Method of processing a polycondensate in a multi-screw extruder
View Patent ↗A method for processing a polycondensate to give a granulate formed as pellets is disclosed, whereby the polycondensate is fused in the course of the method and then later resolidified. In an exemplary method, a total time during which the temperature of the polycondensate is above the melting point thereof is less than about 60 seconds. This method can be carried out by a multi-shaft extruder, whereby the degrassing and/or drying of the polycondensate in the solid state occurs at a pressure below atmospheric pressure and/or with addition of an inert gas. The time period, during which the polycondensate remains in the extruder, after being melted therein, amounts to, for example, less than about 15 seconds.
1. A method of processing a polycondensate to yield granules formed as pellets, comprising:
melting the polycondensate in the process using a twin-screw extruder or a multi-screw extruder, wherein the total time during which the polycondensate is formed as a melt during the process has a first time section during which the polycondensate still dwells in the extruder after melting, and a second time section during which the polycondensate, still molten, is processed outside the extruder, the duration of the first time section amounting to less than approximately 10 seconds; and
solidifying the melted polycondensate wherein a total time during which a temperature of the polycondensate is above a melting point of the polycondensate in the process amounts to less than approximately 60 seconds.
2. The method according to claim 1 , wherein the total time during which the temperature of the polycondensate is above the melting point of the polycondensate during the process amounts to less than approximately 30 seconds.
3. The method according to claim 2 , wherein the residual water content in the melted polycondensate is greater than 200 ppm.
4. The method according to claim 1 , wherein the polycondensate is a polyester.
5. A method of processing a polycondensate to yield granules formed as pellets, comprising:
melting the polycondensate in the process; and
solidifying the melted polycondensate wherein a total time during which a temperature of the polycondensate is above a melting point of the polycondensate in the process amounts to less than approximately 60 seconds, wherein the polycondensate in its starting form is present as a bulk material with a bulk density in a range of 200 kg/m 3 to 600 kg/m 3 .
6. The method according to claim 1 , wherein the polycondensate is formed as flakes or chips.
7. The method according to claim 1 , wherein a starting material of the polycondensate is partially predried before the melting.
8. The method according to claim 1 , comprising:
degassing the polycondensate for removing volatile impurities or decomposition products from the polycondensate.
9. The method according to claim 1 , comprising:
introducing the polycondensate in a solid state into the extruder;
heating the polycondensate to a temperature below the melting point; and
degassing or drying the polycondensate, wherein the degassing or drying of the polycondensate in the solid state is performed at a pressure below atmospheric pressure or by adding an inert gas.
10. The method according to claim 1 , wherein processing of the molten polycondensate outside the extruder includes melt filtration.
11. The method according to claim 1 , wherein processing of the molten polycondensate outside the extruder includes the use of a melt pump.
12. The method according to claim 1 , wherein the polycondensate is a polyethylene terephthalate.
13. The method according to claim 1 , comprising:
using a ring extruder for melting the polycondensate.
14. The method according to claim 3 , wherein the polycondensate is a polyethylene.
15. The method according to claim 14 , wherein the polycondensate in its starting form is present as a bulk material with a bulk density in a range of 200 kg/m 3 to 600 kg/m 3 .
16. The method according to claim 15 , wherein the polycondensate is formed as flakes or chips.
17. The method according to claim 16 , wherein a starting material of the polycondensate is partially predried before the melting.
18. The method according to claim 17 , comprising:
degassing the polycondensate for removing volatile impurities or decomposition products from the polycondensate.
19. The method according to claim 17 , comprising:
introducing the polycondensate in a solid state into the extruder;
heating the polycondensate to a temperature below the melting point; and
degassing or drying the polycondensate, wherein the degassing or drying of the polycondensate in the solid state is performed at a pressure below atmospheric pressure or by adding an inert gas.
20. The method according to claim 19 , wherein processing of the molten polycondensate outside the extruder includes melt filtration.
21. The method according to claim 12 , wherein the polyethylene terephthalate is obtained from recycled bottles.