Dispersible polymer powders
View Patent ↗Disclosed herein is a water-dispersible powder consisting essentially of polymers T comprising recurring thiophene units and at least one further polyanionic polymer P and process for preparing and using the same.
1. A process for preparing water-dispersible powders consisting essentially of polymers T comprising recurring thiophene units and at least one further polyanionic polymer P, the process comprising admixing a dispersion or solution containing polymers T and at least one further polyanionic polymer P with a salt, continuing the addition of the salt until the polymers precipitate and subsequently isolating and drying the latter.
2. A process for preparing a powder as claimed in claim 1 , wherein the salt is selected from the group consisting of sodium chloride, sodium bromide, sodium iodide, potassium chloride, potassium bromide, sodium carbonate, sodium hydrogencarbonate, sodium sulfate, sodium hydrogensulfate, potassium carbonate, potassium hydrogencarbonate, potassium sulfate, potassium hydrogensulfate, sodium and potassium formate, acetate, proprionate and butyrate, alkali metal sulfonates, sodium or potassium salts of polystyrenesulfonic acids, sodium or potassium salts of benzenesulfonic acid, toluenesulfonic acids and ethylbenzenesulfonic acids, ammonium salts, soluble alkaline earth metal salts, and soluble transition metal salts.
3. A process for preparing a powder as claimed in claim 1 , wherein the particle size of the polymers is less than 1 μm.
4. A process for preparing a powder as claimed in claim 1 , wherein the polymers comprising recurring thiophene units are obtained by polymerization of thiophenes of the formula
where
R 1 is a substituted or unsubstituted alkylene radical having from 1 to 10 carbon atoms and
R and R 2 are identical or different and are each hydrogen, a linear or branched alkyl radical having from 1 to 20 carbon atoms, OH, O—OH 2 —CH 2 —CH 2 —SO 3 H or O-alkyl having 1–18 carbon atoms.
5. A process for preparing powder as claimed in claim 1 , wherein the polymer P is polystyrenesulfonic acid.
6. A process for preparing water-dispersible powders consisting essentially of polymers T comprising recurring thiophene units and at least one further polyanionic polymer P, the process comprising admixing a dispersion or solution containing polymers T and at least one further polyanionic polymer P with a compound which forms an azeotrope with water, removing the water by azeotropic distillation and obtaining the polymer by isolating and drying.
7. A process for preparing powder as claimed in claim 6 , wherein the particle size of the polymers is less than 1 μm.
8. A process for preparing powder as claimed in claim 6 , wherein the polymers comprising recurring thiophene units are obtained by polymerization of thiophenes of the formula
where
R 1 is a substituted or unsubstituted alkylene radical having from 1 to 10 carbon atoms and
R and R 2 are identical or different and are each hydrogen, a linear or branched alkyl radical having from 1 to 20 carbon atoms, OH, O—OH2—CH 2 —CH 2 —SO 3 H or O-alkyl having 1–18 carbon atoms.
9. A process for preparing powder as claimed in claim 6 , wherein the polymer P is polystyrenesulfonic acid.