Styrene-free unsaturated polyester resin compositions
View Patent ↗Styrene-free unsaturated polyester resin compositions are provided which have low volatile organic compounds and hazardous air pollutants emissions when these resin compositions are used in open molding applications. A process for the manufacture of these resin compositions is provided.
1. A styrene-free unsaturated polyester resin composition consisting essentially of (1) a dicyclopentadiene-based unsaturated polyester; (2) a urethane (meth)acrylate; (3) a multifunctional (meth)acrylate monomer and (4) from 5-60 percent by weight of a hydroxyl-functionalized (meth)acrylate monomer, wherein the resin composition after cure has a heat distortion temperature (ASTM D-648) of at least 65° C.
2. A resin composition as defined by claim 1 wherein the concentration of the unsaturated polyester is from 15-70 percent by weight.
3. A resin composition as defined by claim 1 wherein the unsaturated polyester has a weight average molecular weight of 800-10,000.
4. A resin composition as defined by claim 1 wherein the unsaturated polyester is the reaction product of dicyclopentadiene with compounds of carboxylic acids and/or anhydrides and alcohols.
5. A resin composition as defined by claim 1 wherein the unsaturated polyester is modified with glycidyl methacrylate at a level up to about 20 percent by weight of the unsaturated polyester.
6. A resin composition as defined by claim 1 wherein the unsaturated polyester is modified with an allyl ether functionalized alcohol or epoxy at a level up to about 20 percent by weight of the unsaturated polyester.
7. A resin composition as defined by claim 1 wherein the concentration of the urethane (meth)acrylate is from 15-70 percent by weight.
8. A resin composition as defined by claim 1 wherein the urethane (meth)acrylate is a reaction product of a hydroxyl-functionalized (meth)acrylate with a diisocyanate or polyiisocyanate.
9. A resin composition as defined by claim 1 wherein the concentration of the multifunctional (meth)acrylate is from 5-60 percent by weight.
10. A resin composition as defined by claim 1 that contains up to about 60 percent by weight of a filler.
11. A resin composition as defined by claim 10 wherein the filler is calcium carbonate, calcium sulfate, aluminum trihydrate, clay or a combination thereof.
12. A resin composition as defined by claim 1 that contains up to about 5 percent by weight of a thixotropic agent.
13. A resin composition as defined by claim 12 wherein the thixotropic agent is fumed silica, organoclays or a combination thereof.
14. A resin composition as defined by claim 1 that contains up to about 2 percent by weight of a barrier forming agent.
15. A resin composition as defined by claim 1 that is cured with 1-3 percent by weight of a diacylperoxide, hydroperoxide, ketone peroxide, peroxyester, peroxyketal, dialkyl peroxide, alkyl perester, percarbonate, azo compound or a combination thereof.
16. A resin composition as defined by claim 1 that is formulated with a derivative of aniline, an amide, an aromatic amine or an aliphatic amine at a level up to about 1 percent by weight.
17. A resin composition as defined by claim 1 that is formulated with a cobalt carboxylate, vanadium, potassium, zinc or iron compound at a level up to about 1 percent by weight.
18. A resin composition as defined by claim 1 that after cure has a tensile strength (ASTM D-638) and tensile modulus (ASTM D-638) of at least 7,000 psi and 350,000 psi, respectively.
19. A resin composition as defined by claim 1 that after cure has a flexural strength (ASTM D-790) and flexural modulus (ASTM D-790) of at least 10,000 psi and 350,000 psi, respectively.
20. A resin composition as defined by claim 1 that contains at least two multifunctional (meth)acrylate monomers.
21. A resin composition as defined by claim 1 that contains at least two hydroxyl-functionalized (meth)acrylate monomers.
22. A resin composition as defined by claim 14 wherein the barrier forming agent is a paraffin, polyester, polysiloxane or a combination thereof.