Supported noble metal, phase-controlled catalyst and methods for making and using the catalyst
View Patent ↗A particulate supported noble metal phase-controlled catalyst material having 5-1000 μm surface area of 50μ500 m 2 /gm is provided for use in direct catalytic production of hydrogen peroxide (H 2 O 2 ) product from hydrogen and oxygen-containing feedstreams. The catalyst is made by depositing phase controlled crystals of a noble metal such as palladium on a suitable particulate support material such as carbon black, by utilizing a precursor solution of the metal and a suitable control ionic polymer having molecular weight of 300-8000 such as sodium polyacrylate in a selected metal to polymer molar ratio of 1:0.1 to 1:10, which procedure provides desired phase control of the noble metal atoms to form widely dispersed minute noble metal crystals on the support material. The invention includes methods for making the catalyst, and also a process for utilizing the catalyst to directly produce high yields of hydrogen peroxide (H 2 O 2 ) product from hydrogen and oxygen-containing gaseous feedstreams.
1. A supported noble metal catalyst, comprising:
a particulate support material; and
at least one noble metal controllably deposited on said particulate support material as widely distributed noble metal crystal particles,
at least a majority of said noble metal crystal particles having a 110 and/or 220 phase exposition so that at least a majority of active surface atoms of the noble metal crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
2. A supported noble metal catalyst as defined in claim 1 , said particulate support material having a particle size in a range of 5-1,000,000 nm.
3. A supported noble metal catalyst as defined in claim 1 , said particulate support material having a particle size in a range of 15-5,000 nm.
4. A supported noble metal catalyst as defined in claim 1 , said particulate support material having a total surface area in a range of 50-500 m 2 /g.
5. A supported noble metal catalyst as defined in claim 1 , said particulate support material comprising carbon black having total surface in a range of 100-250 m 2 /g.
6. A supported noble metal catalyst as defined in claim 1 , said support material comprising at least one member selected from the group comprising alumina, activated carbon, carbon black, and silica.
7. A supported noble metal catalyst as defined in claim 1 , said noble metal having a concentration in a range of 0.1-10 wt. %.
8. A supported noble metal catalyst as defined in claim 1 , said noble metal having a concentration in a range of 0.2-5 wt %.
9. A supported noble metal catalyst as defined in claim 1 , said noble metal comprising at least one member selected from the group comprising palladium, platinum, gold, iridium, osmium, rhodium, and ruthenium.
10. A supported noble metal catalyst as defined in claim 1 , said noble metal comprising an alloy of two or more noble metals.
11. A supported noble metal catalyst as defined in claim 10 , said alloy comprising palladium and at least one other noble metal.
12. A supported noble metal catalyst as defined in claim 11 , said other noble metal in said alloy comprising at least one of gold, iridium, osmium, rhodium, or ruthenium.
13. A supported noble metal catalyst as defined in claim 11 , said other noble metal in said alloy comprising platinum.
14. A supported noble metal catalyst as defined in claim 13 , said noble metal alloy having a palladium to platinum weight ratio in a range of 20:1 to 100:1.
15. A supported noble metal catalyst as defined in claim 1 , said noble metal crystal particles having a size in a range of 1-100 nm.
16. A supported noble metal catalyst as defined in claim 1 , substantially all of said noble metal crystal particles having a 110 and/or 220 phase exposition so that substantially all of the active surface atoms of said noble metal crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
17. A supported noble metal catalyst as defined in claim 1 , said catalyst being suitable for use in the direct catalytic production of hydrogen peroxide (H 2 O 2 ) from hydrogen- and oxygen-containing feedstreams.
18. A method of catalytically producing hydrogen peroxide from hydrogen and oxygen-containing feedstreams, comprising:
(a) providing a gaseous feedstream comprising hydrogen gas and oxygen;
(b) foaming an aqueous liquid slurry comprising the supported noble metal catalyst of claim 1 ; and
(c) reacting the aqueous liquid slurry with the gaseous feedstream to yield hydrogen peroxide.
19. A method of catalytically producing hydrogen peroxide as defined in claim 18 , the gaseous feedstream being continuously introduced into a reactor containing the aqueous liquid slurry and the hydrogen being withdrawn continuously.
20. A method of catalytically producing hydrogen peroxide as defined in claim 18 , said supported noble catalyst comprising palladium.
21. a method of catalytically producing hydrogen peroxide as defined in claim 20 , said supported noble metal catalyst further comprising platinum.
22. A supported noble metal catalyst, comprising:
a particulate support material; and
at least one noble metal controllably deposited on said particulate support material so as to provide a wide distribution of minute noble metal crystal particles having a particle size in a range of 1-100 nm,
said noble metal comprising palladium,
at least a majority of said noble metal crystal particles having a 110 and/or 220 phase exposition so that at least a majority of active surface atoms of the noble metal crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
23. A supported noble metal catalyst as defined in claim 22 , said noble metal further comprising at least one other noble metal in addition to palladium.
24. A supported noble metal catalyst as defined in claim 23 , said noble metal further comprising platinum as an alloying agent.
