Material for shadow mask, method for production thereof, shadow mask comprising the material and picture tube using the shadow mask
View Patent ↗A material for a shadow mask, characterized in that it has a chemical composition: C=0.0030 wt %, Si=0.03 wt %, Mn: 0.1 to 0.5 wt %, P=0.02 wt %, S=0.02 wt %, Al: 0.01 to 0.07 wt %, N=0.0030 wt %, B: an amount satisfying 0.5≦B/N≦2, and balance: Fe and inevitable impurities, and can form a shadow mask having a coercive force Hc of 90 A/m or less; and a method for producing the material, characterized in that use is made of a raw material having the above chemical composition, the finishing temperature in hot rolling is lower than Ar3 point by O to 30° C., the coiling temperature is 650 to 700° C., and the rolling reduction percentage in the final rolling (secondary cold rolling) is 30 to 45%. The material produced by the method exhibits magnetic characteristics being uniform in a coil and excellent as described above.
1. A material for shadow masks, which is characterized in that it consists of C≦0.0030% by weight, Si≦0.03% by weight, Mn of from 0.1 to 0.5% by weight, P≦0.02% by weight, S≦0.02% by weight, Al of from 0.01 to 0.07% by weight, N≦0.0030% by weight and B to satisfy 0.5≦B/N≦2 with a balance of Fe and inevitable impurities and it forms a shadow mask having a coercive force of at most 90 A/m.
2. A method for producing a material for shadow masks, which is characterized in that a steel ingot that consists of C≦0.0030% by weight, Si≦0.03% by weight, Mn of from 0.1 to 0.5% by weight, P≦0.02% by weight, S≦0.02% by weight, Al of from 0.01 to 0.07% by weight, N≦0.0030% by weight and B to satisfy 0.5 ≦B/N≦2 with a balance of Fe and inevitable impurities is hot-rolled at a finishing temperature lower than the Ar3 point thereof by from 0 to 30° C., coiled at a take-up temperature of from 540 to 700° C., washed with acid, cold-rolled, and then continuously annealed as a temperature of not less than 750° C. to make it have a remaining C amount of at most 0.0015% by weight, and thereafter subjected to secondary rolling to a reduction ratio of from 30 to 45%.
3. A shadow mask formed of the material of claim 1 , which has a coercive force of at most 90 A/m and a thickness of from 0.05 to 0.25 mm.
4. A picture tube that comprises the shadow mask of claim 3 .