Coated articles having a protective coating and cathode targets for making the coated articles
View Patent ↗An article includes a substrate, a functional coating deposited over the substrate, and a protective coating deposited over the functional coating. The functional coating and the protective coating define a coating stack. The protective coating provides the coating stack with an emissivity value higher than the emissivity value of the functional coating alone. The protective coating can have a thickness in the range of greater than 100 Å to less than or equal to 10 microns and a refractive index in the range of 1.4 to 2. The protective coating can include a first layer formed over the functional coating and a second layer formed over the first layer. The first layer can include 50 wt. % to 100 wt. % alumina and 50 wt. % to 0 wt. % silica, and the second layer can include 50 wt. % to 100 wt. % silica and 50 wt. % to 0 wt. % alumina. An alternating current power supply and cathode target system includes a cathode target including aluminum in the range of 5 wt. % to 100 wt. % and silicon in the range of 0 wt. % to 95 wt. %.
1. An article, comprising:
a substrate;
a functional coating deposited over at least a portion of the substrate; and
a protective coating deposited over at least a portion of the functional coating,
wherein the functional coating and the protective coating define a coating stack,
wherein the protective coating provides the coating stack with an emissivity higher than the emissivity of the functional coating alone,
wherein the protective coating has a thickness in the range of greater than 100 Å to less than or equal to 10 microns and the protective coating has a refractive index in the range of 1.4 to 2, and
wherein the protective coating comprises a first layer formed over at least a portion of the functional coating and a second layer formed over at least a portion of the first layer, wherein the first layer comprises 50 wt. % to 99 wt. % alumina and 50 wt. % to 1 wt. % silica, and the second layer comprises 50 wt. % to 99 wt. % silica and 50 wt. % to 1 wt. % alumina.
2. The article of claim 1 , wherein the article is a motor vehicle transparency.
3. The article of claim , wherein the first layer comprises 70 wt. % to 99 wt. % alumina and 30 wt. % to 1 wt. % silica.
4. The article of claim 1 , wherein the first layer has a thickness in the range of 50 Å to 1 micron.
5. The article of claim 1 , wherein the first layer has a thickness in the range of 100 Å to 250 Å.
6. The article of claim 1 , wherein the second layer comprises 70 wt. % to 99 wt. % silica and 30 wt. % to 1 wt. % alumina.
7. The article of claim 1 , wherein the second layer has a thickness in the range of 50 Å to 2,000 Å.
8. The article of claim 1 , wherein the second layer has a thickness in the range of 300 Å to 500 Å.
9. A monolithic transparency, comprising:
a glass substrate;
a functional coating deposited over at least a portion of the glass substrate; and
a protective coating deposited over at least a portion of the functional coating to form a coating stack, the protective coating comprising aluminum oxide having a thickness in the range of 1 micron to 10 microns, and
wherein the protective coating comprises a first layer formed over at least a portion of the functional coating and a second layer formed over at least a portion of the first layer, wherein the first layer comprises 50 wt. % to 99 wt. % alumina and 50 wt % to 1 wt. % silica, and the second layer comprises 50 wt % to 99 wt. % silica and 50 wt. % to 1 wt. % alumina.
10. An article, comprising:
a substrate;
at least one solar infrared reflective dielectric functional coating deposited over at least a portion of the substrate; and
a protective coating deposited over at least a portion of the functional coating,
wherein the protective coating has a thickness in the range of greater than 100 Å to less than 10 microns and has a refractive index in the range of 1.4 to 1.8, and
wherein the protective coating comprises a first layer formed over at least a portion of the functional coating and a second layer formed over at least a portion of the first layer, wherein the first layer comprises 50 wt. % to 99 wt. % alumina and 50 wt. % to 1 wt. % silica, and the second layer comprises 50 wt. % to 99 wt. % silica and 50 wt. % to 1 wt. % alumina.