling to a temperature of 750° C. or below at an average cooling rate of at least 3° C./second, heating to an annealing temperature of at least 700° C. and then cooling to a temperature of 600° C. or below at an average cooling rate of at least 3° C./second, then holding in a temperature range of 450-600° C. for at least 10 seconds, and performing hot dip galvanizing after cooling.
2. A method as claimed in claim 1 in which after coiling but before annealing, cold rolling is performed either directly or after scale removal.
3. A method as claimed in claim 1 in which alloying is carried out after galvanizing.
4. A method of manufacturing a high strength steel sheet comprising casting a slab of steel comprising, in mass %, C: 0.02 to 0.04%, Si: at most 0.4%, Mn: 0.5-3.0%, P: at most 0.15%, S: at most 0.03%, Al: at most 0.50%, N: at most 0.01%, Mo: 0.01-1.0%, and at least one of Cr: less than 1.5%, Ti: at most 0.15%, Nb: at most 0.15%, and B: at most 0.01%, performing hot rough rolling either directly or after heating to a temperature of at most 1300° C., commencing hot finish rolling either directly or after reheating or holding, completing finish rolling at a temperature of at least 780° C., performing coiling after cooling to a temperature of 750° C. or below at an average cooling rate of at least 3° C./second, heating to an annealing temperature of at least 700° C. and then cooling to a temperature of 600° C. or below at an average cooling rate of at least 3° C./second, then holding in a temperature range of 450-600° C. for at least 10 seconds, and performing hot dip galvanizing after cooling.
5. A method as claimed in claim 4 in which after coiling but before annealing, cold rolling is performed either directly or after scale removal.
6. A method as claimed in claim 4 in which alloying is carried out after galvanizing.
7. A method of manufacturing a high strength steel sheet comprising casting a slab of steel comprising, in mass %, C: 0.02 to 0.04%, Si: at most 0.4%, Mn: 0.5-3.0%, P: at most 0.15%, S: at most 0.03%, Al: at most 0.50%, N: at most 0.01%, and Mo: 0.01-1.0%, performing hot rough rolling either directly or after heating to a temperature of at most 1300° C., commencing hot finish rolling either directly or after reheating or holding, completing finish rolling at a temperature of at least 780° C., performing coiling after cooling to a temperature of 750° C. or below at an average cooling rate of at least 3° C./second, heating to an annealing temperature of at least 700° C. and then cooling to a temperature of 600° C. or below at an average cooling rate of at least 3° C./second, then holding in a temperature range of 250-600° C. for at least 10 seconds, and then cooling.
8. A method as claimed in claim 7 in which after coiling but before annealing, cold rolling is performed either directly or after scale removal.
9. A method of manufacturing a high strength steel sheet comprising casting a slab of steel comprising, in mass %, C: 0.02 to 0.04%, Si: at most 0.4%, Mn: 0.5-3.0%, P: at most 0.15%, S: at most 0.03%, Al: at most 0.50%, N: at most 0.01%, Mo: 0.01-1.0%, and at least one of Cr: less than 1.5%, Ti: at most 0.15%, Nb: at most 0.15%, and B: at most 0.01%, performing hot rough rolling either directly or after heating to a temperature of at most 1300° C., commencing hot finish rolling either directly or after reheating or holding, completing finish rolling at a temperature of at least 780° C., performing coiling after cooling to a temperature of 750° C. or below at an average cooling rate of at least 3° C./second, heating to an annealing temperature of at least 700° C. and then cooling to a temperature of 600° C. or below at an average cooling rate of at least 3° C./second, then holding in a temperature range of 250-600° C for at least 10 seconds, and then cooling.
10. A method as claimed in claim 9 which after coiling but before annealing, cold rolling is performed either directly or after scale removal.
11. A method of manufacturing a high strength zinc-coated steel sheet comprising electroplating the surface of a steel sheet obtained by the method claimed in claim 7 with a metal or an alloy having zinc as a primary component.