25. A supported noble metal catalyst as defined in claim 22 , substantially all of said noble metal crystal particles having a 110 and/or 220 phase exposition so that substantially all of the active surface atoms of said noble metal crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
26. A method of making a supported noble metal catalyst, comprising:
(a) providing a first solution containing at least one noble metal salt;
(b) providing a second solution comprising at least one ionic control polymer dissolved in water, said control polymer having molecular weight in a range of 300-8000;
(c) mixing said first and second solutions together so as to form a precursor solution in which the molar ratio of said noble metal salt to said control polymer is in a range of 1:0.1 to 1:10;
(d) mixing said precursor solution with a particulate support material so as to impregnate said particulate support material with said precursor solution;
(e) drying said impregnated particulate support material; and
(f) removing said control polymer to yield a supported noble metal catalyst comprising active minute noble metal crystal particles in which at least a majority have a phase exposition of 110 and/or 220 so that at least a majority of active surface atoms of the noble metal crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
27. A method of making a supported noble metal catalyst as defined in claim 26 , said first solution comprising palladium chloride and said second solution comprising sodium polyacrylate.
28. A method of making a supported noble metal catalyst as defined in claim 27 , said first solution further comprising a dilute acid.
29. A method of making a supported noble metal catalyst as defined in claim 27 , further comprising mixing a third solution comprising a platinum salt with said first and second solutions before mixing said precursor solution with said particulate support material.
30. A method of making a supported noble metal catalyst as defined in claim 29 , said platinum salt comprising hydrogen hexachloroplatinate (H 2 PtCl 6 ) in an amount so us to provide a palladium to platinum weight ratio in a range of 20:1 to 100:1.
31. A method of making a supported noble metal catalyst as defined in claim 26 , said control polymer having a molecular weight in a range of 600-6000.
32. A method of making a supported noble metal catalyst as defined in claim 26 , said control polymer comprising a polyacrylate.
33. A method of making a supported noble metal catalyst as defined in claim 26 , said control polymer comprising at least one member selected from the group comprising polyvinyl benzoates, polyvinyl sulfates, polyvinyl sulfonates, polybiphenol carbonates, polybenzimidozoles, and polypyridines.
34. A method of making a supported noble metal catalyst as defined in claim 26 , the molar ratio of said noble metal salt to said control polymer in said precursor solution is in a range of 1:0.5 to 1:5.
35. A method of making a supported noble metal catalyst as defined in claim 26 , the molar ratio of said noble metal salt to said control polymer in said precursor solution is in a range of 1:0.8 to 1:2.
36. A method of making a supported noble metal catalyst as defined in claim 26 , said particulate support material having a surface area in a range of 50‥500 m 2 /g.
37. A method of making a supported noble metal catalyst as defined in claim 26 , further comprising reducing the precursor solution obtained in (c) with hydrogen.
38. A method of making a supported noble metal catalyst as defined in claim 26 , removing said control agent in (f) being performed by reducing the supported noble metal catalyst with hydrogen.
39. A method of making a supported noble metal catalyst as defined in claim 26 , said supported noble metal catalyst being suitable for use in the direct catalytic production of hydrogen peroxide (H 2 O 2 ) from hydrogen- and oxygen-containing feedstreams.
40. A method of making a supported noble metal catalyst as defined in claim 26 , wherein (f) yields a supported noble metal catalyst in which substantially all of said noble metal crystal particles have a 110 and/or 220 phase exposition.
41. A method of making a supported palladium catalyst, comprising:
(a) providing a first solution comprising a palladium salt;
(b) providing a second solution comprising a polyacrylate;
(c) mixing said first and second solutions together so as to form a precursor solution in which the molar ratio of said palladium salt to said polyacrylate is in a range of 1:0.5 to 1:5;
(d) mixing the precursor solution with a particulate support material so as to impregnate said particulate support material with said precursor solution;
(e) drying said impregnated particulate support material; and
(f) reducing said impregnated particulate support material with hydrogen gas to yield a supported palladium catalyst comprising active minute palladium crystals in which at least a majority have a phase exposition of 110 and/or 220 so that at least a majority of active surface atoms of the palladium crystal particles are exposed in an orderly pattern characteristic of the 110 and/or 220 phase exposition.
42. A method of making a supported noble metal catalyst as defined in claim 18 , said first solution further comprising a dilute acid.
43. A method of making a supported palladium catalyst as defined in claim 41 , further comprising adding a platinum salt to the precursor solution.
44. A method of making a supported noble metal catalyst as defined in claim 41 , further comprising reducing the precursor solution obtained in (c) with hydrogen.
45. A method of making a supported noble metal catalyst as defined in claim 41 , the molar ratio of said palladium salt to said polyacrylate in said precursor solution is in a range of 1.0.8 to 1:2.
46. A method of making a supported noble metal catalyst as defined in claim 41 , wherein (f) yields a supported noble metal catalyst in which substantially all of said noble metal crystal particles have a 110 and/or 220 phase exposition.